Sio2 silicon dioxide 21 % al2o
Aluminum oxide 5.30 % fe2o3
Ferric oxide 3.30 % cao
Calcium oxide 65.60 % mgo
Magnesium oxide 1.10 % so3
Sulphur trioxide 2.70 % loi
Loss of ignition 0.90 %
C3a tricalcium aluminates 8.05 %
C3s tricalcium silicate 60.00 %
C2s dicalcium silicate 15.00 % c4af
Tricalcium alumino ferric 9.76 %
Physical and mechanical properties
Blain cm2/gr 3.250
Autoclave expansion 0.02
Initial setting time (vicat) 105 minutes
Final setting time (vicat) 135 minutes
Compressive strength
03 days - 230 kg/cm2
07 days 305 kg/cm2
28 days 420kg/cm2.
On the customer requirements.