Qatari Agricultural Chemicals Suppliers and Manufacturers

Pozzolan is a siliceous or siliceous and aluminous material that in itself possesses little or no cementitious value but will, in finely divided form and in the presence of moisture, chemically react with calcium hydroxide at ordinary temperatures to form compounds having cementitious properties. It is therefore classified as a cementitious material. There are both natural and artificial pozzolans. The quantification of the capacity of a pozzolan to react with calcium hydroxide and water is given by measuring its pozzolanic activity.

Microsilica (silica fume) is a by-product of silicon metal or ferrosilicon industries, is an amorphous silicon dioxide SiO2. This product reacts chemically with the calcium hydroxide in the cement paste which yields a calcium silicate hydrate gel that significantly enhances strength and durability. The super fine microsilica fills the voids between cement particles creating a very dense, less permeable concrete. Physical characteristics: Color: gray or gray white powder Bulk density: 320-700 kg/m3 Chemical composition: Items SiO2 Al2O3 Fe2O3 MgO CaO Na2O Moisture Content 75-98% 1.0-0.2% 0.9-0.3% 0.7-0.1% 0.3-0.1% 1.3-0.2% Fineness: the fineness of the silica fume is less than 1 1/4m, and the average particle size is 0.1 0.3 1/4m, and the specific surface area is 20 - 28 m2/g. The fineness and specific surface area are about 80-100 times of cement and 50-70 times of fly ash. Maxtech Micro Silica supplies will be as per QCS 2014 (ASTM C1240): SiO2: >/= 92% LOI:

Microsilica (silica fume) is a by-product from silicon metal or ferrosilicon industries, is an amorphous silicon dioxide SiO2. This product reacts chemically with the calcium hydroxide in the cement paste which yields a calcium silicate hydrate gel that significantly enhances strength and durability. The super fine microsilica fills the voids between cement particles creating a very dense, less permeable concrete. White Cement advantages: Sustainability: Solar Reflectance Index (SRI): Floors finished with white or pastel color concrete will have a much higher SRI than floors with gray concrete, therefore they will reflect light better, and generate energy savings for the lifetime of the floors. Reduction of Heat Island effect: By constructing buildings with white concrete roofs or light-colored roof tiles, the Heat Island Effect is reduced from surfaces generating less heat and improved reflectivity. Architectural Concrete: White Portland Cement is ideal for decorative concrete and Architectural Concrete applications, Masonry and Cementitious Building Products. A key advantage of using white cement for these applications is that it provides a base color that can be tinted to custom colors to meet any color spectrum demand.

GGBFS Ground granulated blast furnace slag (GGBFS) The ground granulated blast furnace slag (GGBFS) is a by-product of iron manufacturing which when added to concrete improves its properties such as workability, strength and durability. This material is obtained by the heating of iron ore, limestone and coke at a temperature about 1500 degree Celsius. The process is carried out in a blast furnace. The formation of GGBFS is not direct. The by-product of iron manufacturing is a molten slag and molten iron. The molten slag consists of alumina and silica, also with the certain amount of oxides. This slag is later granulated by cooling it. For this, it is allowed to pass through a high-pressure water jet. This result in quenching of the particles which results in granules of size lesser than 5mm in diameter. The main constituents of blast furnace slag are CaO, SiO2, Al2O3 and MgO. These are the minerals that are found in most of the cementitious substances. The particles are further dried and ground in a rotating ball mill to form a fine powder, known as ground granulated blast furnace slag cement. Now different methods can be employed to perform the main process called as the quenching. Applications & Benefits of GGBFS: In concrete: The incorporation of ground granulated blast furnace slag in concrete manufacture gains many advantages which are mentioned below: GGBFS in concrete increases the strength and durability of the concrete structure. It reduces voids in concrete hence reducing permeability GGBFS gives a workable mix. It possesses good pumpable and compaction characteristics The structure made of GGBFS constituents help in increasing sulphate attack resistance. The penetration of chloride can be decreased. The heat of hydration is less compared to conventional mix hydration. The alkali-silica reaction is resisted highly. These make the concrete more chemically stable. Gives good surface finish and improves aesthetics. The color is more even and light. Lower chances of efflorescence. The maintenance and repair cost of structures are reduced thus increasing the life cycle of concrete structures. Unlike cement, GGBFS does not produce carbon dioxide, sulphur dioxide or nitrogen oxides. White Cement: White Portland Cement is of high quality, whiteness and strength, it essentially has the same properties and characteristics as gray cement, except for color. It is widely used in numerous applications such as precast concrete, cast-in-place concrete, terrazzo, median barriers, curbs, tile grout, paint, masonry units, swimming pools, glass fibre reinforced surface bonding mortars.