LDPE Granules Low-density polyethylene (LDPE) is a synthetic resin using a high-pressure process via free radical polymerization of ethylene and is therefore also called high-pressure polyethyleneâ. It features light, flexible, good freezing resistance and impact resistance. LDPE is chemically stable. It has good resistance to acids (except strongly oxidizing acids), alkali, salt, and excellent electrical insulation properties. Its vapor penetration rate is low.
Low density polyethylene (LDPE), also known as high pressure polyethylene, is a kind of plastic material, it is suitable for thermoplastic molding processing of various forming processes, forming processing is good. LDPE is mainly used for thin film products, but also for injection products, medical devices, medicine and food packaging materials, blow molding hollow molding products and so on. Item Value Product Name LDPE Granules Other Names Low Density Polyethylene Place of Origin China Grade Standard Industrial Grade,Injection molding grade Density 0.91-0.93 g/cm³ Appearance White Granules,customized color Application Plastic,film , bag Sample provide Package 25 kg/bag,1000 kg/bag,customized packag
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
Packaging & delivery Package Type: Export Standard Packing / as per customerâ??s need Supply Ability Supply Ability 1000 Ton/Tons per Month
Virgin HDPE,LDPE,PP Granules Film Grade HDPE Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190°C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50°C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 °C Blowing molding Grade HDPE Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190°C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Granule LDPE/HDPE virgin granules for General Purpose Injection Molding Features · Good Process Ability, High Stiffness, Homopolymer. ASTM and ISO Properties Properties Unit ASTM Test Density 0.900 g/cm³ D1505 MI (230 ºC/2.16 kg) 14 g/10min D1238 Tensile Strength @ Yield 35.3 MPa D638 Elongation @ Yield 10 % D638 Flexural Modulus 1720 MPa D790B Notched Izod Impact Strength @ 230 ºC 25.5 J/m D256A Heat Deflection Temperature @ 4.6 kg/cm² 99 ºC D648 Rockwell Hardness (R-Scale) 97 D785A Water Absorption after 24 hours 0.020 % D570 Fabrication · Equipment Raw or Screw Injection Machine · Techniques Standard Processing Advantages · Good Process Ability · High Stiffness · Good Heat Deflection Temperature · Microwaveable for Food Reheating Purposes Applications · Closures · Containers · Housewares · Medical / Healthcare Applications · Toys · Writing Instruments
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
Virgin & Recycled Low Density Polyethylene LDPE Granules
Specification: Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating. Application: HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams. Application Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.