White Marble Blocks directly from our Quarry. Possible to cut into Slabs/Tiles upon request.
Dear Sir. We can offer portland Cemment 42.5N/R ASTM C150/ EN 197-2000 from Vietnam Min. 20.000 ton FOB $52/ MT FOB Campha Port Vietnam Packing in Jambo bag Waiting for reply soon
Dear Sir. We can offer portland Clinker High Quality Ground Granulated Blast Furnace Slag from vietnam, FOB $40/ MT Packing in Bulk Waiting for reply soon
Cement Clinker C-150 Type 1 ASTM â?? CPC50 TCVN; tyle II Origin: Vietnam Capacity factory: 200.000MT/ month MOQ: 20,000 MT in bulk Payment term: T/T or L/C Port Loading: Hon Net port, Cam Pha Capacity loading at port: 7500 MT/ days
We are very confident to be a reputable company in Vietnam, supplier of Limestone for Cement and Steel at high quality and best price. We supply 2 kinds of limestone: Limestone for Cement Industries and Limestone for Steel. Packing detail: 1. Packing:Â Bulk Vessel 2. Quantity: 200,000Mt per month Delivery detail: 1. Delivery time: 20 days after the order confirmed 2. Port loading: Cam Pha, Quang Ninh, Vietnam.
Acacia Hardwood Decktile with/without plastic size: 24 x 300 x 300 / 600
We have high quality limestone, boulders, stone, aggregate that suits for sea backfilling, concrete, and other constructions. Hardness: >9 CaO > 53% Silic > 0.82% Magnesia > 1% Size: 60-80cm 20-30cm 10-20cm 5-8cm 2-5cm 1-2cm Others: Based on your requirements. Note: The given FOB price is without VAT.
PVC/ ABS plastic sheet Surface treatment Embossing and printing Printable wood grain and any pattern can be produced according to demand for any kind make door or Building materials
PVC/ABS Composite material Door all water proof Mothproof Customizable
Polyester RAL7035 Powder Coatings with Smooth Glossy or Wrinkle are available
Portland Cement Type CEM II 42.5R Specifications: SO3: 2.20 % Chloride: 0.003 % Finess test: 3578 cm2/g Setting time: - Initial set: 125 minutes Soundness (LeChatelier): 0.5 Mm Compressive strength: - 2 days: 27.5 Mpa - 28 days: 54.6 Mpa
Portland Cement Type CEM I 52.5N SO3: 2.2 % SiO2: 21.33 % Fe2O3: 2.92 % Al2O3: 6.03 % CaO: 61.65 % Chloride: 0.005 % MgO: 1.78 % LOI: 2.75 % Insoluble residue: 0.37 % Total alkali: 0.56 % Finess test: 3614 cm2/g Setting time: - Initial set: 145 minutes - Final set: 205 minutes Soundness (LeChatelier): 1.0 Mm Compressive strength: - 2 days: 23.1 Mpa - 28 days: 54.2 Mpa
Portland Cement ASTM C150 Type I Specifications: SO3: 2.2 % MgO: 1.77 % LOI: 2.88 % Insoluble residue: 0.39 % Total alkali: 0.56 % Finess test: 0.56 cm2/g Setting time: - Initial set: 109 minutes - Final set: 191 minutes Autoclave expansion: 0.07 % Air content of mortar: 7.96 % False set, final penetration: 89.5 % Compressive strength: - 3 days: 21.41 Mpa - 7 days: 32.00 Mpa - 28 days: 44.28 Mpa
Warranty: Lifetime After-sale Service: Other Style: Japan Style Occasion: Outdoor Project Solution Capability: Others Application: Apartment Design Style: Modern Place of Origin: Vietnam Brand Name: VIETGO Model Number: VGRT456 Surface Treatment: Full Body Tiles Product Name: Roof tile 3D nano silicon paint Type: 3D nano silicon paint Feature: Water, UV, Dirt Resistance Advantages: Self-cleaning, Scratch & Moss Resistance Water permeability (%): < 9.5 Size after roofing: 363mmx303mm Quantity per m2: 9 pieces/m2 Weight per piece: 3.3 (+/-2) kg/pc (>1400) Durability: Colour up to 20 years Payment Term: LC / TT Delivery Time: 10 - 15 days
The QUICKLIME is produced from limestone containing over 95% calcium carbonate. They produce by heating raw limestone deposits in a kiln up to temperatures of 900 degrees. This process is referred to as calcination process. Quick Lime Powder is much used in Sugar Refinery, Steelmaking, FGT, Construction, Masonry & Mortars, Water Treatment, Chemical Processes, Mining Industryapplications, ... SIZE 150MESH, COLOR MILKLY WHITE CaO > 90%, S < 0.08%, MgO < 2.0%, Fe2O3 < 0.05%, Al2O3 < 0.5%, SiO2
The QUICK LIME is produced from limestone containing over 95% calcium carbonate. They produce by heating raw limestone deposits in a kiln up to temperatures of 900 degrees. This process is referred to as calcination process. CaO > 90%, S < 0.08%, MgO < 2.0%, SiO2 < 0.68%, L.O.I < 4.0%, Fe2O3 < 0.05%, SLAKING TIME: 2-5MINUTES, Al2O3 < 0.5%. SIZE: 0-10mm, COLOR: MILKLY WHITE. Packing by 25kg, 50kg, 1.000kg, 1.200kg Bag Loading by container 20feet with pallet or without pallet (Optional). Quick Lime Granular is much used in Sugar Refinery, Steelmaking, FGT, Construction, Masonry & Mortars, Water Treatment, Chemical Processes, Mining Industryapplications,... The capacity per month is 3,000 metric tons and it is exported to mainly Asian countries.
GENERAL INFORMATION Quicklime or Calcium Oxide (CaO) is produced by heating Calcium Carbonate (e.g., limestone) in a special limekiln to about 1050�°C, decomposing it into Calcium Oxide and Carbon Dioxide. Our Quicklime product is sold in several sizes TYPICAL CHEMICAL PROPERTIES Calcium Oxide (CaO) : > 90.0 % Residue Calcium Carbonate (CaCO3): < 5.00 % Iron Oxide (Fe2O3): < 0.10 % Aluminum Oxide (Al2O3): < 0.50 % Magnesium (MgO):< 1.50 % Silicon Oxide (SiO2): < 0.80 % Sulfur (S):< 0.50 % Sodium Oxide (Na2O):< 0.01 % Potassium Oxide (K2O): < 0.05 % Strontium Oxide (SrO) : < 0.02 % TYPICAL PHYSICAL PROPERTIES pH 12.4 Lumps Size 10 â?? 60 mm Moisture Content 0.3 % Max PACKING 1-1.25MT Jumbo Bag LOADING 20-25MT/20 DC FCL APPLICATION Metallurgy Paper Sugar Industries