HDPE: HDPE cable material Property Unit Typical Value Mass density g/cm 3 0.941-0.959 Melt flow Rate(190 centidegree /2.16kg) g/10min 1.0 Tensile yield strength MPa 19.0 Flexural modulus Mpa 965 Elongation@ break % 400 Impact Embrittlement temperature centidegree MAX -118 Dielectric Constant 100KHZ 2.32 1MHZ 2.31 Loss Tangent 100KHZ MAX 0.0001 1MHZ MAX 0.0001 Volume resistivity OHM-CM MIN 1x10 15 Application Mainly used for the production of high toughness of the telephone,cable insulation material LDPE: Physical Properties Test Method Nominal Value Unit Density ISO 1183 0.921 g/cm3 Melt Mass-Flow Rate (MFR) ISO 1133 1.9 g/10min Hardness Shore Hardness (shore D) ISO 868 45 Mechanical Properties Tensile Modulus ISO 527-2 175 MPa Tensile Strength Yield, ISO 527-2 9.0 MPa Break, 13.0 MPa Tensile Strain(Break) ISO 527-2 850 % Modulus of Elasticity Internal Method 250 MPa Thermal Vicat Softening Temperature ISO 306/A50 89.0 �°C Melting Temperature (DSC) DIN 53765 108 �°C Peak Crystallization Temperature (DSC) DIN 53765 97.0 �°C Heat of Fusion DIN 53765 110 J/g Electrical Volume Resistivity ASTM D257 8.5E+15 ohm â?¢cm Dielectric Strength ASTM D149 30.0 kV/mm Dielectric Constant (60Hz) ASTM D150 2.20 % Dissipation Factor (60 Hz) ASTM D150 0.00050 LLDPE Properties Test conditon Test method Test data Unit Density 0.91 MFI 2 Drop impact strength ASTM D-1709 90 g Elongation ,vertical/horizontal ASTM D-882 600/800 % tensilestrength,thermal resistance ASTM D-1004 105/95 Kg/cm elongation ASTM D-638 930 % tensile strength ASTM D-638 180 tensile strength,vertical/horizontal ASTM D-882 380/350 Vicat softening point ASTM D-1525 103 C melting point ASTM D-2117 126 C Turbidity ASTM D-1009 12 % 45 glossness ASTM D-2457 75 %
Specification: Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating. Application: HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams. Application Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.
Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade
We also have the following products: - HDPE Clear/Natural Regrind (clean and washed) - HDPE Clear/Natural Scrap Baled - HDPE White Regrind/Baled (clean and washed) - HDPE Milk Bottle Regrind - LDPE Film Baled 100, 98/2 and 95/2 - LDPE Clear/Natural Regrind - LDPE White Regrind Specifications HDPE drum scrap 1 ISO,SGS test 2 free sample 3 manufacture 4.factory price HDPE drum scrap 1.Hot water washed and no label, no any contaminant 2.dry and clear flakes 3.white,blue, red, yellow and so on 4.from drums PE FLAKE 1.DENSITY:0.956G/CM3 2.MELT MASS-FLOW RATE:0.04G/10MIN 3.HS CODE:3901902000 4.ELONGATION AT BREAK %500
HDPE , LDPE , LLDPE ,PP, PET Resin Available For Immedieate Shipment , Virgin And Reprocessed Grade Available
Film grade, pipe grade, bottle grade and so on... In 25kg bags
we specialize in this field for many years,with good quality and pretty competitive price.such as PET Chips, HDPE, LDPE, LLDPE ABS, AS, EPS, EVA, PP, PS, PVC, PE, HIPS, GPPS Hope to find a way to cooperate with you
This is Bella Yang from Hebei Zongyan Technology Co.,Ltd.. Glad to hear that you're on the market for PET Chips.we specialize in this field for many years,with good quality and pretty competitive price.such as Polyester Staple Fiber, Polyester fibers, Polypropylene Staple Fiber, Polypropylene fiber(PP fiber), PET Chips, HDPE, LDPE, LLDPE,etc.
We are suppliers of PP , HDPE, LDPE GRANUELS in all major countries
We are deal in plastic like HDPE,LDPE,PP,PET,strip etc , and also supply tyre scrap capacity 60 ton/month .
