Constant-fluron PTFE particle resin G401 is a free-flowing white powder composed of relatively large particles that is ideal for isobaric molding. Its most unique features are improved moldability at lower pressures and improved surface smoothness of finished parts. PTFE G401 is often used to form thicker sheets, and sometimes for the stamping of rods and pipes with thicker cross sections. Properly processed products made from high purity PTFE G401 have the superior properties typical of fluoroplastic resins Processing suggestion Fluoron PTFE is processed in two steps: preforming and sintering. The powder is first pressed into a preformed shape close to the desired molded product and then consolidated at temperatures higher than the melting point of the pure powder crystal using precise heating (sintering) and cooling cycles. The performance of the finished product depends on the bottle failure pressure, sintering time and temperature, and cooling rate. PTFE is used to make relatively large objects in molds that can be manually filled. Small particles of resin do not flow properly in the automatic feeding system.
EverFlon ®PTFE Dispersion Fine Powder F500 is a soft white polymer made from a water-based dispersion of PTFE. These fine powders have the lowest coefficient of friction, highest heat resistance, chemical resistance, electrical properties and non-stick properties of all fluoropolymers. It has the unique ability to shear a lubricating paste by extruding it into a bonded fiber matrix with useful structural integrity. EverFlon ®PTFE F500 is designed for machining at medium and high pressure rates from 100:1 to 600:1. It is particularly suitable for the production of high quality tubes, spiral tubes and wire coatings. This grade is also well suited for post-processing techniques such as flanging, welding, blow molding and turning. Processing suggestion EverFlon ®PTFE F500 is extruded using liquid processing AIDS such as naphtha. During the paste extrusion process, the powder is mixed with a lubricating agent and then compressed under light pressure (1.5-2.0 MPa[220-290 psi]) into a cylindrical pre-formed bad material. The preformed blank is placed into the barrel of the paste extruder, where the composition is passed through a finishing die under high pressure to produce foaming, tubing or wire coating. After extrusion, the product has a low density but coherent fiber structure. PTFE F500 is usually processed under heat in a step-by-step process into solid resin products, such as tubes. Heating is carried out in two steps, either simultaneously with extrusion or separately. Usually the lubricant must be removed first by heating in a temperature range of 100-300°C(212-572°F). A sintering step is then performed to melt the resin above its melting point of approximately 342°(648°F) and produce a non-porous solid PTFE resin.
Fluoron PTFE fine powder F100 is a soft, white polymer made from an aqueous dispersion of PTFE. These fine powders have the lowest friction coefficient of all fluoropolymers and the highest heat resistance, chemical resistance, electrical properties and non-stick properties. It has the unique ability to shear a lubricating paste by extruding it into a bonded fiber matrix with useful structural integrity. Fluoron PTFE F100 is designed for machining with low compression ratios of 10:1 to 300:1. It aims to promote the production of high-quality, low-density tapes Processing suggestion PTFE F100 is extruded using liquid processing AIDS, such as naphtha. During the paste extrusion process, the powder is mixed with a lubrication agent and then compressed under light pressure (1.5-2.0 MPa[220-290 psi]) into a cylindrical preformed blank. The preformed blank is placed into the barrel of the paste extruder, where the composition is passed through the finishing mold under high pressure to produce foaming, tubing or wire coating. After extrusion, the product has a low density but coherent fiber structure. PTFE F100 is usually further processed under heat into solid resin products, such as tubes. Heating is carried out in two steps, either simultaneously with extrusion or separately. Usually the lubricant must be removed first by heating in a temperature range of 100-300°C(212-572°F). A sintering step is then performed to melt the resin above its melting point of approximately 342°C(648°F) and produce a non-porous solid PTFE resin.
Supplier: Aluminum, iron, stainless steel,copper,brass,abs,pa,pc,pe,pp,peek,pmma,pom,ptfe ,resin printing,nylon powder printing.
Buyer: Aluminum,iron,stainless steel,copper,brass,abs,pa,pc,pe,pp,peek,pmma,pom,ptfe,resin printing etc.
Supplier: Virgin Teflon Ptfe Resin
DAIKIN POLYFLON PTFE Polytetrafluoroethylene Resin POLYFLON PTFE is composed of polytetrafuluoroethylene, the most commonly used fluoroploymer. PTFE has a very long chain molecular structure in which all of the hydrogen atoms of polyethylene are replaced by fluorine atoms. PTFE is superior in heat resistance and chemical resistance compared with the other plastics. These properties result from stable chemical structure consisting of only carbon and fluorine atoms with the highest electro negativity. DAIKIN PTFE M-Series: M-18/ M-18F M-111 M-112 M-139 M-531 M-532 / M-532C M-533 DAIKIN PTFE F-Series: F-104 / F-104C F-106C F-201 F-205 F-208/ F-208H F-302 DAIKIN PTFE D-Series: D-110 D-210 /D-210C D-411 D-711 DAIKIN PTFE OTHER GRADE: MG-1030 / MG-1030F MG-1040 / MG-1040F MG-1050 / MG-1050F MG-1241 / MG-1241F MG-1431 / MG-1431F MG-2030 MG-2060 MG-3060 MG-5201 / MG-5201F MG-5202 / MG-5202F MG-6020 / MG-6020F MG-6030 / MG-6030F MG-6050 / MG-6050F MG-7040 / MG-7040F MG-7060 / MG-7060F L-2 L-5 / L-5F We can give discount according to order quantity
FEATURES: Excellent chemical resistance Low coefficient of friction High operating temperature and stability Physiological insert (virgin) Excellent electrical properties Food prade ptfe powder, machine grade ptfe powder Style: molded polytetrafluoroethylene pipe APPLICATIONS: Suitable for corrosion resistant liner, seal, lining and gasket, guide rail, dielectric material for different frequency, bridge bearing slide, etc. Product thickness (mm) : 1.0mm to 6mm Product width (mm) : 1500, 1200, 1000, 500mm Density (g/cm3) : 2.2 to 2.3
Project Unit Standard Tensile strength MPa 15.0 Ultimate elongation % 150 ¡«400 Apparent density g /cm 3 2.2 ¡«2.3 Dialectic strength KV/mm 10 Resistance of surface (Working voltage 500V) 3.7 x 10 16. Thickness max:100mm Width max:1200mm Length max:1200mm.
Supplier: Polytetrafluoroethylene(PTFE) molded sheet, filled polytetrafluoroethylene(PTFE) sheet, PTFE skived sheet tape & film, polytetrafluoroethylene(PTFE) rod, colorized PTFE round red, PTFE square bar, polytetrafluoroethylene(PTFE) tube, filled PTFE products, CNC machining PTFE finish part, soft fibration PTFE(E-PTFE) sealing sheet, expanded PTFE tape(with adhesive), free flow granulated PTFE resin, pure PTFE adhesive tape, PTFE coated fiberglass fabric, PTFE coated glass fabric silicone PSA tape