Quantity: 100-200 MT
Specs:
MN: 55% Minimum
SI: 12%
C: 3% Max
P: 0.3% Max
S: 0.05% Max
Size: 0 to 3 mm (90%)
Origin: India
Packing: 1 MT bags.
Rate: Please give your best Offer
The Manganese layer, belongs to brown manganese ore (manganite), has a symbol MnO, and corresponds to an oxidation state of +
These indicators are the best characteristic of our final product, as they show a single oxidation-reduction reaction.
The prepared layer has a reserve of 4,000,000 metric tons of manganese ore, with a low concentrate of iron and phosphorus, without carbonate impurities and the following characteristics of manganese concentration:
Medium Level 30 35%
Low Level 23 29%
The granulation produced by our crusher is next:
Zero 10mm 25%
100 150mm 75%
Transportation is carried out in closed containers for better safety of Mn percentage in ore.
Manganese ore is a silver-gray metal with a pinkish tinge.
It is a hard metallic element although it is quite brittle.
Manganese ores are found in metamorphic rocks or sedimentary deposits.
Pyrolusite is the main ore mineral for manganese.
Manganese: Ore 42-46%
Mo 0,024%
Zr 0,015%
Pb 0,101%
Zn 0,012%
Co 0,99%
Fe 10,12%
Mn 36,81%
V 1,28%
Ti 4,20%
As 0,068%
W 0,458%
Hf 0,789%
Cr 0,125%
We supply the Quality Ferro Alloys Like
Ferro Manganese HC / MC / LC
Grade I II III
Mn 65% min 70% Min 75% Min
Si 2% Max 2% Max 1.50% Max
C 8% Max 8% Max 8% Max
S 0.05% Max 0.035% Max 0.03% Max
P 0.40% Max 0.30% Max 0.25% Max
MC FeMn
Mn 70%Min /75% Min / 78% Min
Si 1.50% Max
C 1.50% MAX
S 0.03% Max
P 0.25% Max
We supply the Quality Ferro Alloys Like
Silico Manganese HC
Grade I II
Mn 60% min 65% Min
Si 14% Min 15% Min / 16% Min
C 2.50% Max 2% Max
S 0.03% Max 0.03% Max
P 0.30% Max 0.30% Max
Ferro Manganese (FeMn) is product of the blast furnace containing besides iron, 70 to 85% of manganese. It is used as a de-oxidizer for manufacturing of non-magnetic stainless steel and for the introduction of manganese into steel. Manganese is very important element in steel as it improves the strength, toughness, hardness and workability. Manganese also helps in getting ingots free from blow holes.
It lowers the critical temperature and promotes the formation of pearlite. Manganese dissolves in solid solution of ferrite, combines with carbon to form carbides. it improves weldability, wear resistance and strength without adversely affecting the ductility of steel.