Corundum and corundum-mullite AL2O3 porcelain balls and porcelain lining bricks are most suitable to be used as grinding media and drum linging of various grinding equipments because of its excellent properties such as high strength,high hardness,high abrasion resistance, high gravity, small size,high temperature resitance. Application: It is mainly used for non-metalmineral products extra refining, it is ideal grinding media for stirring grinding, sand grinder and vibeation grinding. And it is widely applied in ceramics, paint, ink coatings,dyes, rubber and power industries. Performance: 1. High density and hardness,impact resistance, low loss rate, smooth surface and no contamination to products. 2. Fine chemical stability, anti-corrosion.. 3. Under condition of appropriate ball size ration, it can achieve high grinding efficiency with material results D¡Ü2¦Ìm. 4. High performance and low price. Wooden box.
Active alumina can be used widely as excellent de-fluorine agent in drinking water, in the production of acid and in the production of alky benzene and the de-acid regeneration agent of oil transformer, in addition, active aluminum can also be used as drying agent,purifying agent, catalyst and their carrier in the industy of fertilizer, petroleum and chemisty. Active alumina cann¡¯t dissovle in water and organic solvent, but it dissolves in strong acid and alkli. It is tasteless and nonpoisonous and possesses high crush strength, strong hygroscopicity and can maintain original state instead of breaking into pieces after sucking up moisture. Content: AL2O3 Appearance: White, round Size: Dia3-Dia6 Strength: 120N/Grain Water absorption (m/m): 20+/-2 Packing density (kg/L): 0.7+/-0.05 Specific surface (m/g2): 300+/-20 Abrasion: 0.1 Pore volume: 0.4+/-0.05. Wooden box.
Product: 92% alumina ball Specification: 30 mm, 40mm, 50 mm, 60mm Bulk density:í²3.6 g/cm3 Wear rate:ín0.12íd Hardness:8-9 mohs Compression strength:í²2000 Water absorption:ú+0.01 Color:white Packing: 25kg/bag, 1.25ton/pallet, 25ton/container.
RP-99 is widely used as catalyst and adsorbent bed support in refining, petrochemical and gas processing applications, where low silica content or high density is required. Available sizes: 3mm, 6mm, 10mm, 13mm, 19mm, 25mm, 38mm, 50mm, 75mm Chemical composition: SiO2 í_0.20% Al2O3 í¦99.2% CaO 0.08% TiO2 0.05% MgO 0.05% K2O 0.04% Na2O 0.09% leachable Iron less than 0.01% Physical properties: Free volume (%) 40 Water absorption (wt. %) ú+3 Hardness, Mohsí» ú+8 Particle density ( gm/cc ) 3.5 Bulk density (kg/m3) 1900-2100 Maximum operating temperture(íµ) 1800 Crush Strength size Crush strength, lbs(kg) 3mm (1/8í¦) 200 (90) 6mm (1/4í¦) 450(205) 10mm (3/8í¦) 880 (400) 13mm(1/2í¦) 1870 (850) 19mm(3/4í¦) 2860(1300) 25mm(1í¦) 3740(1700) 30mm(1-1/4í¦) 3740(1700) 38mm(1-1/2í¦) 4840(2200) 50mm(2í¦) 5500 (2500).
The technical ceramic alumina ball with the characteristics of high density,high hardness,low abrasion,good anti-seismic stability, corrosion resistanceis which can improve the ball milling efficiency of the ball mill, reduce the pollution of glaze slurry, improve the product quality and economic benefits of the enterprise that is made of selected high-quality raw materials, advanced molding technology and calcined in high-temperature tunnel kiln at 1600 �ºC. It is an ideal grinding medium for processing glazes, billets and various mineral powders. The technical ceramic alumina ball is used in the grinding process of ceramic glaze, including the grinding process of ball mill. The semi-finished glaze slurry after grinding by ball mill is put into the mixing mill for fine processing, so that it becomes glaze. Or put the glaze powder directly into the agitation mill for fine processing to make it into glaze. We can supply 65-70% alumina content classified as medium alumina ball, 75% - 80% alumina content called medium high alumina ball, and more than 90% alumina content is high alumina ball. Among them, the high alumina ball is subdivided into 90% porcelain, 92% porcelain, 95% porcelain and 99% porcelain.
Maheshwari A 99.9 aluminum oxide beads have a very high purity with an Al2O3 content of > 99.9% and with minor secondary components of < 1000 ppm. These beads are suitable for the preparation and wet grinding of high-quality aluminum oxide raw materials for e.g. special technical, electrical and optical components and high-purity coatings made from special suspensions. Very small beads down to 0.1 mm and sizes up to 60mm are available of this type. Technical Data: High purity 99.9 % Al2O3 Specific Weight 3.8 kg/dm3 Bulk Density 2.3 kg/dm3 Roundness 0.93 (ratio width/length (xmin/xmax)) Colour: White satin smooth Fields of application In the mining industry A 99.9 ceramic beads are used for the grinding of minerals and precious metals. Quality attributes The ceramic beads type A 99.9 have a dense sintered structure, a smooth surface, high roundness and high hardness.
High alumina ball means alumina ball with aluminium oxide content higher than 90%, high alumina ball is high efficiency grinding media in today industry. The high alumina ball works together with the high alumina mill linings brick will benefits you: > Less grinding time, doubled productivity. > Less wear loss of the ball and linings, more clean you final product keep. > Longer service life, less down time Physical Properties: 1) Bulk Density : 60mm > 3.65, 50mm > 3.65, 40mm > 3.65, 30mm > 3.65, 20mm > 3.63 2) Self Wearloss (24h) : < 0.04 3) Water absorption : < 0.1% 4) Hardness (M0hs) : 9 5) Service Temp : > 1600 C 6) Color : White
High alumina ball Al2O3(%):99.3 Bulk density(g/cm³):3.92 Wear rate(%):0.006 FEATURES: Higher density; Higher hardness; Higher wear resistance; Higher grinding efficiency. APPLICATION: Minerals industry Chemical industry Metallic minerals like copper, silver, nickel, gold, zinc, etc. Non-metallic minerals like calcium carbonate, kaolin clay, zirconium silicate, TiO2 and other minerals White pigments, coatings, paints, inks, etc. -
Refractory ball are used by users as refractory ceramic balls. They are made of industrial alumina and refractory kaolin. They are scientifically formulated, formed and calcined at high temperature. The refractory balls are widely used in high and low temperature converters and reformers in fertilizer plants. The push-plate kiln ball acts to disperse the gas and liquid, and to support, cover and protect the catalyst. Refractory balls can also be used in steel mill hot blast stoves and heating converters. Refractory ball are divided into two types, ordinary and high-alloy. The former is often used in converters and converters in industries such as sulfuric acid and fertilizers, while the latter is used in industries such as steel. The refractory ball has the advantages of high strength, wear resistance, small thermal conductivity, high efficiency and good chemical stability, and is not easy to be broken when the temperature is drastically changed. The service life is long, and the cleaning equipment is also convenient after use.
1. Product Description The alumina grinding ball has been widely used in ball mills as abrasive media for ceramic raw materials and glaze materials in ceramic factories, cement factories, enamel factories and glass work owing to the excellence of high density, high hardness, high wear resistance. During the abrasive/grinding processing, ceramic balls will not be broken, it will not pollute the 95%material to be grinded. 2. Type According to the content of aluminum: 60-70%, 65-75%, 92%, 95%. According to the specification: 10mm-75mm. 3. Features: 1) High density. 2) High hardness. 3) Very low wear resistance. 4) Widely used for milling minerals and ceramics. 5) High efficiency, lower cost 6) Three kinds of high alumina grinding balls and one kind of alumina lining available. 7) High alumina grinding balls (white surface and body): a) Usual Al2O3: 92% b) Density: 3.62 - 3.65g/cm³ c) Grinding lose (abrasion): 0.015% (0.15g/kg.h) d) Applications: milling and grinding any kind and color of ceramic materials and minerals, including sanitary wares, white glaze materials, iron ores, and copperores e) We call it white ball 8) High alumina grinding balls (white yellowish surface and body): a) Usual Al2O3: 65 - 70% b) Density: 2.90 - 3.05g/cm³ c) Grinding lose (abrasion): 0.03% (0.3g/kg.h) d) Applications: milling and grinding any kind and color of ceramic materials, including sanitary wares and white glaze materials e) We call it yellowish ball 9) High alumina grinding bricks and lining (white surface and body) a) Usual Al2O3: 92% b) Density: 3.58 - 3.65g/cm³ c) Grinding lose (abrasion): 0.015% (0.15g/kg.h) d) Applications: milling and grinding any kind and color of ceramic materials and minerals, including sanitary wares, white glaze materials, iron ores, and copperores e) We call it white brick or white lining. 25kg/bag or 1MT/bulk bag.