Low carbon steel shot as abrasive media Longer lasting and more durable Sae standard Save shot blasting cost Material: q195 Residual amount of low carbon steel shot, common low carbon steel shot and high carbon steel shot respectively is 70%, 40% and 20% after impacted 500 times. Low carbon steel shot is low wear, low breakage and long service life. In addition, low carbon steel shot could be applied to all the fields suitable for common steel shot. We promise to offer you the right low carbon steel shot with best price and best service! all items we are selling are best quality among the similar products. All items will be strict tested before shipping! welcome your negotiated prices, we promise your good price will be our consideration. We are sincerely looking for your cooperation.
Steel cut wire shot Size: 1.0mm, 1.5mm Chemistry composition: C: 0.45-0.75% Mn: 0.40-1.20% Si: 0.10-0.30% S: 0.04%max P: 0.04%max Average degree of hardness: 1.0mm: 51-53hrc (525-561hv) 1.5mm: 41-45hrc (388-436hv) Degree of hardness deviation the anti-pulls strength: 1.0mm: 1750-2150mpa 1.5mm: 1250-1450mpa Minimum density: 7.8g/cm3 25kgs/bag, 40kgs/ton/pallet
Strictly according to American motorcar engineer association "J441 SAE standards," the People's Republic of China machinery industry "JB/T 8354-1996 steel wire cut shots standard" material requirements to production, but since using recycled steel wire its length and standard a slightly different. Steel cut wire shot plastic woven sack packaging, packaging bags which steel grit, steel cut wire shot wood pallet packaging, paper bag steel cut wire shot t packaging, bucket type steel bolus packaging.
Blast cleaning of steel cut wire:used for blast cleaning of casting, die-casting, forging, sand removal of casting, steel plate, h type steel, steel structure. 25kgs/bag, 40 bags/pallect.
Main specification:1.0mm,1.5mm,2.0mm,2.5mm. The quality of products has met SAE & ISO international standards and the company has passed international standard ISO9001. The products have been exported to more than 20 countries and regions and have got a high reputation from home and abroad.
Products Cut Wire Shot Chemical Composition C 0.45~0.75% Mn 0.40~1.20% Si 0.10~0.30% S
Hardness: CW: 35-48HRC 1.0mm: 51-53HRC 1.5mm: 41-45HRC Chemical Composition:C= 0.45-0.75% Mn= 0.40-1.20% Si =0.10-0.30% S¡Ü0.40% P¡Ü0.40%
Strictly according to Japan JIS standard production stainless steel wire ingredients to production. Stainless cut wire steel shot plastic woven sack packaging, packaging bags which steel grit, Stainless steel shot wood pallet packaging, paper bag Stainless steel shot t packaging, bucket type steel bolus packaging.
Application:Our products main used for sand and rusts removing of cast iron cast steel, steel structures, steel plate, steel pipes, forging and surface treatment of oxidized workpieces Stainless Steel Cut wire shot have different materials:SUS304 ,SUS202,SUS205,SUS430 Specification:0.2 0.3 0.4 0.5 0.6 0.8 1.0 1.2 1.4mm Chemical compositions: 304 Austenite Typeú¦Cú+0.25%,Cr=16í½18%, Ni=6í½10%, Siú+1%,Mnú+2% 430 Ferrite Typeú¦Cú+0.25%, Cr=16í½18%, Siú+1%, Mnú+1% 410 Martensite Typeú¦Cú+0.25%, Cr=11í½13%, Siú+1%, Mnú+1% Hardness: 308-509HV 32-50 HRC Duraility:6500 times Microstructure:304 Deformed Austenite 430 Deformed Ferrite 410 Deformed Martensite Density: 7.8g/ cm3 Bulk Density:4.5g/ cm3 Packing types: braided bag packing: 25kg/bag, 40 bags/pallet, flexible container packing:1000kg/bag, stock packing, paper bag packing:25kg/bag, 40bags/pallet, with paper bag barrel packing:900kg/barrel.
Used for shot peening for all kinds of metal parts Sae Vdfi Iso Din Mil