Al2O3 Content (%): 75%-90% Refractoriness (Degree): Common (1580°< Refractoriness< 1770°) Model Number: GLM- FIRE CAST Brand Name: GLM
Refractory temperature: 1800 () Compressive strength: strong (mpa) Specifications: according to customer requirements (mm) Gongyi taurus refractory material factory is a professional refractory materials manufacturers and refractory materials suppliers, mainly supply refractory bricks, unshaped refractories, silicon carbide refractory castable, castable refractory cement, pouring material, castable refractory concrete, silica ramming mass etc. Series of refractory materials products, sincerely welcome everyone to visit.
refractory castable Casting is a kind of refractory material made of granular and powdery material, and add a certain amount of binder and water together. It has a high mobility, suitable for casting construction, and no need to heat can be hardened unshaped refractory.z
Non-stick aluminum refractory castable or non-stick castable, the non-stick aluminum castable combines with the feature of inorganic binder, add a certain amount of insoluble in aluminium new composite refractory material, control the liquid aluminum erosion of refractory, non-stick aluminum castable with high volume density, high strength, not for the nature of the aluminum liquid wetting, can significantly reduce the corundum phase anomaly grew up and molten metal and permeability of materials.Suitable for the bottom of aluminum melting furnace, wall of furnace, slag-scraping slope, chute, aluminum water bag and degassing box, etc.
The improvement of the performance of low cement casting material is actually the application of micro powder technology. There is a gap between the stability of low cement castable and that of laboratory castable.Low cement castable easy to occur problems are: 1, poor construction performance, poor liquidity;2. The hardening speed varies greatly, and there is quick setting or non-setting;3, easy to burst in baking;4. Abscission occurs;5. Low strength and poor wear resistance.These are caused by refractory castable products abnormal damage and other quality problems. Low cement refractory castable itself in addition to wear resistance, refractory aggregate, is used with good raw materials fine powder and ultrafine powder, cement and admixture, etc., through adjusting the proportion of each component, improve the high temperature performance of castable, thereby improve the strength of refractory castable. Low cement castable key construction, should pay attention to is: (1) do not arbitrarily increase the water content of refractory castable, (2) mold support set too high, leading to castable water content is too large and vibration compaction;(3) No mold shall be set during lining construction of feeding pipe, and castable material shall be manually daubed;(4) In order to save the mold, the maintenance is less than 48 h to remove the mold, resulting in the casting cracking or internal damage;(5) The material, shape, size, welding quality, quantity, anti-expansion treatment and unreasonable expansion joints of the anchoring parts;Do not follow the operational sequence of dry stirring, wet stirring and feeding, directly mix the dry and wet materials, resulting in the castable is not fully mixed evenly, part of the material is not wetted by water, making the castable has no strength. There are also key water issues, to use tap water, to avoid the introduction of acid and base impurities, gradually add, in order to make the dispersant in the powder to play a full role.Excessive water addition will directly lead to a significant decline in the strength of refractory castable construction, and in the field construction the water addition tends to exceed the degree of artesification.The pouring body itself is easy to appear when the ambient temperature rises rapidly, the baking burst, resulting in large area of damage.Once the temperature of the castable itself is below 5 the castable will still have no strength even after curing for 24 hours.The construction and maintenance shall be carried out in strict accordance with the 48-hour mold removal mechanism. In dry areas, water and wet maintenance shall be carried out; in cold areas, airtight heating maintenance shall be realized within 48-hour maintenance to ensure the maintenance temperature. In a word, if the above points can be achieved step by step in accordance with the requirements, it will certainly improve the performance of low cement casting.
Refractory temperature: 1800 () Compressive strength: strong (Mpa) Specifications: According to customer requirements (mm) Molten copper furnace refractory castable is suitable for oil refinery catalytic cracking equipment cyclone separator, double slide valve, riser, dilute phase tube, foot, etc., other chemical equipment, such as ammonia pouring in a conversion furnace lining, two paragraphs.
High-alumina refractory castable is high-alumina raw materials for the aggregate and powder, adding the binder made of refractory castable. With high mechanical strength and good thermal shock resistance, abrasion resistance and other properties, mainly used for boilers, blast furnace hot stove, heating furnace, ceramic kiln and other furnace lining. Gongyi taurus refractory material factory is a professional refractory materials manufacturers and refractory materials suppliers, mainly supply refractory bricks, unshaped refractories, silicon carbide refractory castable, castable refractory cement, pouring material, castable refractory concrete, silica ramming mass etc. Series of refractory materials products, sincerely welcome everyone to visit.
Light refractory castable is made of lightweight refractory aggregate, refractory powder, binder and admixture, etc., in the construction of water or with a binder solution into the castable castable unshaped refractory. Generally used as thermal insulation equipment, lining to reduce energy consumption. Gongyi Taurus Refractory Material Factory is a professional refractory materials manufacturers and refractory materials suppliers,mainly supply Refractory Bricks,Unshaped Refractories,Silicon Carbide Refractory Castable,Castable Refractory Cement,Pouring Material,Castable Refractory Concrete,Silica Ramming Mass etc. series of refractory materials products, sincerely welcome everyone to visit.
Refractory castable is one of the unshaped refractory materials. It is made of refractory aggregate, refractory powder, binders and other additives. It is loose, no fixed shape, has high liquidity, casting and vibration molding, can use directly or use after add appropriate water or other liquid. It is one of the new type refractory material of don't need calcination.
Mullite Steel Fiber Reinforced Refractory Castable is made from high quality synthetic mullite aggregate, high temperature filler, ultrafine powder and high temperature binder combination, with high temperature structure strength, high temperature Low creep rate, low coefficient of thermal expansion, anti-peeling, strong corrosion resistance, quick release, anti-burst, thermal shock stability and other advantages, successfully used in cement kiln before and after the kiln, industrial kiln lining, Ditch cover lining and other projects, the effect is outstanding.