Solar EVA encapsulant is made by ethylene vinyl acetate (EVA) , eva encapsulant 2008B especially for crystal and polycrystalline silicon module encapsulation, after cured, it is characterized with high adhesion, excellent weather and uv resistance, good insulation, low shrinkage, high optical transmission.
V-gool EVA Encapsulant outstanding property:
1. Damp and heating Test (8585RH ) continuously 1000 hours, and temperature cycles test (-40-85)___IEC61215
2. Excellent adhesive strength with glass and TPT 60N/cm
3. Light transmission > 91%
4. Cross-linking rate is ranged from 80-85%.
Cartons with pallet.
Solar EVA encapsulant is made by ethylene vinyl acetate (EVA), EVA encapsulant 2008a especially for thin film module encapsulation, after cured, it is characterized with high adhesion, excellent weather and UV resistance, good insulation, low shrinkage, high optical transmission.
V-gool EVA Encapsulant outstanding property:
1. Damp and heating Test (8585RH ) continuously 1000 hours, and temperature cycles test (-40-85)___IEC61730
2. Excellent adhesive strength with glass and TPT £¾80N/cm, suitable for double glass structure, no bubbles and Delamination.
3. Light transmission > 91%
4. Cross-linking rate is ranged from 80-90%.
Cartons with pallet.
Solar EVA encapsulant is made by ethylene vinyl acetate (EVA) , EVA encapsulant 2009 especially for C-SI module encapsulation , after cured , it is characterized with high adhesion , excellent weather and uv resistance, good insulation , low shrinkage , high optical transmission.
V-gool EVA Encapsulant outstanding property:
1. Damp and heating Test (8585RH ) continuously 1000 hours, and temperature cycles test (-40-85)___IEC61215
2. Excellent adhesive strength with glass and TPT £¾80N/cm.
3. Light transmission up to 92%
4. Cross-linking rate is ranged from 80-90%.
Carton with pallets.