Specifications: Project Guaranteed values Examination result Color White White powder The ph value 5.5-7.0 7 Oil absorptiong/100g 25-35% 29 Residue on sieve(45um)≤ 0.50% 0.4 Moisture% ≤1.5 0.9 P2o5% 35-40 35.8 Al2o3% 12-18 17 Sio2% 8-12 9.3 Specifications: Project Guaranteed values Examination result Color White White powder The ph value 5.5-7.0 7 Oil absorptiong/100g 25-35% 29 Residue on sieve(45um)¡ü 0.50% 0.4 Moisture% ¡ü1.5 0.9 P2o5% 35-40 35.8 Al2o3% 12-18 17 Sio2% 8-12 9.3 1.Usage:aluminium tripolyphosphate is the ideal substitute of toxic antirust pigments containing lead or chrome. This product is superior to such antirust pigments as lead red, zinc chrome yellow and zinc phosphate in rust prevention and practicality. 2.Properties: white powder, insoluble in water, density: 2.6-3g/cm, nontoxic, not irritative to skin, free of harmful heavy metal elements like lead or chrome and good thermal stability. 3.Applications: this coloring pigment is able to widely substitute conventional toxic antirust pigments such as lead red and zinc chrome yellow in the production of various prime coats and combined coating materials. With good compatibility with varnish paints, it can be used together with various coloring pigments, filling agents and antirust pigments in the production of high performance anti-corrosion coating materials.
Applications: This coloring pigment is able to widely substitute conventional toxic antirust pigments such as lead red and zinc chrome yellow in the production of various prime coats and combined coating materials. With good compatibility with varnish paints, it can be used together with various coloring pigments, filling agents and antirust pigments in the production of high performance anti-corrosion coating materials. In composite paper bags25kg each,20MT/FCL' with pallet.
Aluminium tripolyphosphate Ubstitute for toxic antirust pigment including lead and chromium. This achievement was awarded the State Sci-tech Advancement Award for 1990, and has been incorporated into the State Spark Program. This achievement has been put into production in the Plant for the first time. Thanks to advanced production equipment and sound examination and test means, aluminium tripolyphophate series products producted by the Plant have reached the world advanced level in terms of quality. Main composition: aluminium dihydrogen tripolyphophateííALH2 P3O10.2H2O Main antirust group: P3O105- Performance: non-volatile white powder with very fine crystal, nonsoluble in water, density of 2.0-3.0g/cm3, non-toxic, nonirritant to skin, with good thermal stability Uses: widely applied to various types of priming paints or prime and top combined coat paints, not subject to contraints of other conditions. Applicable to phenolic resin, alkyd resin, epoxy resin and epoxy aldehyde resin, acrylate resin as well as other oilsoluble resin and various watersoluble dry or air drying resinú¼producing acid-resistant, salt water-resistant, fireproof, anti-corrosive paints with distinctive antirust performance. Production specifications Modified aluminium tripolyphophate APW-1 type: used for oilsoluble paint. Modified aluminium tripolyphophate APW-1 type: mostly used for watersoluble paintú¼but also for oilsoluble paint.Product features Non-toxic: this product is non-toxic, does not contain harmful heavy metals including lead and chromium, can substitute for traditional harmful antirust pigment including red lead, zinc chrome yellow. Strong rustproof: to add this product used as antirust pigment to antirust paints can effectively improve the adhesive force of painting, and salt atomization-resitance, anti-corrosiveness and anti-bubbling. Its antirust performance is better than that of antirust pigment including red lead, zinc chrome yellow , zinc phosphate. It has the effect of isolation and rustproof as well as passivation and anti-corrosiveness after painting. Wide application: paints made of this product can be used for the anti-corrosive treatment of not only steel and iron, but also light metals such as zinc, aluminium. White: this product is white powder, with colours of paint blended freely, can be widely applied to various types of priming paints or prime and top combined coat paints. Small amount of use: 25KGS BAG
Aluminum dehydrogenate tripolyphosphate series Main composition: aluminium tripolyhosphate (alh2p3o10.2h2o) Main anticorrosive group: p3o105 Properties: nonvolatile white powder with very fine crystal Unsoluble in water densityú¦ 2.6-3.0g/cm3. Nontoxic Nonirriant on skin thermal stable.() Character: excellent anticorrosion low consumption low cost Wilde adaptability. Uses: widely used in many kinds of primers, or mingle paint of primer and top-coat . It can be employed in phenol resiníóalkyd resiníóepoxy resiníóacrylic resin and other oilsoluble resins or water-soluble air drying or boking resin to produce paints with high anticorrosive performanceíóacid-resistanceíówater-resistance and fire-resistanceíúnow our customers use this new pigment in the painting of ocean ship, coat, car... Packing: in woven bags of 25kgs net each, with pvc lining. Also 500 kgs in big woven bag. Items Test rating Color White powder Moisture content ín1.5% P2 o5 % 40-46% Degree of fineness(#400 mesh) ín0.5 Oil absorption 25-35 Ph value 5-7 Al2 o3 % 10-13% Zinc oxide 10-15% 25kgs/bag or 500kgs/bag
Aluminium tripolyphosphate 1.Contents:p2o5%35-40 2.Usage: it is usd as antirust pigment in product of anti-corrosion coating Modified aluminum tripolyphosphate 1.Content:p2o5(%)42-46 2.Use:for water paint 3.Residue on sieve(45um)%
D G EXIM is one of the leading suppliers of Industrial Chemicals Acetic Acid Glacial Activated Carbon Aluminium Sulphate Magnesium Sulphate Aluminium Sulphate Ammonium Chloride Ammonium Sulphate Borax Decahydrate Borax Anhydrous Boric Acid Butyl Glycol Ether Calcium Chloride Caustic Soda Flakes / Pearls Citric Acid Gum Rosin Hydrogen Peroxide 50% Sodium Metabisulphite f.g Iso Cyanuric Acid Iso Propyl Alcohol Lactic Acid Methylene Chloride Mono Ethylene Glycol Mono Propylene Glycol Nonyl Phenyl Ethoxalates â?? np9 Oleic Acid Potassium Chloride Potassium Hydroxide Flakes Potassium Nitrate Sodium Formate Sodium Gluconate Sodium Hexametaphosphate Sodium Hydroxide Pearl/Flake Sodium Metasilicate Xanthan Gum Sodium Molybdate Sodium Tripolyphosphate Tetra Potassium Pyrophosphate Tetra Sodium Pyrophosphate Triethanolamine 85% Zinc Sulphate Calcium Chloride Edta Glycerine Guar Gum Mineral Oil Light / Heavy Phosphoric Acid 85% Soda Ash Dense/Light Sodium Benzoate Sodium Bicarbonate Sodium Carboxy Methyl Cellulose (CMC)
Supplier: Water treatment poly aluminium chloride/ aluminium sulphate / polyacrylamide, phosphate sodium tripolyphosphate / sodium hexametaphosphate /sodium triphosphate
1.Properties : Condensed aluminum phosphate is a type of colorless and odorless white crystalline powder, insoluble in water but freely soluble in chlorhydric acid or nitric acid.It will turn into colloid instead of melting at high temperature. In polyreaction, it will formstable a-ALPO4. 2.Applications: It is mostly used as binder and curing agent in the production of hi-temp refractory materials for kiln. It also serves as fluxing agent in the production of specialglass, as binder in fabrication of ceramics or tooth, and as catalyst in organic synthesis. In composite paper bags25kg each,20MT/FCL' with pallet
Acid-resistant glass cement is composed of water glass, curing agent and powder filler. Water glass, also known as sodium silicate chemically, is a type of metasilicate water solution. It will be known as potash water glass if potassium metasilicate is used commonly. Sodium silicate cement has good mechanical strength, excellent acid resistance (except for fluohydric acid and pyrophosphoric acid) and cheap price, but high in factor of porosity and irresistible to alkali. Potash water glass cement is made up of potash water glass, condensed aluminum phosphate as curing agent and acid-resistant fillings. It is superior to sodium silicate cement in impermeability, resistance to dilute acid and cohesive strength. In composite paper bags25kg each, 20mt/fcl' with pallet.