Performance characteristics: Cold work mould steel, quench-hardening ability, the hardness of tempering, wear resistance and strength are better than cr12. Applications: All kinds of cold blunt mould and tools, such as punching concave die, trimming, roll mould, steel plates,deep drawing die, circular saws, standard tools and gauge, thread rolling mould and so on. Chemical Composition (%): C 1.45 1.70 Si 0.40 Mn 0.40 S 0.030 P 0.030 Cr 11.00 12.50 Ni 0.25 Cu 0.30 V 0.15 0.30 Mo 0.40 0.60 Heat Treatment Standard: 1) Quenching, 950 ~ 1000 centigrade cold oil 2) Quenching 1020 , 200 tempering 2 hours. Mechanical properties: Hardness: annealing, 255 ~ 207 HB, creasing diameter 3.8 ~ 4.2 mm; Quenching,more than or equal to 58 HRC Delivery status: Annealing. Under the client's requirement.
Performance Characteristics: 1, Good toughness; 2, High abrasive resistance; 3, High hardenability; 4, less deformation in quenching. Applications: 1. Suitable to make the punch dies or drawing dies which are complicated in shape and high in precision; 2. Suitable toHigh-speed punch head and cold forging dies; 3. Suitable to make the blanking dies and punching dies with a thickness. Chemical Composition (%): C 0.90/1.10 Mn 0.40 Si 0.80/1.20 Cr 7.50/8.50 P 0.025 S 0.020 Mo 1.80/2.0 V 0.20/0.50 Delivery Condition: Annealing. Under your requiremnet.
Performance Characteristics: Widely used cold work mould steel, with good quench-hardening ability, good wear resistance , as well hot workability. Applications: Making efficient blanking mould, stamping mould, all kinds of scissors , cold shearing , drilling bushing , gauge, wortle, coining die, thread rolling die, screw thread rolling die, cold extrusion dies . Chemical Composition : C 2.00¡«2.30 Si 0.40 Mn 0.40 S 0.030 P 0.030 Cr 11.50¡«13.00 Ni 0.25 Cu 0.30 Co 1.00 Heat treatment standard: (1) Quenching, 950 ~ 1000 centigrade cold oil; (2) Quenching 980 centigrade, cold oil, 180 centigrade tempering 2 hours Annealing temperature: 800-850 Centigrade. Annealing hardness: 248 HB Max. Destressing temperature: 650 Centigrade Approx. Hot forming temperature: 1050-850 Centigrade. Quenching temperature: 940-970 Centigrade. Hardening media: oil quenching, salt bath 220-250 Centigrade or 500-550 Centigrade, air or compressed air. Quenching hardness: 63-65 HRC. Delivery condition : Annealing. Under the client's requirement
Performance characteristics: Widely used cold work mould steel, belongs to ledebrite steel .Good hardenability and rigidity, excellent wear resistance; minimal distortion. Applications: Various tool & die, such as a variety of punching die, trimming die, steel tensile modulus, trim mold, drawing die, slot die, thread twistsilk panels, cold extrusion die, cold-cut scissors, circular saw blades, standard tools, measuring tools, etc. Chemical Composition (%): C 1.40~1.60 Si 0.60 Mn 0.60 Cr 11.00~13.00 V 1.10 Mo 0.70~1.20 Co 1.00 P 0.030 S: 0.030 Under the client's requirement.
Performance characteristics: Vacuum deairing with fine steel, it is easy for cutting after quenching , high hardness, good abrasion resistance , dimension stability and minimal distortion. Applications: It is suitable for cutting tools, such as broach, filament hammer and gauge and complex shape of cold mould, plastic mould, precise screw, etc. Chemical Composition (%): C 0.85¡«0.95 Si 0.40 Mn 0.90¡«1.20 S 0.030 P 0.030 Cr 0.50¡«0.80 Ni 0.25 Cu 0.30 W 0.70¡«1.2 Heat Treatment Standard: Quenching, 800 ~ 830 centigrade cold oil. Forging: Oil quenching cold die has crack sensitivity,so it should not be quickly heated,it had better for a preheating in 650-750 centigrade .The temperature of forging is 1130-1150 centigrade, eventually temperature should be more than 800-850 centigrade, steel ingot take upper limit temperature.while blank forging take lower temperature. Delivery condition: Annealing. Under the client's requirement.
Electro galvanized wire BWG20 , wire diameter: 0.93-0.95 mm.
Supplier: Aluminium ( ingots, t bars, sows, rods), copper (cathodes, cakes, billets, ingots, rods), lead (ingots), nickel (cathodes both cut and uncut briquettes, pellets, discs, etc.), tin (ingots, etc.), zinc (ingots both regular size and jumbos), steel billets (all types including crc, hrc, hdgc, plates, sheets), concentrates and ores for above items including bauxite, manganese, clinker and iron ores etc), scraps of above items including hms 1&2 and steel scraps
Buyer: Aluminium ( ingots, t bars, sows, rods), copper (cathodes, cakes, billets, ingots, rods), lead (ingots), nickel (cathodes both cut and uncut briquettes, pellets, discs, etc.), tin (ingots, etc.), zinc (ingots both regular size and jumbos), steel billets (all types including crc, hrc, hdgc, plates, sheets), concentrates and ores for above items including bauxite, manganese, clinker and iron ores etc), scraps of above items including hms 1&2 and steel scraps
We deals in the following products of India, China, Taiwan and Korea Origin:- Cold Rolled Steel (Cold Rolled Steel Strips, Cold Rolled Steel Coils, Cold Rolled Sheets etc.)
We deals in the following products of India, China, Taiwan and Korea Origin:- Cold Rolled Steel (Cold Rolled Steel Strips, Cold Rolled Steel Coils, Cold Rolled Sheets etc)