Latex reclaim rubber is made from gloves and condom waste. It's best replacement for natural rubber. It reduce your cost with keeping same quality.
Performance Specification of Reclaim Rubber Sheet: water content : 120 %, ash : 15.0% acetone extract : 20.0% tensile strenght : 8 Mpa elogation : 300 density : 1.20 mooney MI : 40-70 (mooney viscocity could be adjust to customer requirements) we are a trading company based in singapore, we book order based on customer requirments. all reclaim rubber sheet are pre-order only, full pre-payment by TT for all pre-order quantity, delivery within 30 days after receipt of TT pre-payment. thanks
Let us introduce ourselves, we are Mehra Polymers, manufacturers of latex based reclaimed rubber with RHC(Rubber Hydro Content) varying from 50% to 75%. Currently we are manufacturing White, Blue & Grey coloured reclaimed rubber in three different grades (SF-Super Fine, SP-Semi Pure & HR-Highly Refined). 25 & 50 Kg per bag
Would be provided by email Global(at)hightechreclaim(dot)com 25 kg woven laminated bales loosely stuffed or ldb.
Reclaimed rubber sheet from devulcanize waste tyre. Having a high tensile strength and elongation. 10kg or 20kg per sheet
Butyl rubber has several features like good gas tightness, ozone resistance, aging resistance, good thermo stability, inorganic acid resistance and common solvent proof. Also... Short and fast mixing power Reduce power consumption Low heat buildup in processing Low thermo plasticity High rate of curing Cost reduction Long shelf life. 25kg/pc, naked with calcium powder, packaged with white/black plastic film, woven bag, packaged by pallet.
Commodity Name: Tyre reclaimed rubber Tensile strength : 16Mpa Elongation: 460 (%) Mooney Viscosity: (as request) Moisture content :max1.0 (%) Capacity: 20000MT/year Lead time: 7 days Deliver Port: LianYunGang, China. 20kg /piece, packing:plastic film.
Commodity Name: Tyre reclaimed rubber Tensile strength :12Mpa Elongation : min 440 (%) Mooney Viscosity:60 (as request) Moisture content :max1.0 (%) Capacity: 20000MT/year Lead time: 7 days Deliver Port: LianYunGang, China. 20kg/piece , packing: plastic film.
Item\IndexSpecies,Grade Water content Ash content Extraction of acetone Density Stretch strength Elongation rate Menni viscosity % % % g/cm3 MPa % ML(100C,1+4) Inner Tire Excellent 0.5 6 10 1.2 11 . 0 490 40 ~ 50 First Grade 0.5 8 15 1.2 8.0 480 50 ~6 0 Capsule Excellent 0.8 8 15 1.2 10. 0 480 50 ~6 0 First Grade 0.8 10 18 1.2 7.0 460 60 ~7 0 Nude packing, black or white plastic film, pallets.
A method from waste tire makes reclaimed rubber, though tire cutting equipments decompose and break the tire into small blocks, then smashed by crushing mill into granular, and filtered by the screener, with the help of the difference of air and wind of the separator, separates the fine fiber and rubber then get semi-finished products, then make the semi-finished reclaimed rubber though contaminated, desulfurization, cleaning and refining, we can get high purity reclaimed rubber. This method is not polluting the environment, promotes recycling, reduces human laboratory. Wooden case.
Technical specifications Physical appearance Black slab Chemical properties Acetone extract (%) 14 ¦ 3 Ash (%) 7 ¦ 2 Carbon black (%) 27 ¦ 2 Rhc (%) Min 47 Volatile matter (%)
Rubber content : 70 % Ash : 20 % Acetone extract: 4 % Mooney viscosity : 54 Specific gravity : 1.118 25 kg / bale 20 m.Tone / 20ft containre ( loose loading ).
Rubber content : 65 % ( +/- 5 % ) Ash : 20 % ( +/- 5 % ) Acetone extract: 7 % ( +/- 3 % ) Mooney viscosity : 26.5 Specific gravity : 1.122 25 kg / bale 22 m.Tone / 20ft container ( loose loading ).
Physical appearance black slab Acetone - extract % 10 ¦ 3 Ash % 4 ¦ 2 Carbon black % 30 ¦ 2 Rhc % 50 ¦ 4 Specific gravity 1.10 ¦ 0.05 Volatile matter % < 1 Mooney viscosity ml (1+4) 100o c 30 - 50 Tensile strength kg/cm2 80 Elongation > 450
1'with ce and iso9001-2000 certificates 2'finest workmanship, high quality at reasonable price 3'good reputation widely Main uses: This rubber cutting machine is mainly used to cut the natural rubber, synthetic rubber, and other plastic materials, especially it is suitable to be installed near the rubber mixer to cut small piece of rubber.