Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
Specifications: 1. HDPE 2. Transparent granule 3. We have all grades - Injection, Film and Moulding, all Density and Melt Flow Rate.
Quick Details Place of Origin:China Density:0.946-0.957g/cm3 Type:100% Virgin HDPE Material Appearance:Transparent Granular Application:Shopping Bag Packing:25kg/bag Grade:TR144 / HTA001 / F4055 / F00952 Supply Ability Supply Ability:400 Metric Ton/Metric Tons per Month
Property itemstest condition test method test datadata unit Basic property mfr astm d-12380.035g/10min Density astm d-7920.957g/cm3 Water absorption astm d-570>0.01% Mechanical propertyforming shrinkage linearkpic method1.5-2.5% Tensile strength astm d-638400kgf/cm2 Fracture stretching rate astm d-638
Virgin HDPE,LDPE,PP Granules Film Grade HDPE Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190°C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50°C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 °C Blowing molding Grade HDPE Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190°C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Granule LDPE/HDPE virgin granules for General Purpose Injection Molding Features · Good Process Ability, High Stiffness, Homopolymer. ASTM and ISO Properties Properties Unit ASTM Test Density 0.900 g/cm³ D1505 MI (230 ºC/2.16 kg) 14 g/10min D1238 Tensile Strength @ Yield 35.3 MPa D638 Elongation @ Yield 10 % D638 Flexural Modulus 1720 MPa D790B Notched Izod Impact Strength @ 230 ºC 25.5 J/m D256A Heat Deflection Temperature @ 4.6 kg/cm² 99 ºC D648 Rockwell Hardness (R-Scale) 97 D785A Water Absorption after 24 hours 0.020 % D570 Fabrication · Equipment Raw or Screw Injection Machine · Techniques Standard Processing Advantages · Good Process Ability · High Stiffness · Good Heat Deflection Temperature · Microwaveable for Food Reheating Purposes Applications · Closures · Containers · Housewares · Medical / Healthcare Applications · Toys · Writing Instruments
Specification: Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating. Application: HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams. Application Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.