Vamsikrishna Chemical Industreis

SPECIFICATION +97 +96 +94 +93 +92 +90 (A) +90 (B) +85 +80 +75 +70 +60 % OF AVAILABLE LIME AS CA(OH)2 97 96 94 93 92 91 90 85 80 75 70 60 % OF AVAILABLE LIME AS CA(OH)2 97 96 94 93 92 91 90 85 80 75 70 60 % OF AVAILABLE LIME AS CAO 73.40 72.64 71.13 70.37 69.62 68.86 68.10 64.32 60.54 56.75 52.97 45.40 % ADD INSOLUBLE (MAX.) 0.08 0.1 0.15 0.2 0.5 0.8 1.00 1.3 2.5 3 4 5.7 % IRON ALUMINA IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces IN Traces % MAGNESIA AS MGO 0.04 0.5 0.55 0.6 0.7 0.8 1 1 1.20 1.4 2 2 MESS (BSS) 600 500 450 400 350 300 250 250 200 200 150 150 Packing Laminated PP/HDPE Bag, Jumbo Bags

Specification 700 500 300 250 200 Total CAO 90% 88% 86% 85% 82% %Acid Insoluble (Max.) 0.7 1 1.2 1.25 1.25 R2 O3 In Traces In Traces In Traces In Traces In Traces %Magnesia AS MGO 1.20 1.40 1.45 1.50 1.50 Mesh (Passing) 99% 99% 99% 99% 99% SLAKING TEMPERATURE 600ML WATER 150GM Sample 15 Min 15-20 Min 15-20 Min 20-25 Min 30 Min

Specifications: 1 Calcium Hydroxide Ca(OH)2 90% 2 Calcium Hydroxide Ca(OH)2 90% 3 Calcium Oxide CaO 68% 4 Calcium Carbonate CaCO3 2% 5 Magnesium Oxide MgO 0.4% 6 Acid Insoluble SiO2 0.4% 7 Alumina Al2O3 0.05% 8 Iron Fe2O3 0.05% 9 Chloride Cl Traces 10 Moisture 0.3% 11 Mesh (BSS) 250-300

Specifications : Percent of lime as CaO - >90 Acid Insoluble % - 1.0 (max) Magnesia as MgO % - 1.0 (max.) Metal Oxides as Fe2O3 & Al2O3)% -0.15(max.) L.O.I (Loss on Ignition)% - 3.0 (max.) Reactivity (4N HCl) - 400 ml Brightness % - >80 Sizes % - 0 - 3 mm 0 - 10mm 10 - 50mm

Calcium Oxide (Lime) is made by thermal decomposition of high purity limestone above 900�°C, the process is called calcinations or lime burning. It is also referred to as burnt lime or quick lime. Price: INR 5,000/- to 20,000/-

Hydrated lime