Mgpr International

HDPE: HDPE cable material Property Unit Typical Value Mass density g/cm 3 0.941-0.959 Melt flow Rate(190 centidegree /2.16kg) g/10min 1.0 Tensile yield strength MPa 19.0 Flexural modulus Mpa 965 Elongation@ break % 400 Impact Embrittlement temperature centidegree MAX -118 Dielectric Constant 100KHZ 2.32 1MHZ 2.31 Loss Tangent 100KHZ MAX 0.0001 1MHZ MAX 0.0001 Volume resistivity OHM-CM MIN 1x10 15 Application Mainly used for the production of high toughness of the telephone,cable insulation material LDPE: Physical Properties Test Method Nominal Value Unit Density ISO 1183 0.921 g/cm3 Melt Mass-Flow Rate (MFR) ISO 1133 1.9 g/10min Hardness Shore Hardness (shore D) ISO 868 45 Mechanical Properties Tensile Modulus ISO 527-2 175 MPa Tensile Strength Yield, ISO 527-2 9.0 MPa Break, 13.0 MPa Tensile Strain(Break) ISO 527-2 850 % Modulus of Elasticity Internal Method 250 MPa Thermal Vicat Softening Temperature ISO 306/A50 89.0 �°C Melting Temperature (DSC) DIN 53765 108 �°C Peak Crystallization Temperature (DSC) DIN 53765 97.0 �°C Heat of Fusion DIN 53765 110 J/g Electrical Volume Resistivity ASTM D257 8.5E+15 ohm â?¢cm Dielectric Strength ASTM D149 30.0 kV/mm Dielectric Constant (60Hz) ASTM D150 2.20 % Dissipation Factor (60 Hz) ASTM D150 0.00050 LLDPE Properties Test conditon Test method Test data Unit Density 0.91 MFI 2 Drop impact strength ASTM D-1709 90 g Elongation ,vertical/horizontal ASTM D-882 600/800 % tensilestrength,thermal resistance ASTM D-1004 105/95 Kg/cm elongation ASTM D-638 930 % tensile strength ASTM D-638 180 tensile strength,vertical/horizontal ASTM D-882 380/350 Vicat softening point ASTM D-1525 103 C melting point ASTM D-2117 126 C Turbidity ASTM D-1009 12 % 45 glossness ASTM D-2457 75 %

Specification: Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating. Application: HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams. Application Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.

Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade

Product’s name: Injection mold Keyword: Injection mold,blow molding, rotary mold, roto mold. Specification: We offer to make molds for injection molding, blow molding, rotary molding roto molding. We also undertake injection, blow or rotary molding works from Toys to Big bins or water tanks, floating docks, road barrier etc. We can do custom design plastic parts or components. Water Tanks ( Roto Molding process)

Plastic Floating Dock ( Blow molding process) Keyword: Injection mold,blow molding, rotary mold, roto mold. Specification: We offer to make molds for injection molding, blow molding, rotary molding roto molding.

Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %

Item Test Condition Test Method Value Unit MFR 190C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C

Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %