Specifications: 1 Calcium Hydroxide Ca(OH)2 90% 2 Calcium Hydroxide Ca(OH)2 90% 3 Calcium Oxide CaO 68% 4 Calcium Carbonate CaCO3 2% 5 Magnesium Oxide MgO 0.4% 6 Acid Insoluble SiO2 0.4% 7 Alumina Al2O3 0.05% 8 Iron Fe2O3 0.05% 9 Chloride Cl Traces 10 Moisture 0.3% 11 Mesh (BSS) 250-300
Specifications : Percent of lime as CaO - >90 Acid Insoluble % - 1.0 (max) Magnesia as MgO % - 1.0 (max.) Metal Oxides as Fe2O3 & Al2O3)% -0.15(max.) L.O.I (Loss on Ignition)% - 3.0 (max.) Reactivity (4N HCl) - 400 ml Brightness % - >80 Sizes % - 0 - 3 mm 0 - 10mm 10 - 50mm
SPECIFICATION +97 +96 +94 +93 +92 +90 (A) +90 (B) +85 +80 +75 +70 +60 % OF AVAILABLE LIME AS CA(OH)2 97 96 94 93 92 91 90 85 80 75 70 60 % OF AVAILABLE LIME AS CA(OH)2 97 96 94 93 92 91 90 85 80 75 70 60 % OF AVAILABLE LIME AS CAO 73.40 72.64 71.13 70.37 69.62 68.86 68.10 64.32 60.54 56.75 52.97 45.40 % ADD INSOLUBLE (MAX.) 0.08 0.1 0.15 0.2 0.5 0.8 1.00 1.3 2.5 3 4 5.7 % IRON ALUMINA IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces % MAGNESIA AS MGO 0.04 0.5 0.55 0.6 0.7 0.8 1 1 1.20 1.4 2 2 MESS (BSS) 600 500 450 400 350 300 250 250 200 200 150 150 Packing Laminated PP/HDPE Bag, Jumbo Bags
Mumal Microns are a reputed manufacturer, supplier and trader of high quality hydrated lime powder in India. We use latest technology
Calcium Oxide (Lime) is made by thermal decomposition of high purity limestone above 900�°C, the process is called calcinations or lime burning. It is also referred to as burnt lime or quick lime. Price: INR 5,000/- to 20,000/-
Specification 700 500 300 250 200 Total CAO 90% 88% 86% 85% 82% %Acid Insoluble (Max.) 0.7 1 1.2 1.25 1.25 R2 O3 In Traces In Traces In Traces In Traces In Traces %Magnesia AS MGO 1.20 1.40 1.45 1.50 1.50 Mesh (Passing) 99% 99% 99% 99% 99% SLAKING TEMPERATURE 600ML WATER 150GM Sample 15 Min 15-20 Min 15-20 Min 20-25 Min 30 Min
Lime stone BUCHING 600x150mm chocolate
Hydrated lime
Quicklime is Calcium Oxide (CaO) also known as burnt lime. The molecular weight of CaO is 56.08 g/mol and the boiling point is around 2600 degree