Performance characteristics: wear resistance, corrosion resistance, peeling resistance, low creep, good thermal shock stability, service life is 1.5 times that of ordinary products; Main uses: Mainly used in blast furnaces, hot blast furnaces, carbon roasting furnaces, carbon calciners, coke ovens, steel barrels, casting systems, boilers, cement kilns, glass kilns and various kiln lining and thermal equipment, etc., suitable for metallurgy, machinery, building materials, casting, ceramics, electric power, petroleum, chemical and other industries. Standard size:230*115*65mm First-class high-alumina bricks Al2O3 75% second-class high-alumina bricks Al2O3 60%~75% third-class high-alumina bricks Al2O3 48%~60%
Fire clay & High Alumina bricks are special type of brick which are form of Refractory ceramic material. It is used for inner surface lining of Boiler, furnace, kiln, fireplaces & fireboxes. Quality of Bricks: We offer various quality bricks are IS-6, IS-8, PI - 30% to 90% Alumina offering high temperature resistance of 1100 C to 1700 C. Standard Sizes (inch): 9*4.5*3 / 9*4.5*2.5 / 9*4.5*2 / 9*4.5*1.5 / 9*4.5*1 Side Arch / Side Tapper, End Arch / End Tapper Sizes (inch) 9*4.5*3/2.75 9*4.5*3/2.50 9*4.5*3/2 9*4.5*3/1.5
1. High temperature strength; 2. Resistant to corrosion in various atmospheres; 3. Excellent thermal shock stability; 4. Good thermal insulation; 5. The energy-saving effect is remarkable The operating temperature is below 1350C. Thermal insulation refractories are characterized by high porosity, generally 40%-85%; Low bulk density and low dry 1.5g/cm3: low thermal conductivity, generally less than 1.0W (m.K), it acts as the thermal insulation material of industrial kiln, can reduce the heat dissipation loss of the furnace, save energy, and can reduce the quality of the equipment under heat, the mechanical strength, wear resistance and slag erosion resistance of the thermal insulation refractory material is poor, and it is not suitable for the load-bearing structure of the kiln and direct contact with slag, charge, molten metal and other parts
Product Description: We are a trusted name in manufacturing fire bricks which are a block of ceramic material used in masonry construction. These are sized to be layered with one hand using mortar. Our fire bricks are made from fire clay which is widely used as refractory insulating bricks to maintain insistent temperature. Thee bricks are extensively used in lining furnaces, kilns, fireboxes, and fireplaces.
As per standards. Loose & Pallets
Our company located in yangquan city, shanxi province, china, and yanquan city is one of the Largest refractory material base in china. We are in position to supply various kinds of Refractory bricks, such as high alumina and fireclay bricks, insulating bricks etc With the catalogue as follows: 1. Fireclay brick 2. High alumina brick 3. Insulating brick 4. Unsintered phosphate brick 5. Al-c sliding plate 6. Nozzle 7. Hollowwares 8. Refractory mortar 9. Refractory castables 10.Other refractory material.
For hot blast stoveFor eaf roofFor general use Goods no.Ghha65,Ghha55,Ghha48,Rhs,Rh1,Rh2Al,75Al-1Al-2 Al2o3(%) min655548807565756555 Refractoriness( ) min179017701750185018001790179017901770 Refractriness under load 0.2 mpa( )150014701420155015301520152015001470 Apparent porosity (%) max_191922232322 Ccs (mpa)min4944.139.278.568.658.8544944.1 Shrinkage after reheating 1500x2h (%) max+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4.
High Alumina Bricks for general uses are made from bauxite of super quality, bonding chamotte and additives. It is noted for good erosion resistance high refractorinessthermal shock resistance and accurate dimension. They were widely accepted in various kilns ,thermal equipment of metallurgy, petroleum, chemical industrysuch as high aluminum bricks for blast furnaces steel ladle and electrical furnace and so on .
High alumina bricks
Physical properties Brand SK-32 SK-34 SK-35 SK-36 SK-38 Index Refractoriness íµ 1730 1750 1770 1770 1790 bulk density g/cm3 2.15 2.2 2.3 2.35 2.52 Apparent porosity ¿Q% 24 24 23 23 23 Cold crushing strength ¿RMpa 30 35 40 45 65 Refractoriness under load (0.2MP) íµ 1350 1350 1400 1450 1550 Permanet liner change 1500íµ 2hrs% +0.2to-0.2 +0.2to-0.2 +0.1to-0.4 +0.1to-0.4 +0.1to-0.4 Thermal expansion at 1000 íµ 0.5 0.5 0.5 0.5 0.5 Fe3O4% 1.96 1.93 1.9 1.87 2 Al2O3% ¿R 42 48 55 60 65 SiO2 48-50 46-48 41-44 37-40 27-30
Al2O3: 42-99% refractoriness min 1790 bulk density: 2.1-3.0 apparent porosity: 24-17%
The Al2O3 content is more than 55%, and is calcined from a high-content alumina raw material such as a silicone raw material or a bauxite. High heat resistance and high temperature resistance at 1770 C and above. Has good slag resistance, mainly used in the masonry of steelmaking electric furnace, glass furnace, cement rotary furnace and so on. Characteristics of High Alumina Brick Price: 1.Refractoriness: More refractory than refractory clay bricks and semi-silica bricks, up to 1750-1790C, belonging to high-grade refractory materials. 2. Load softening temperature: Since the high aluminum has a high Al2O3 content, a low impurity content, and a low formation of the molten glass body, the fire-resistant softening temperature is higher than that of the refractory clay brick. However, since the mullite crystal has not yet formed a network structure, the load softening temperature is lower than the load softening temperature of the silica brick. 3. Slag resistance: High Al2O3 has high Al2O3 content, close to neutral refractory material, and can resist the erosion of acid slag and alkali slag. Because it contains SiO2, the resistance to alkali slag is less than acid resistance.
High alumina bricks are commonly utilized in industries such as steelmaking, cement manufacturing, and non-ferrous metallurgy for lining furnaces, kilns, and other high-temperature equipment due to their excellent resistance to thermal shock, abrasion, and chemical corrosion.
High Alumina bricks and Shapes as per custom Requirements
Our high alumina brick is manufactured with selected bauxite chamotte as main material, fired at high temperature by advanced process with strict quality control. High alumina, as the name tells, meaning the content of alumina percentage is higher than 45. And alumina is one of the most chemically stable oxides, it offers excellent hardness, strength and spalling resistance. Our high alumina brick is widely used in industries which need heat insulation, such as the linings of masonry furnaces, hearth and shaft of blast furnaces, ceramic kilns, glass tanks, cement rotary kilns and so on.
High aluminum refractory brick belongs to the silicate aluminum refractory, it is a common refractory produced from refractory clay and high bauxite. The main mineral composition of these kinds of products is aluminum oxide, mullite and corundum, with good physical properties, through chemical analysis and physical experiments, the indexes such as refractoriness and soft charge all reach international and ministerial standards, widely used in blast furnace, hot air stove, thermal storage room, machinery manufacturing, petrochemical and other industries. Introduction of our company Gongyi taurus refractory material factory is a professional refractory materials manufacturers and refractory materials suppliers, mainly supply refractory bricks, unshaped refractories, silicon carbide refractory castable, castable refractory cement, pouring material, castable refractory concrete, silica ramming mass etc. Series of refractory materials products, sincerely welcome everyone to visit.
Refractory Fire Bricks, High Alumina Bricks
High alumina description generally means content of alumina percentage is higher than 45. Alumina is one of the most chemically stable oxides, and it offers excellent hardness, strength and spalling resistance. Alumina refractories are suitable for lining furnace operating up to 1850C. Alumina refractories have the advantages of a high resistance in oxidizing and reducing atmosphere and is extensively used in heat processing industries.
Refractory Brick's Standard size ( 230x115x75 mm ) But we make all sizes of bricks as per Requirement. Alumina ( AlO) - 70 % The weight of bricks is 5.2 KG Bulk density (B.D) - 2.6 Apparent porosity % Max - 22 Ferric ( FeO) % Max - 2.5 Cold Crushing Strength - 500 kg/cm RUL Temperature % MAX - 1480 PLC Temperature % MAX - 1500
Product Introduction: High alumina brick refers to refractory products with Al2O3 content higher than 48%.It is made of bauxite or other raw materials of high alumina content .The refractoriness of high alumina brick can be more than 1770 C . According to the content of Al2O3, high alumina bricks are usually divided into three grades: Grade I Al2O3 content 75%; Grade II Al2O3 content is 60 75%; Grade III Al2O3 content is 48~60%. Application: High alumina bricks are mainly used for lining blast furnaces, hot blast furnace, electric furnace roofs, blast furnaces,reverberatory furnaces, and rotary kilns. Features: 1.Low creep. 2.Good slag resistance. 3.Strong thermal shock stability. 4.Good erosion resistance.