Specification:
Screw diameter: d20mm-d220mm
Mould clamping force: 250t-3200t
Shot weight: 30g-30000g
Technical information
Base materials:
(1)38crmoala(jis sacm645)
(2)42crmo(aisi 4140)
(3)4cr5mosi v1 (jis skd-61)
(4)9cr18mov
(5)hpt
Bimetallic alloy materials:
1)fe-based alloy
2)ni-based alloy/deloro alloy
3)co-based alloy
4)nico-based alloy
5)tungsten carbide/wolfram carbide
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000hv
Nitrided brittleness: less than grade 1
Surface roughness: ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: ¡ã 950hv
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm.
Slushing oil coated& film wrapped in wooden case
Specification:
Screw diameter: d20mm- d220mm
Mould clamping force: 250t-3200t
Shot weight: 30g-30000g
Base materials:
(1)38crmoala(jis sacm645)
(2)42crmo(aisi 4140)
(3)4cr5mosi v1 (jis skd-61)
(4)9cr18mov
(5)hpt
Bimetallic alloy materials:
1)fe-based alloy
2)ni-based alloy/deloro alloy
3)co-based alloy
4)nico-based alloy
5)tungsten carbide/wolfram carbide
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000hv
Nitrided brittleness: less than grade 1
Surface roughness: ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: 950hv
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm.
Slushing oil coated& film wrapped in wooden case
Specification:
Screw Diameter: D15- D 300
L/D ratio: 15-46
Product classification:
Aiming at different plastic products the screw can be chosen from: General type, pin type, barrier type, separation type, and gas-exhausting type, etc.
Base Materials:
(1)38CrMoAlA(JIS SACM645)
(2)42CrMo(AISI 4140)
(3)4Cr5MoSi V1 (JIS SKD-61)
(4)9Cr18MOV
(5)HPT
Bimetallic alloy materials:
1)Fe-based alloy
2)Ni-based alloy/Deloro alloy
3)Co-based alloy
4)NiCo-based alloy
5)Tungsten carbide/Wolfram carbide
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000HV
Nitrided brittleness: less than grade 1
Surface roughness: Ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: >950HV
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm
Slushing Oil Coated& Film Wrapped in Wooden Case
Specification:
Screw diameter: d15- d 300
L/d ratio: 15-46
Product classification:
Aiming at different plastic products the screw can be chosen from: general type, pin type, barrier type, separation type, and gas-exhausting type, etc.
Base materials:
(1)38crmoala(jis sacm645)
(2)42crmo(aisi 4140)
(3)4cr5mosi v1 (jis skd-61)
(4)9cr18mov
(5)hpt
Bimetallic alloy materials:
1)fe-based alloy
2)ni-based alloy/deloro alloy
3)co-based alloy
4)nico-based alloy
5)tungsten carbide/wolfram carbide
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000hv
Nitrided brittleness: less than grade 1
Surface roughness: ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: >950hv
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm
Slushing oil coated& film wrapped in wooden case
Specification:
45/90, 45/100, 50/105, 51/105, 55/110, 55/120, 58/124, 60/125, 65/120, 65/132, 68/143, 70/135, 70/140, 75/150, 80/143, 80/156, 92/188
The above are standard specifications, we can customize according to customers' requirements.
The compression ratio of screws can be designed according to different products and ingredients.
Base materials:
1)38crmoala(jis sacm645)
2)42crmo(aisi 4140)
3)4cr5mosi v1 (jis skd-61)
4)9cr18mov
5)hpt
Technics:
Heat treatment
High-frequency quenching
Nitriding treatment
Hard-chrome electroplating
Bimetallic alloy welding
Bimetallic alloy centrifugal casting
Technical parameter:
Nitrided layer depth: 0.5-0.8mm
Nitrided hardness: 900-1000hv
Nitrided brittleness: less than grade 1
Surface roughness: ra0.4
Linearity of screw: 0.015mm
Hard-chrome plating hardness after nitriding: ¡ý 950hv
Chrome-plating layer depth: 0.025-0.085mm
Bimetallic layer depth: 3mm
Slushing oil coated& film wrapped in wooden case