Calcined Bauxite: Calcined Bauxite is obtained by calcining (heating) superior grade Bauxite at high temperature (from 850 oC to 1600 oC). This removes moisture thereby increasing the alumina content. Compared to an alumina content of about 57 % to 58 % in raw Bauxite, Calcined Bauxite has an alumina content of 82 % to 86 %. The heating is carried out in rotary kilns. Calcination is done at different temperatures ranging from 850 oC to 1600 oC depending upon the customer’s application. We export Calcined Bauxite for various applications such as refractory bricks, abrasives, steel polishing, etc. We provide consistency in quality and availability of Calcined Bauxite at extremely competitive prices. Applications of Calcined Bauxite: Refractory Grade Calcined Bauxite (CB - I and CB - II Grade) : To make refractory grade, Bauxite is thermally treated at 1600 oC to produce Calcined Bauxite where the Alumina content is mostly above 82%. Brown Fused Alumina, Proppants and Road Surfacing : To make the above grades, Bauxite is thermally treated at 1000 oC - 1200 oC to produce Calcined Bauxite where the Alumina content is anywhere between 80-88% depending on the requirement. Minimum Order Quantity : 1 Containers
We are supplier and exporter of Calcined China Clay. We are offering an extensive range of high-quality Calcined China Clay that is used for paints, rubber and soap industries. Features: Chemically inert Correctly formulated Enhanced shelf life Specifications: Type: Powder Colour: White Packaging - As per Client Applications- Paints, Rubber and Soap industries. China Clay is a clay mineral with the chemical composition AlSiO3O5(OH)3. It is layered silicate mineral. It is soft earthy, usually white in color, produced by the chemical weathering of Aluminium Silicate mineral like Feldspar. Commercial grades of China Clay are supplied and transported as dry powder form, semi dry noodle form or as slurry.
Features Of Calcined Bauxite Calcination is a process of heating, hence calcined bauxite is obtained by heating the high grade ore of the bauxite. Heating further removes the moisture content from the ore and thus results in the increase of the alumina content. Applications Abrasives Refractories Road surfacing
Calcined bauxite is produced by sintering/calcining with natural bauxite ore of low iron, low alkali at temperatures of 1600 - 1800 degree Celsius in the rotary kiln or round kiln through pre-heationg, calcination, cooling and other processes. During Calcining, it can be removed impurities and improving the content of alumina. Refractory grade bauxite has high refractoriness, good mechanical strength and moderate slag resistance. Therefore calcined bauxite is one of the most important raw materials for the production of shaped and unshaped refractories for the steel industry, foundries, glass and cement plants.
Supplier: Aluminium ( ingots, t bars, sows, rods), copper (cathodes, cakes, billets, ingots, rods), lead (ingots), nickel (cathodes both cut and uncut briquettes, pellets, discs, etc.), tin (ingots, etc.), zinc (ingots both regular size and jumbos), steel billets (all types including crc, hrc, hdgc, plates, sheets), concentrates and ores for above items including bauxite, manganese, clinker and iron ores etc), scraps of above items including hms 1&2 and steel scraps
Buyer: Aluminium ( ingots, t bars, sows, rods), copper (cathodes, cakes, billets, ingots, rods), lead (ingots), nickel (cathodes both cut and uncut briquettes, pellets, discs, etc.), tin (ingots, etc.), zinc (ingots both regular size and jumbos), steel billets (all types including crc, hrc, hdgc, plates, sheets), concentrates and ores for above items including bauxite, manganese, clinker and iron ores etc), scraps of above items including hms 1&2 and steel scraps
Desulphurisation Slag is an iron slag derived from the desulphurisation skimming process. This material is an iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si), but has a stable chemistry with 75 -80% chemistry. The level of Fe% in the slag has been estimated by water displacement test. This material con offer competitive advantages respect other metal scraps: Price; Stable Chemistry; The material can be loaded loose in 20 heavy duty container. For further details feel free to contact us.
We are glad to propose 500 MT of stain less steel mill scale. Mill scale is formed on the outer surfaces during by the hot rolling lamination of stainless-steel products. At a visual inspection the material is a hard brittle sand and is mainly composed of iron oxides, mostly ferric, and is bluish black in colour, but it also contains considerable alloying elements such as chromium and nickel. The recovery ratio after melting in furnace for the most valuable alloy elements is: - Ni: 3.5 - 4.5% - Cr: 6-8% From the chemical and physical analysis performed on the scrap, and according to the European environmental rules, the material has been classified as a special non dangerous waste, listed in green list. In particular the mill scale can be classified as follows: Waste code: 10 02 10 The material is stored on cemented flooring, and it can be loaded loose in tipper trucks or containers. Chemical analysis of the material is available on request.
We are proposing about 1000 1200 Mt/ton monthly of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag : 1. >85% Fe Average 600mm Max Fraction 2. >78% Fe Average 20-300mm Fraction The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact
We are proposing about 2000tons of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag - European Code: 19.12.01 - Basel Code: B1010 - HS Code: 2619.0020 - Quantity: 2000 tons currently available - Monthly quantity: 500-1000 tons depending on production - Size: 350 1200 mm - Fe content: from 77 to 86% - C content: above 2,5-3% - Bulk density: 2,8-3,4 tons/m3 - Loading type: loose in 20 (26-27 tons on average) The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact us