Overview:
Zrd--135 lubricant is constituted of fatty acid calcium and a variety of extreme pressure agent, anti-wear agent, additives, through special process synthesis, mainly for low carbon steel wire without pickling drawing.
Performance:
Fatty acid content: 40%-45% color: yellow-gray
Softening point: 205 ? water content: 0.4-1%
Decomposition temperature: 410-440 ? size: medium particles
Application:
Mainly be used in phosphate, boron-treated, without pickling, used in the front pass drawing, also used in all pass drawing, film thickness, in the case of cooling is not good, possible appear coking, dry pull backward water tank can improve the quality of steel wire, reduce mold consumption.
Overview:
Zro-45 polishing lubricant oil is surface treatment material composed by a special vegetable oil , machine oil and anti-rust agent, anti-friction agent and nano-materials. It can improve the anti-rust performance and smoothness of welding. Due to the presence of nano-materials , it also has excellent performance for copper coated wire.
Performance:
Form: pale yellow oily liquid specific gravity: 0.91 (20 ?)
Viscosity: 40cst (40 ?) ph value: 6.7 moisture: 0.3 max
Application:
It can be used for all drawing passes and will form thin film under in a bad cooling conditionn, it may appear coke, drawing speed of crude rough is 100 ~ 200m / min, while the small size of the drawing speeds is up to720 ~ 800m / min, the film is easy to clean.
1. Properties
Pale yellow oily liquid
Specific gravity 0.91 (20 ?)
Viscosity 40cst (40 ?)
Ph value of 6.7 or less moisture 0.3
Ingredients: vegetable oil, additives
2. Features
It has excellent lubricity and significant anti-rust performance to the copper wire. The anti-friction agent and nano-materials make wire surface more smooth, and more smoothly for wire feeding.The materials do not contain any hazardous and noxious substances, when welding the lubricant on wire surface does not produce harmful substances.
3.Uses
Polished copper or copper wire for surface coating
4.Usage
Directly pour into the mould box
Used in circular fashion
Coating by felt jig
5. Notes:
Black residue when direct drawing, may be caused by water incorporation or polishing mold too hot, remove the deposition , use the upper layer oil.