GGBFS Ground granulated blast furnace slag (GGBFS) The ground granulated blast furnace slag (GGBFS) is a by-product of iron manufacturing which when added to concrete improves its properties such as workability, strength and durability. This material is obtained by the heating of iron ore, limestone and coke at a temperature about 1500 degree Celsius. The process is carried out in a blast furnace. The formation of GGBFS is not direct. The by-product of iron manufacturing is a molten slag and molten iron. The molten slag consists of alumina and silica, also with the certain amount of oxides. This slag is later granulated by cooling it. For this, it is allowed to pass through a high-pressure water jet. This result in quenching of the particles which results in granules of size lesser than 5mm in diameter. The main constituents of blast furnace slag are CaO, SiO2, Al2O3 and MgO. These are the minerals that are found in most of the cementitious substances. The particles are further dried and ground in a rotating ball mill to form a fine powder, known as ground granulated blast furnace slag cement. Now different methods can be employed to perform the main process called as the quenching. Applications & Benefits of GGBFS: In concrete: The incorporation of ground granulated blast furnace slag in concrete manufacture gains many advantages which are mentioned below: GGBFS in concrete increases the strength and durability of the concrete structure. It reduces voids in concrete hence reducing permeability GGBFS gives a workable mix. It possesses good pumpable and compaction characteristics The structure made of GGBFS constituents help in increasing sulphate attack resistance. The penetration of chloride can be decreased. The heat of hydration is less compared to conventional mix hydration. The alkali-silica reaction is resisted highly. These make the concrete more chemically stable. Gives good surface finish and improves aesthetics. The color is more even and light. Lower chances of efflorescence. The maintenance and repair cost of structures are reduced thus increasing the life cycle of concrete structures. Unlike cement, GGBFS does not produce carbon dioxide, sulphur dioxide or nitrogen oxides. White Cement: White Portland Cement is of high quality, whiteness and strength, it essentially has the same properties and characteristics as gray cement, except for color. It is widely used in numerous applications such as precast concrete, cast-in-place concrete, terrazzo, median barriers, curbs, tile grout, paint, masonry units, swimming pools, glass fibre reinforced surface bonding mortars.
We are proposing about 2000tons of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag - European Code: 19.12.01 - Basel Code: B1010 - HS Code: 2619.0020 - Quantity: 2000 tons currently available - Monthly quantity: 500-1000 tons depending on production - Size: 350 1200 mm - Fe content: from 77 to 86% - C content: above 2,5-3% - Bulk density: 2,8-3,4 tons/m3 - Loading type: loose in 20 (26-27 tons on average) The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact us
This Cast Iron slag is a by-product derived from the production of thermal insulating products. The byproduct is a ferrous slag which can be utilised in an electric arc furnace to produce crude steel. Physical Description On visual inspection, it appears to be made up of irregular shapes. Dimension: 500mm -800mm Chemical Composition Its chemical composition is homogeneous and stable with Fe contents in the range of 90 +/- 5% and P contents < 0.6% S around 0.15% and C% around 3.5%. Packing: Loose in container Loading: in 20 Container For further information, please feel free to contact us.
We are proposing about 1000 1200 Mt/ton monthly of iron slag derived from the desulphurisation skimming process. This material is a iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si). In order to enhance its usability, the material is processed and screened. We can propose two specifications of Iron Slag : 1. >85% Fe Average 600mm Max Fraction 2. >78% Fe Average 20-300mm Fraction The level of Fe% in the slag has been estimated by water displacement test. For any further information please feel free to contact
Desulphurisation Slag is an iron slag derived from the desulphurisation skimming process. This material is an iron by- product that is encapsulated in varying levels of contaminants (S,Mg,Si), but has a stable chemistry with 75 -80% chemistry. The level of Fe% in the slag has been estimated by water displacement test. This material con offer competitive advantages respect other metal scraps: Price; Stable Chemistry; The material can be loaded loose in 20 heavy duty container. For further details feel free to contact us.
About THE Product : Blast furnace slag is used in the production of cement (iron Portland and blast furnace cement). Air-cooled blast furnace slag is formed by allowing the molten slag to cool relatively slowly under ambient conditions; final cooling can be accelerated with a water spray. The cooled material is hard and dense, although it can have a vesicular texture with closed pores. After crushing and screening, air-cooled slag can be used in several applications. Granulated slag is formed by quenching molten slag in water to form sand-sized particles of glass. The disordered structure of this glass gives the material moderate hydraulic cementitious properties when very finely ground into granulated blast furnace slag, but if it can access free lime, the granulated blast furnace slag develops strong hydraulic cementitious properties. Pelletized or expanded slag is cooled through a water jet, which leads to rapid steam generation and the development of innumerable vesicles within the slag. The vesicular texture reduces the overall density of the slag and allows for good mechanical binding with hydraulic cement paste. Blast Furance Slag is a nonmetallic co-product which is produced in the process of iron manufacturing, Granulated Blast Furnace Slag is a glassy granular material formed when molten blast furnace slag is rapidly cooled by direct water. Rapid cooling prohibits the formation of crystals and forms glassy, non-metallic, silicates and alumino silicates of calcium. GBFS : (Granulated Blast Furnace Slag) Source : Granulated BF Slag From Gujarat State, India Supply Quantity : 50,000 Metric Tons Per Month Packing: Bulk Parameters (% BY MASS) CaO 30-38 Al2O3 15-20 SiO2 30-40 Glass Content 85-97 MgO 8-11 Fe2O3 0.5-1.5 Moisture 10 MAX Size -5mm Min 95, +5 mm Max 5 Relative Gravity 2.9 Bulk Density(Bagged) 1200 KG/M3
Supplier: Cast iron skulls, cast iron borings and turnings, steels skulls, eaf skulls, plate iron, mill scale, metal scrap, incinerated scrap (e46)
Supplier: Aluminium ( ingots, t bars, sows, rods), copper (cathodes, cakes, billets, ingots, rods), lead (ingots), nickel (cathodes both cut and uncut briquettes, pellets, discs, etc.), tin (ingots, etc.), zinc (ingots both regular size and jumbos), steel billets (all types including crc, hrc, hdgc, plates, sheets), concentrates and ores for above items including bauxite, manganese, clinker and iron ores etc), scraps of above items including hms 1&2 and steel scraps
Buyer: Aluminium ( ingots, t bars, sows, rods), copper (cathodes, cakes, billets, ingots, rods), lead (ingots), nickel (cathodes both cut and uncut briquettes, pellets, discs, etc.), tin (ingots, etc.), zinc (ingots both regular size and jumbos), steel billets (all types including crc, hrc, hdgc, plates, sheets), concentrates and ores for above items including bauxite, manganese, clinker and iron ores etc), scraps of above items including hms 1&2 and steel scraps
We are supplier and exporter of Copper Slag. Copper slag is a low cost expendable abrasive suited for open blast cleaning and due to its low silica content it does not pose the health hazards created by silica sand. Its sharp, hard particles can provide a fast cleaning action and an excellent surface profile. It is available in various sizes Copper slag is abrasive blasting grit made of granulated slag from metal smelting processes (also called iron silicate). Copper slag abrasive is suitable for blast cleaning of steel and stone/concrete surfaces, removal of mill scale, rust, old paint, dirt etc. Suitable for SA-3, SA-2 and SA-2. Copper slag blasting media/grit is manufactured of the granulated slag of copper refineries, and used for blast-cleaning of metal surface. In different industries it is called different names abrasive powder, grit, copper slag grit, mineral grit, grinding grains, etc.