Laxmi Minerals

Calcined Bauxite: Calcined Bauxite is obtained by calcining (heating) superior grade Bauxite at high temperature (from 850 oC to 1600 oC). This removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57 % to 58 % in raw Bauxite, Calcined Bauxite has an alumina content of 82 % to 86 %. The heating is carried out in rotary kilns. Calcination is done at different temperatures ranging from 850 oC to 1600 oC depending upon the customer’s application. We export Calcined Bauxite for various applications such as refractory bricks, abrasives, steel polishing, etc. We provide consistency in quality and availability of Calcined Bauxite at extremely competitive prices. Applications of Calcined Bauxite: Refractory Grade Calcined Bauxite (CB - I and CB - II Grade) : To make refractory grade, Bauxite is thermally treated at 1600 oC to produce Calcined Bauxite where the Alumina content is mostly above 82%. Brown Fused Alumina, Proppants and Road Surfacing : To make the above grades, Bauxite is thermally treated at 1000 oC - 1200 oC to produce Calcined Bauxite where the Alumina content is anywhere between 80-88% depending on the requirement. Minimum Order Quantity : 1 Containers

We are glad to propose 500 MT of stain less steel mill scale. Mill scale is formed on the outer surfaces during by the hot rolling lamination of stainless-steel products. At a visual inspection the material is a hard brittle sand and is mainly composed of iron oxides, mostly ferric, and is bluish black in colour, but it also contains considerable alloying elements such as chromium and nickel. The recovery ratio after melting in furnace for the most valuable alloy elements is: - Ni: 3.5 - 4.5% - Cr: 6-8% From the chemical and physical analysis performed on the scrap, and according to the European environmental rules, the material has been classified as a special non dangerous waste, listed in green list. In particular the mill scale can be classified as follows: Waste code: 10 02 10 The material is stored on cemented flooring, and it can be loaded loose in tipper trucks or containers. Chemical analysis of the material is available on request.

We are proposing about 2000tons of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag - European Code: 19.12.01 - Basel Code: B1010 - HS Code: 2619.0020 - Quantity: 2000 tons currently available - Monthly quantity: 500-1000 tons depending on production - Size: 350 1200 mm - Fe content: from 77 to 86% - C content: above 2,5-3% - Bulk density: 2,8-3,4 tons/m3 - Loading type: loose in 20 (26-27 tons on average) The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact us

Mill scale, is formed on the outer surfaces of plates, sheets or profiles when they are being produced by rolling hot iron or steel billets in rolling or steel mills. It looks like a hard brittle sand and is mainly composed of iron oxides, mostly ferric, and is bluish black in color. Being produced during the reheating, conditioning and hot rolling operation for the production of steel articles, the mill scale initially adheres to the steel surface and protects it from atmospheric corrosion, provided no break occurs in this coating. From the chemical and physical analysis performed on the scrap, and according to the european environmental rules, the material has been classified as a special non dangerous waste, listed in green list In particular the mill scale can be classified as follows: Einecs (european commission no.): 266-007-8 Waste code: 10 02 10 Basel code: b 12 30 Hs code: 2619.00

Desulphurisation Slag is an iron slag derived from the desulphurisation skimming process. This material is an iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si), but has a stable chemistry with 75 -80% chemistry. The level of Fe% in the slag has been estimated by water displacement test. This material con offer competitive advantages respect other metal scraps: Price; Stable Chemistry; The material can be loaded loose in 20 heavy duty container. For further details feel free to contact us.