Handan Chaoyo Metallurgical Materials Co., Ltd

RP Graphite electrode,HG Graphite electrode,UHP graphite electrode Resistivity: 4.8-6 3.5-5 Bending Strength:10-14 Mpa 20-24 MPa Young's Modulus: Electrode 9.0-13 Nipple 15-18 Bulk Density: Electrode 1.68-1.74 Nipple: 1.77-1.82 CTE: Electrode 1.1-1.4 Nipple 0.9-1.2

Artificial graphite electrode is made of high-quality low ash materials, such as petroleum coke, needle coke and coal pitch.after calcining,burdening,kneading,forming,baking and pressure impregnation, graphitization and then precision machined with professional CNC machining.such of the products own characteristics with low resistivity, good electrical conductivity ,low ash, compact structure,good anti oxidation and high mechanical strength, so it is the best conductive material for electric arc furnace and smelting furnace.

HP Size and Tolerance Diameter (mm) Length (mm) Nominal diameter Actual diameter Nominal length Tolerance Short feet length mm inch max min mm mm max min 200 8 209 203 1600/1800/ 2000/2200/ 2400/2700 ±100 -100 -275 250 10 258 252 300 12 307 302 350 14 357 352 400 16 409 403 450 18 460 454 500 20 511 505 550 22 556 553 600 24 613 607 Physical and Chemical Index of HP Items unit Diameter: 250-600mm Standard Test data Electrode Nipple Electrode Nipple Electrical resistance μΩm 6.5-7.5 6.0 6.0-7.0 5.5 Flexure strength Mpa 9.8-10.5 14 12-15 15-18 Modulus of elasticity GPa 12 16 12 14 Ash content % 0.2 0.2 0.2 0.2 Apparent density g/cm3 1.6 1.7 1.68-1.73 1.75 Factor of expansion(100-600) x10-6/ 2.4 2.2 2.2 2.0 Operating instruction 1. Use special hoist tools to hoist graphite electrode. It is strictly forbad to prize electrode ends up with crowbar. It must be handled with great care during transport to avoid being struck. 2. Graphite electrode must be kept away from being moistened or wetted by rain, snow and water, and must be kept dry. 3. Carefully checking before making connection, make sure that socket and nipple thread is not damaged, nipple pitch plug is in. 4. Blow the nipple and socket threads with compressed air. 5. It must be dried in the furnace before use, the drying temperature in the furnace should be less than 150,the drying period should be more 30 hours 6. Graphite electrode must be connected and contacted closely and straightly.Use moment spanner for connecting electrode with suitable force. Mustnt decline. 7. The holding device must hold the electrode tightly, good contact and no arc. 8. To avoid the electrode breakage, put the large materials in lower part and small materials in the upper part. Insulating materials should not be put into the furnace. The working current of electrode must be conformity with the allowable current of electrode in the instructions.

China dia 550mm HP graphite electrode plant price manufactures China dia 550mm HP graphite electrode plant price manufactures

HP graphite electrode is mainly used for ultra high power electric arc furnaces with the current density range of 18-25A/cm2. >Anti-oxidation treatment for longevity. >High-purity,high-density,strong chemical stability. >High machining accuracy,good surface finishing. >High mechanical strength,low electrical resistance. >Resistant to cracking & spalling. >High resistance to oxidation and thermal shock.

Petroleum coke is a carbonaceous solid derived from oil refinery cocker units or other cracking process. Petroleum coke can be devided into low sulfur petroleum coke,sulfur petroleum coke and high sulfur petroleum coke,petroleum coke for making graphite,smelting and chemical industries.

Petroleum coke is a carbonaceous solid derived from oil refinery cocker units or other cracking process. Petroleum coke can be devided into low sulfur petroleum coke,sulfur petroleum coke and high sulfur petroleum coke,petroleum coke for making graphite,smelting and chemical industries.

UHP 400mm*1800mm UHP 450mm*1800mm Used in steel, cement and glass manufacturing, expanded graphite - based sealing gaskets, graphite grease, braid, brushes, brake lining, etc.