Barytes, China clay, Dolomite, Micro Silica TiO2
Sio2%- 67.7 Al2O3%- 20.9 Fe2O3%- 0.40 Tio2%- 0.45 CaO%- 0.57 MgO%- 0.23 K2O%- 0.08 Na2O%- 0.34 L-90.7 A-0.80 B-7.01 Whiteness- 74.5 Shrinkage- 3.42 Plasticity- 28.6 Tempreature C- 1213/1214 Cycle min.-60 Dry MOR- 14.6 Kg/Cm2 Fired MOR- 102.6 Kg/Cm2
SiO2%- 56.19 Al2O3%- 36.98 Fe2O3%- 0.19 TiO2%- 0.58 CaO%- 0.28 MgO%- 0.42 K2O%- 0.08 Na2O%- 0.21 L- 97.12 A- 0.21 B- 2.92 Whiteness- 91.1 Shrinkage - 4.72 Plasticity- 33.9 Tempreature C - 1206/1218 Cycle Min - 60min
Sio2%- 48.10 Al2O3%- 36.11 Fe2O3%- 0.45 Tio2%- 0.99 CaO%-0.24 MgO%- 0.32 K2O%- 0.10 Na2O%- 0.19 L-94.20 A-1.21 B-3.32 Whiteness- 88.5 Shrinkage- 4.73 Plasticity- 34.5 Tempreature C - 1209/1220 Cycle min.- 60
Kaolin mines in Malaysia looking for miner/investor for tae over or JV. Small manageable acreages. We assist procurement, set up and export.
Ceramic Grade Paint Hydrus kaolin crude kaolin Levigated kaolin
HIGH QUALITY DRY KAOLIN NOODLE, We have dry kaolin Moisture Max 30% and with a concentration of aluminum oxide up to 36%. Fire Brightess up to 84% Origin: Belitung Island, INDONESIA.
HIGH QUALITY DRY KAOLIN POWDER, We have dry kaolin Moisture Max 3% and with a concentration of aluminum oxide up to 36%. Fire Brightess up to 84 Origin: Belitung Island, INDONESIA. Size: Powder "325 Mesh".
We PT.CHORI are authorized distributor of below supplier. Product Name : Kaolin (Cas No. 1332-58-7) Aluminum silicate hydroxide, Bolus, Hydrated aluminum silicate Manufacturer : In Indonesia Characteristic : 1. Biggest Supplier in Indonesia 2. widely used in the world. Application for : Paper, Refractory, Cement, Pesticide, Rubber filler, Paint Please feel free to inquiry to us so that we could send more detail spec, production capacity and price. When you send inquiry to us, we will send company profile and product documents, we hope to have intimate relationship.
Good day! Our company produces the high quality 3 sorts of kaolin please see attached files, where you can read more about our company. AKT - 10 - it can be used as a filler for rubber products,cables and plastic. AKF - 78 - this product is used in the paper industry and manufacture of ceramics and glazes AKC - 30 - used in production of porcelain and ceramic goods, as well as sanitary ceramics.
Elemental Oxide Chemistry IGM Kaolin ----------------------------------------------------------------------------- Silica SiO2 46.2% Alumina Al2O3 37.8% Magnesia MgO 0.1% Potash K2O 0.67% Soda Na2O
Kaolin and Silica mixed material Particle Size (typical) : < 0.6mm Unfired Brightness : 83 Composition (typical) LOI (1,000o C) : 8% SiO2 : 54% Al2O3 : 33% Fe2O3 : 1.5% K20 : 2.4% MgO : 0.5% TiO2 : 0.3% CaO : 0.01% Theoretical Mica/ Illite : 20%
Elemental Oxide Chemistry IGM Kaolin ----------------------------------------------------------------------------- Silica SiO2 46.2% Alumina Al2O3 37.8% Magnesia MgO 0.1% Potash K2O 0.67% Soda Na2O
Product: GB-CK90 Package: 25kg plastic woven bag without pallets Quantity: 20FT(20MT) Condiiton: FOB XINGANG Typical Physical Properties: Brightness(T457): 93.5%min Particle Size (0-2micron)%: 80+/-2 Particle Size (0-10micron)%: 100% Refractivity: 1.62 Screen residue (325 mesh %): 0.005max Oil Absorbency (g/100g): 60+/-5 Dispersion (micron): 50max pH: 5.5-7.0 Bulk Density (kg/m3): 330 Specific Gravity (kg/m3): 2600 Moisture (%): 0.5max The GB-CK series of Kaolin based pigments are produced through delamination,calcination and classification. The well-controlled processes ensure the GB series have no coarse particles and maintains an absolute minimum of 325 mesh residue, so the end user can achieve a high Hegman grind. The GB series pigments also have high brightness, strong hiding powder and superior dispersibility, and it is widely applied in latex paint, powder coating and electrophoresis coating. Its main benefits are: It is the best extender of titanium dioxide with excellent opacity that can improve efficiency and cut costs by partly replacing titanium dioxide; It can easily disperse in water based systems; It offers superfine particle and with excellent anti-settling property; It is inert to most acids and alkaline at ambient temperature and offers good anticorrosive capabilities.
Product: GB-CK95 Package : 25kg plastic woven bag without pallets Quantity: 20FT(16MT), 40FT(27.5MT) Condiiton: FOB XINGANG Typical Physical Properties: Brightness(T457): 93.5%min Particle Size (0-2micron)%: 80+/-2 Particle Size (0-10micron)%: 100% Refractivity: 1.62 Screen residue (325 mesh %): 0.005max Oil Absorbency (g/100g): 60+/-5 Dispersion (micron): 50max pH: 5.5-7.0 Bulk Density (kg/m3): 330 Specific Gravity (kg/m3): 2600 Moisture (%): 0.5max The GB-CK series of Kaolin based pigments are produced through delamination,calcination and classification. The well-controlled processes ensure the GB series have no coarse particles and maintains an absolute minimum of 325 mesh residue, so the end user can achieve a high Hegman grind. The GB series pigments also have high brightness, strong hiding powder and superior dispersibility, and it is widely applied in latex paint, powder coating and electrophoresis coating. Its main benefits are: It is the best extender of titanium dioxide with excellent opacity that can improve efficiency and cut costs by partly replacing titanium dioxide; It can easily disperse in water based systems; It offers superfine particle and with excellent anti-settling property; It is inert to most acids and alkaline at ambient temperature and offers good anticorrosive capabilities.
Kaolin (kaolin) is a non-metallic minerals formed by weathering bedrock containing agar. Kaolin is important minerals and is used in many different areas such as: Manufacture of ceramics, refractory, aluminum production, paint fillers, rubber, paper, white cement, ...
U.S. Mine Corporation's Ione Airfloated Kaolin Clay is a western U.S based deposit (California) suitable for calcining as a metakaolin and used in high-strength cements. It is available in 50 lb bags, Supersacks, and bulk. SiO2 47.0% Al203 36.31% Fe203 0.55% Ti02 2.4% Ca0 0.05% Mg0 0.03% Alkalies (Na20, K20) 70 Moisture Content (dry) %
Ione Industrial kaolin Clay is a high purity kaolin clay, which is low in iron and alkali content, a run-of-mine kaolin that is sold out of stockpiles. The low iron, low alkali and high aluminum content makes this an ideal kaolin for cement production, and for application in the rubber, fiberglass and agriculture industries. Si02 47.0% Al203 36.31% Fe203 0.55% Ti02 2.4% Ca0 0.05% Na20, K20 70 +325 mesh 5-15% pH (40% solids) 4.0 Moisture Dry 12-16% Raw clay color - white High purity kaolin clay sold in bulk/supersack.
The Limited liability company Resource-S can supply secondary kaolin (kaolinite) production of Ukraine, grades KÐ?-0, KÐ?-1, KÐ?-2, KÐ?-3, in the amount of 200-250 thousand tons within 2019. The volume of kaoline deposits in case of the reservoir management is within 8-12 mln. tons. If you are interested, we are ready to provide you with the results of tests of secondary kaolin, and we can also provide you with samples of kaolin to analyze its chemical composition.
Available Mesh Size: 200/300/325 Packing: 25/40/50 Kg Bags And Jumbo Bags.