Origin: China Steel grade: D2/ 1.2379/ SKD11 Brand name: Fangyuan Special Certificate: ISO9001:2000 Delivery condition : HB180-225 Size(mm) 50-300 rounds, 20-250 (flats/thickness) Property & Application: Recognized for its high resistance against wear, high compression stregth and fine robustness .the spheroical annealed process make it easy process by shearing and cutting with no worry about crack during process. Applied in thickness no less than 2mm punch mould , all kind of small mould for shearing and cutter together with screw-rolled or slappered mould as well as some other forming mould like rulers .
Origin: China Steel grade: D3/ 1.2080/ Cr12 Brand name: Fangyuan Special Certificate: ISO9001:2000 Delivery condition : HB190-235 Size(mm): 50-300 (rounds) 20-250 (flats/thickness) Property & Application: with good wear-resisting and high hardening to prevent from deforming , can be used to make non punch tough tools, measurements like reamers, car cutter, plastic crush blade,Guage knife, also used in such precise moulds as gaskets, silicon glue mould, keyboard mould ,cold dies,punch head , samples, cold punch, drill set,silk-drawing mouls, stainless steel thin plate punch moulds, cold pressing mould etcs.
Origin: China Steel grade: D6/ 1.2436/ Cr12W Brand name: Fangyuan Special Certificate: ISO9001:2000 Delivery condition : HB190-235 Size(mm) 50-360, rounds, 20-250 (flats/thickness) Property & Application: it has super wear-resisitance, anti-pression and super lower hardenability as well as its strong and high ability on bearing tempering. Based on its property, it is widely applied in such molds as punch, pression dies and sips as well as in hard sheets, ceramics, tiles, abrasive materials, plastics and silicon steel sheets etc.
Standards: ASTM,GB,EN,JIN Diameter: 4.8mm-12.7mm Uses: inlet and exhaust valves of cars , light trucks, mini trucks, motorcycles, heavy trucks, tractors, diesel locomotives, generators , ships, etc. Quotation need data: material+diameter+packing weight. Standard export packing---water proof material wrapped and wooden crate will be used.
Alloy steel: Special stainless steel.Monel alloy series, GH series of high-temperature alloys, NS series of corrosion resistance alloys, precision alloy, inconel alloy series, as a result of alloys keluo YI series, harrington series alloys We can offer the sheets, tubes and bars used the material above. As per the clients' requirement.
1. Bars:12-400mm 2. Flats:20-250*60-750mm 3. Length:1500-6000mm 4. EAF/ESR+Forged +Annealed+Grinded/Machined 5. 100% UT acco to En1921Dd 6. Delivery time:35-40days. 7. Payment item:L/C,T/T 8. Delivery status:black/grinded/machined 9. Packing:standard export sea-worthy packing 10. With high quality and competitive price 11. With 10years professional experience 12. Exported many countries directly 13. Productivity:1000 tons per month. According to customers' requerement.
1. Standard: BS4449 Gr. 460B, ASTM A615 Gr. 40/60, ASTM A706, HRB 335/400/500 etc. 2. Diameter: 8~50mm 3. Length: (1) 8mm and 10mm: in coil If you want diameter 8mm and 10mm to be in straight bar, our factory could produce as you requested. (2) 12~50mm: 6~12m. In bundles.
Carbon steel products,
Product Name: 4Cr3Mo3SiV/ H10/1.2365/round bar/flat bar/hot work tool steel/die steel/mould steel Chemical Composition: Standard Steel Grade C Si Mn P S Cr Mo V W DIN 1.2365 0.28-0.35 0.10-0.40 0.15-0.45 0.030 0.030 2.70-3.20 2.60-3.00 0.40-0.70 - ASTM H10 0.35-0.45 0.80-1.20 0.25-0.70 0.030 0.030 3.00-3.75 2.00-3.00 0.25-0.75 - GB 32CrMoV12-28 0.28-0.35 0.10-0.40 0.15-0.45 0.030 0.030 2.70-3.20 2.50-3.00 0.40-0.70 - Specification: Round bar Diameter Length Forged round bar 50~450 2000~6000 Rolled round bar 10~80 2000~6000 Flat bar Thickness(mm) Width(mm) Length(mm) Forged plate 20~300 50~710 2000~6000 Rolled plate 10~65 155~610 2000~6000 DIN AISI JIS GB 1.2365 H10 - 4Cr3Mo3SiV Steel Properties: Excellent wear resistance and toughness at high temperatures. Good machinability in annealed condition. Good polishability. Good hardenability. Very good dimensional stability. Excellent tempering resistance. Applications: Dies, tools for the production of screws and forging machines, highly stressed extruding tools for light metal processing-mandrels, pressing die cast moulds.
1. High speed steelM2 2. Forged or hot rolled 3. Fast cutting steel with high resistance 4. High hardness 5. EAF+LF+VD+ESR Technogoly:EAF+LF+VD+ESR Trade patterns:CIF and FOB Shape:round bars and flat bars 1. M2 is a general purpose high speed steel. M2 high speed steel offers good wear resistance with excellent toughness and cutting power. 2. Chemical composition :(%) C:0.80~0.90; Si: 0.40; Mn: 0.40; W: 5.50~6.75; Mo:4.50~5.50; Cr:3.80~4.40; V:1.75~2.20, S:0.030 P:0.030 3.Forging: The forging temperature for high speed steels is 1050¡ã/1150¡ãC. Do not charge direct into the high temperature part of the furnace, but pre-heat slowly to 850¡ã/900. During the forging, the temperature of the material drops below 880/900¡ãC, reheating will be necessary. Cool very slowly after forging. 4.Features : 1) excellent ductility and abrasion resistance 2) well distribution of carbide and thermal plasticity 3) high hardness and high temperature hardness 5.Applications : For making all sorts of general tools, forming tool, and also some components, such as cold extruding dies, etc. 6.Steel Grade: GB:W6Mo5Cr4V2 AISI:M2 DIN:1.3343 JIS:SKH9 7.Mechanical Property Annealed Hardness: HB255 Quenching Hardness: HRC¡Ý63 8.Delivery Condition Forged + Annealed + Machining (Peeled/Turned) Our main products: Plastic mould steel: 1.2311, 1.2738, P21, 1.2316, 1.2083 etc. Hot work tool steel: H11, H13 etc. Cold word tool steel: O1, D2, D3, D6 etc High speed steel: M2, M35, M42 etc. Carbon steel: AISI1045, AISE1050, Q235, SS400 etc. As per standard exporting.
Plastic mould steel AISI P20 1, Chemical composition(% for reference only): C: 0.36~0.42, Si:0.3~0.4, Mn:1.0~1.2, Cr:1.7~2.0, P
1) Delivery condition: EAF&ESR, Hot rolled&forging, black surface, machined/milled surface, annealing Hardness: HBS=217~269 2) Chemical composition (% for reference only): C Si Mn P S Cr 2.0~2.3
Steel H13 flat bar, 1) Grade:H13 SKD-61, DIN1.2344 2) EAF+LF+ESR+FORGEN+ANNEAL+UT+PEELING/TURNNING/MILLING 3) Size: flat sheet: thickness 30-300MM, width:100-600MM Length: 1.5-3.5m 4) Annealed Hardness: HBS
1, Steel feature: Cold-work steel DIN1.2510, O1,SKS3, 9CrWMn has good cutting edge maintenance ability and treatment distorts slightly. 2. Steel grade:DIN1.2510, O1,SKS3, 9CrWMn 3, Application: this kind of steel can be used for resistant punching pins and dies, shear blades and thread rolling dies. 4, Chemical composition (% for reference only): C Si Mn Cr V Others 0.9 0.3 1.2 0.5 0.2 W0.6 5, Material Character: Have quenching appear nature and wearable, mini quencher and distortion, distributing equal carbide and small granule. Our main products: Plastic mould steel: 1.2311, 1.2738, P21, 1.2316, 1.2083 etc. Hot work tool steel: H11, H13 etc. Cold word tool steel: O1, D2, D3, D6 etc High speed steel: M2, M35, M42 etc. Carbon steel: AISI1045, AISE1050, Q235, SS400 etc. As per standarded exporting.
TMT. As required or preffered by customer.
Size: Round: 8-300 mm Flate: 12-90*205-305 mm Chemical composition%(for reference): C Si Mn Cr 2.00-2.30 0.40 0.40 11.50-13.00 Delivery condition: Soften annealed:255HB Application: Cr12 steel has excellent wear-resisting performance. It is mainly used for long-life punching die, blanking die, drawing die, press rolling die, edge rolling die that are designed for processing the sheet metal with thickness not greater than 2 mm, and is also widely used for ceramic dies. It is also used for making various scissors, crushing cutters for waste plastics, etc. Features: Cr12 steel is a high-carbon and high-chromium alloy tool steel. It features good size stability after heat treatment, strong hardenability, high quenching hardness and high compressive strength. It is suitable for making the high-precision and long-life cold work dies.
Cold drawn & polished. Cold drawn, centerless ground & polished peeled, centerless ground & polished peeled (rough turned) buffed (mirror finish) HDPE Wrapping
Detailed Product Description: Cold work tool steel D2/DIN1.2379 Soft annealing to HB230 Used for variou high precision,long lifetime cold work mould like punch mould 1.2379 Tool steel SKD11 Grade:D2/1.2379/SKD-11 Flate size:20-200*200-600mm Lenth:1-4m Round size:Dia20-300mm Length:1-6m Factory state:soft annealing to HB230 Application: Used for variou high precision,long lifetime cold work mould like punch mould,cold squeezing mould Other cold work tool steel are supplied, like AISI D3, AISI D6, AISI O1 etc. steel round bars, flat bars, plates, and block.
Detailed Product Description: High speed tool steel M2/1.3343 High speed cutting steels, Execution anneal HB to 260 Surface Hardness in HRC:61-66 High speed cutting steels, execution anneal HB to 260, surface Hardness HRC after Tempering 61-66 Application: They can be used high speed cutting cutter, precision cold punch mold, roller, pinmold and so on. Molds: Flat bars and round bars Dia:12-200mm Width:60-600mm Thickness:20-300mm We also supply other high speed steel, like M2, M42, M35 and so on Large stock, good quality and competitive price.
42CrMo4 / 1.7225 / 4140 Alloy steel description: Available sizes: Round: Dia. 20 ¨C 1200mm Flat: Thickness 20 ¨C 120mm, width 305 ¨C 660mm Delivery condition: Hot rolled or forged, Peeled or black surface, annealed or QT. Properties: One of the chromium, molybdenum, manganese low alloy steels noted for toughness, good torsional strength and good fatigue strength Applications: Statically and dynamically stressed components for vehicles, engines and machines. For parts of larger cross-sections, crankshafts, gears. Heat Treatment: Soft annealing: heat to 680-720C, cool slowly. Hardness after annealing: Max. 241 HB Hardening: 820 - 850 C Normalizing temperature: 840-880C Tempering: 540-680C.