Two component Epoxy based anti corrosive primer containing zinc phosphate as corrosion inhibiting pigments
Recommended Use :-
It is recommended as primer on M.S surface for OEM's as well as for process industries like fertilizers, refineries, chemicals and other plants. It can also be applied in diverse areas of tank exteriors, equipments, pipelines, structural steel, etc. Not to be used for immersion application.
Physical Data :-
COLOUR :- Yellow
FINISH :- Matt
SOLIDS BY VOLUME :- 40 �± 3%
THEORETICAL SPREADING RATE :- 13.33 sq.mt. / ltr. at recommended DFT of 30 �µ
FLASH POINT :- Base : 23�°C Hardener : 23�°C
DRYING CHARACTERISTICS :- SURFACE DRY : 60 to 90 minutes
(At 30�°C & 65% Relative Humidity) :- HARD DRY : Overnight. FULL CURE : 7 Days
SHELF LIFE :- BASE : 6 months HARDENER : 6 months
SURFACE PREPARATION
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application
Application Data
MIXING RATIO :- Base : Hardener (As per our recommendation)
APPLICATION :- By Brush / By Conventional Spray / By Airless Spray
THINNER :- Epoxy Thinner 190
POT LIFE :- 4 hours min at 30�°C
RECOMMENDED DFT :- 30 - 40 �µ.
OVERCOATING INTERVAL :- MIN : 8 Hours MAX : 24 Hours
COMPATIBILITY :- Can be over coated with Epoxy, PU, Chlorinated rubber and Oleo-resinous topcoats.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Add Epoxy Thinner into the mix, if required, depending on application method, and stir gently for few minutes. Strain the paint through Nylon filter cloth and apply uniformly over the surface. All equipments used for above should be properly cleaned. Application : By Brush / By Conventional Spray / By Airless Spray Generally no thinner is required for Brush application; however under adverse environmental conditions about 5% of thinner, by volume, can be added. . Apply evenly in crossed manner, ensuring the uniform application. Use quality brushes for paint application.
Two component Epoxy based anti corrosive primer containing red oxide and zinc chromate as corrosion inhibiting pigments
Recommended Use :-
Recommended as a primer on suitably cleaned mild steel surface in various fertilizer units, refineries, chemical and other plants, transportation industries, steel plants, cement plants, power plants, pulp and paper industries, pharmaceutical industries, etc. for application on tank exteriors, structural steel, pipelines, machineries, vessels, etc. The product is recommended as a primer for mild to moderate service conditions. Not to be recommended for immersed water condition
Physical Data
COLOUR : Red
FINISH : Matt
SOLIDS BY VOLUME : 40 + 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt / lt at recommended DFT of 30 FLASH POINT : Base : Above 23C Hardener : Above 23C
DRYING CHARACTERISTICS (At 65% Relative Humidity & at 30C) : SURFACE DRY : 60 - 90 minutes HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Epoxy Thinner 190
POT LIFE at 30�°C : 4 hours min at 30�°C
RECOMMENDED DFT : 30 40 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated Rubber and Synthetic Enamel finish paints.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Add Epoxy Thinner into the mix, if required, depending on application method, and stir gently for few minutes. Strain the Application : By Brush / By Conventional Spray / By Airless Spray Generally no thinner is required for Brush application; however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in crossed manner, ensuring the uniform application. Use quality brushes for paint application.
For Conventional Spray application :-
Thinner : Epoxy Thinner 190
Addition : 10-15%
Nozzle Orifice : 1.2 -1.4 mm
Nozzle Pressure : 40-70 p.s.i.
For Airless Spray application :-
Thinner : Epoxy Thinner 190
Addition : Max 5% if required
Nozzle Orifice: 0.37- 0.42mm
Nozzle Pressure : 1400-1800 p.s.i.
Two component metallic zinc rich epoxy high performance primer.
Recommended Use :-
The zinc pigment in dry film renders excellent protection to steel structure, tanks, bullets, dam gates, pipelines, plant equipments, jetty, etc. in both interior and exterior exposed conditions of fertilizer units, chemical plants, steel plants, cement plants, pulp and paper industries, ports, power plants, petrochemical and pharmaceutical industry, transformer, machines & other heavy duty OEMs. It also provides cathodic protection to steel and gives good resistance to corrosion at local damaged areas. It is useful in heavy-duty protective paint systems. It is recommended not to expose the primed coat alone to chemical and saline atmosphere for a long time.
Physical Data
COLOUR : Grey
FINISH : Matt
SOLIDS BY VOLUME : 50 �± 3%
THEORETICAL SPREADING RATE : 10 sq.mt / ltr at DFT of 50 �µ
FLASH POINT : Base : Above 23�°C Hardener : Above 23�°C
DRYING CHARACTERISTICS (at 30�°C & at 65% Relative Humidity) : HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to minimum Sa 2 1/2 Standards is recommended with a profile of 35 - 75 microns. The surface should be absolutely dry and salt free before application. The primer should be applied preferably immediately or within 4 hours of blasting.
Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Epoxy Thinner 190
POT LIFE : 4 hours min at 30�°C
RECOMMENDED DFT : 30 50 µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : Infinite
COMPATIBILITY : Compatible with Epoxy, PU, Chlorinated Rubber intermediate/finish coat.
Two component Epoxy based anti corrosive primer pigmented with Zinc Chromate as corrosion inhibiting pigments.
Recommended Use :-
It is recommended as primer on M.S surface for original equipment manufacturing as well as for process industry as in various fertilizer, refineries, petrochemical, chemical and other plants, applied in diverse areas of tank exteriors, equipments, pipelines, structural steel, etc. Not to be used for immersion application.
Physical Data
COLOUR : Assorted
FINISH : Matt
SOLIDS BY VOLUME : 40 ± 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt. / ltr. at recommended DFT of 30 �µ
FLASH POINT : Base : Above 23�°C Hardener : Above 23�°C
DRYING CHARACTERISTICS : SURFACE DRY : 60 90 minutes
(At 65% Relative Humidity & at 30�°C) : HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application.
Application Data
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray
THINNER : Epoxy thinner 190
POT LIFE : 4 hours min at 30 C
RECOMMENDED DFT : 30 - 40 au.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated rubber and Oleo-resinous topcoats.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Add Epoxy Thinner into the mix, if required, depending on application method, and stir gently for few minutes. Strain the paint through Nylon filter cloth of 100 mesh size and apply uniformly over the surface. All equipments used for above should be properly cleaned.
Application :- By Brush / By Conventional Spray / By Airless Spray
Generally no thinner is required for Brush application, however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in criss-cross manner and ensure the uniform application. Use quality brushes for paint application
it is mainly used for color cement, color cement floor tiles, color cement tiles, imitation glazed tiles, concrete floor tiles, color mortar, color asphalt, terrazzo, mosaic tiles, artificial marble and wall painting.
2. It can be used for colouring and protecting substances of various coatings, including water-borne interior and exterior wall coatings, powder coatings, etc. It can also be used for various primers and topcoats such as epoxy, alkyd, amino, etc. in oily paints, as well as for toy paints, decorative paints, furniture paints, electrophoretic paints and enamels. Iron red primer has anti-rust function, can replace high-priced red red paint, save non-ferrous metals.
The manufacturer supplies iron oxide red, iron oxide green, iron oxide blue, iron oxide yellow, iron oxide violet, iron oxide brown, iron oxide black and so on. The color is complete, the quantity is large and the discount is favorable. Support mixed batches. Welcome to call for consultation.
Neo has extensive range of primers based on Epoxy / PU / Synthetic Resins. NEO PRIME GUARD grades are quality Epoxy based primers while NEO SHIELD PRIME grades are PU primers. These are used as a primer. They exhibit excellent adhesion properties and will stick to bare metal, Paints, primers, and fillers. They are used as a anti corrosive / protective primers. Neo offers multiple grades loaded with special additives, pigments for meeting specific requirements.
Two-component,water-based epoxy primer, high surface hardness, high moisture,water and chemical resistance, high mechanical resistance. It is excellent for bridging the water-based topcoat applications. There are no harmful chemicals in its composition.
940 102 Epoxy Zinc Chromate Primer Suppliers
Short on time? Let 102 Epoxy Zinc Chromate Primer sellers contact you.