Bearing Steel Grit is processed to the high quality,with strict quality control at every stage of processing,packaging and transportation.Compared with traditional steel grit made by crushing steel shot, bearing steel grit is crushed directly from cut-off bearing steel into grit. It has the better resistance due to it has higher metallic cr composition than normal casting steel grit.
Name Bluing steel strap Painting steel strap Primary color Galvanized steel strap Color blue black, blue, green, coffee color, grey primary, white galvanize Surface finish blue & oiled painted & waxed primary & oiled galvanized Material Q195 / Q235 / Q345B / DB460 / high tensile steel Elongation 3-6% / 6-8% / 8-12% Tensile strength 600-700Mpa / 700-780Mpa / 780-880Mpa / 880-980Mpa Enwind type Ribbon / Oscillated Width 9.5-50mm (Width tolerance: 0.1mm) Thickness 0.27-2.5mm (Thickness tolerance: 0.02mm)
Bearing Steel Grit is processed to the high quality,with strict quality control at every stage of processing,packaging and transportation.Compared with traditional steel grit made by crushing steel shot, bearing steel grit is crushed directly from cut-off bearing steel into grit. It has the better resistance due to it has higher metallic cr composition than normal casting steel grit.
Blasting abrasive material steel grit 1, factory price with good quality. 2, G10-G120 3, 0.2mm-2.5mm 1. Production specification: g10, g12, g14, g16, g18, g25, g40, g50, g80, g120 2. Chemical composition of cast steel grit: c 0.70-1.20%, mn 0.60-1.20%, si0.40-1.20%, s0.05%, p 0.05% 3. Gp: 42-50hrc (399-509hv). Gl: 56-60hrc (620-713hv). Gh: 63-66hrc (795-889hv). 4. Microstructure: tempered marten site high strength, durable, ervin life: cast steel grit: 2500 cycles.
1. Production specification: g10£¬g12, g14, g16, g18, g25, g40, g50, g80, g120 2. Chemical composition of the products: c 0.70-1.20%, mn 0.60-1.20%, si0.40-1.20%, s¡ü0.05%, p ¡ü0.05% 3. Gp: 42-50hrc (399-509hv) Gl: 56-60hrc (620-713hv) Gh: 63-66hrc (795-889hv) 4. Microstructure: tempered marten site high strength, durable, ervin life: cast steel grit: 2500 cycles Pallet with 40 bags of 25 kgs
1. Production specification: g10£¬g12, g14, g16, g18, g25, g40, g50, g80, g120 2. Chemical composition of the products: c 0.70-1.20%, mn 0.60-1.20%, si0.40-1.20%, s¡ü0.05%, p ¡ü0.05% 3. Gp: 42-50hrc (399-509hv) Gl: 56-60hrc (620-713hv) Gh: 63-66hrc (795-889hv) 4. Microstructure: tempered marten site high strength, durable, ervin life: cast steel grit: 2500 cycles Pallet with 40 bags of 25 kgs
STEEL GRIT CAPABILITY INTRODUCTION: Raw material is non casting bearing steel, it is crushed after quenching, then it is tempered. Product features with wear resistance and high impact toughness. According to different application, steel grit is devided into below 3 types: Type A: Hardness>60HRC This type is specially developed for granite cutting with stable performance, uniform grain size and high wear resistant. It has been approved by our customers that angular steel grit are sharper, faster cutting speed than arc steel grit and sawing surface finished is flatter and smoother. Type B: Hardness>53-60HRC It is angular shape in the originals and is gradually ground round, especially applicable to removing the oxygenated surface, cleaning of metal parts and shot peening Type C: Hardness> 40-50HRC The hardness is lower than type B, In the process of the abrasives blasting. Its edges are removed slowly, especially applicable to removing the oxygenated surface, cleaning of metal parts and pre-treatment. 25kgs/bag.
We strictly according to GB "GB/T18838.3-2008 high carbon steel shot and sand", American steel casting association "SFSA20-66 cast steel abrasive standard", American motorcar engineer association "SAE standards," J827 cast steel shot in Chinese Black people republic of metallurgical industry "YB/T5149-93 cast steel shot", the U.S. army standard "MIL - S - 851 cleaning and strengthen with metal kind steel grit and steel shot standards" and "international organization for standardization ISO11124-3 standard high carbon steel shot cast. Steel grit plastic woven sack packaging, packaging bags which steel grit, steel grit wood pallet packaging, paper bag steel grit packaging, bucket type steel bolus packaging.
Made of bearing steel material with special technology, the bearing angular steel grit has fine and homogeneous microstructure. With advantages of higher efficiency, longer life-cycle and less consumption than normal steel grit, it will obviously reduce the comprehensive cost. Such an excellent steel grit is recommended for blast cleaning and surface preparation. G10, G12, G14, G16, G18, G25, G40, G50, G80, G120.
Products steel grit Chemical compositionc0.70~1.20% Mn0.6~1.20% Si0.40~1.20% Sless than 0.05% Pless than 0.05% Microhardnessnormal: 40~50hrc (377~509hv) Special: 52~56hrc (543~620hv) Special: 56~60hrc (620~713hv) Hardness deviationmax deviation ± 3.0hrc, ± 40hv Microstructureeven tempered martensite and dispersed carbon Density7.2g/cm3 Steel grit types: Gp:angular when new, this grit rapidly rounds off in use and its particularly suited descaling applications. Gl:although harder then gp steel grit, also loses its sharp edges during shto basting and is particularly suited to descaling and surface preparation applications. Gh:having maximum hardness, gh always remains angular in its operating mix. These abrasive are particularly effective in surface treatment processes and produce a uniform, etched finish, gh angular grit should only be used in wheel machines where working requirements take precedence over cost price considerations (for example with rolling mill cylinders or when a special finish is needed). For use mainly with compressed air equipment. 25 kgs/bag, 40bags/pallect.