Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit Density ISO 1183 0.944-0.955 g/cm3 MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min Tensile strength at yield ISO 527-2 22 MPa Elongation at break ISO 527-2 >350 % ESCR F50,50 C,100% ASTM D-1693A 1000 h VICAT ASTM D-1525 126 C For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Tests Value Unit Melt Flow Rate (MFR) 3.2 g/10min Density 0.939 g/cm3 Melting Point 127 C Tensile Yield Strength 21 Mpa Tensile Strength at Break 28 Mpa Elongation at Break 1,100 % Flexural Modulus 750 Mpa Brittle Temperature
Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 % Dark Drop Impact 105 g Brittle Temperature(F 50) -70 C Vicat Softening Point 90 C
Tests Value Unit Melt Flow Rate (MFR) 20 g/10min Density 0.924 g/cm3 Tensile Strength MD12 Mpa TD 10 Elongation at Yield 13 % Elongation at Break 200 % Dark Drop Impact 105 g Brittle Temperature(F 50) -70 C Vicat Softening Point 90 C
Name of Product: Recycled Polypropylene Granules Product origin: Product is recycled and reprocessed in United Arab Emirates Key Specification: The melt flow index (MFI) is from 6-10g/10mins. Depending on the customer we can have different formulation to be customer specific Minimum Order: 20 metric tons or one 20ft container
HDPE BLACK GRANULES, PIPE GRADES from Thailand. Please contact us for further discussions
PVC compound can be divided into three main categories: 1. Soft PVC Compound, 2. Rigid PVC Compound 3. Pharmaceutical Grade Compound Contact us for more information
Grade: Injection Grade / Application: Electronic appliance Body Part / Type: Raw Granules Resins / Material: PC Plastic Raw Material Granules / Appearance: Clear - Transparent Pellets / Package: 25 KG PP Bag / Melt Flow Index: 15 / Impact: 50-65
Grade: Injection Grade / Application: Electronic Appliance Body Part, Power Plugs and Socket / Type: Raw Granules Resins / Appearance: White Pellets / Black Pellets / Package 25 KG PP Bag / Melt Flow Index: 8 / Impact: 8-9
Grade: Injection Grade/Extrusion Grade / Application: Electronic Appliance Body Part, Luggage Case, Toys Spare Part / Type: Raw Granules Resins / Material: ABS Plastic Raw / Material Granules / Appearance: White / Black Pellets / Package: 25 KG PP Bag / Melt Flow Index: 28 / Impact: 15-16 (Black pellets) / 18-22 (White pellets)
Grade: Injection Grade / Application: Electronic Appliance Body Part, Pen, General Injection Products / Type: Raw Granules Resins / Material: GPPS Plastic Raw Material Granules / Sample: Available / Melt Flow Index: 7-8 / Impact: 4 / Appearance; Clear / Transparent Pellets Package 25 KG PP Bag
Material: Hdpe Plastic Granules Color: Natural Tea Color Application: Plastic bag packing film grade Density: 0.940~0.976 G/cm3
Contact Us
Pom Regrind Mixed Color, Black Color, White / Natural Color
Pom Regrind, Black, White / Natural, Mixed Colors
Pom Regrind, White / Natural Color, Origin: Thailand. Contact Us
Clear PETG granules / Virgin PETG plastic raw material / PETG pellet. contact us for more information
100% biodegradable PBS resin / Polybutylene succinate granules / PBS pellets. Please contact us for more information
100% PLA biodegradable corn starch plastic granules for blowing film. Please contact us for more information