95# Fischer Tropsch Wax

PTFE Wax for Coating and Ink

Fischer Tropsch wax Grade: Candle grade Usage and Advantage Usage :This wax is Fischer-Tropsch wax can completely replace the pafaffine wax and slack wax applied in the candle industry. End user can reduce the input proportion and save 20% cost . This wax is widely used for cup candle products . Advantages : Less smoke, resistant to burning, more white color , power state easy for production and save the cost .

SC178 is a modified micronized Fischer-Tropsch wax that is a primary replacement for fluorinated mixed wax powders for general purpose inks, coatings, wood finishes and more. A more economical one, balancing performance and cost, is available:Less matting,Good slipperiness,Excellent abrasion resistance and Anti-adhesion properties. SC178 has an average particle size of 5.5 to 6.5 microns with a maximum particle size of 21 microns. It is recommended to add 0.5-1% of SC178 to the system.SC178 is insoluble in solvents at room temperature as well as UV-based monomers and oligomers.

SC178 is a modified micronized Fischer-Tropsch wax that is a primary replacement for fluorinated mixed wax powders for general purpose inks, coatings, wood finishes and more. A more economical one, balancing performance and cost, is available:Less matting,Good slipperiness,Excellent abrasion resistance and Anti-adhesion properties. SC178 has an average particle size of 5.5 to 6.5 microns with a maximum particle size of 21 microns. It is recommended to add 0.5-1% of SC178 to the system.SC178 is insoluble in solvents at room temperature as well as UV-based monomers and oligomers.

Properties Unit Specification Solidifying point 100-109 Drop point 110-119 Viscosity mm2/s at120 18-35 Penetration 0.1mm/100g 5s at 25 Max.2 Oil content % wt Max.0.2 Size,16mesh - 85% PACKING :25 KG Valve bag / 980KG Jumbo bag

Application:It is used in the manufacture of adhesives, rubber, cosmetics and industrial cleaners, as well as in metalworking. Features and Benefits: 1.Low oil content 2.Low Penetration 3.High Hardness Properties Unit Test method Specifications Result Melting point C ASTM D3954-94-2004 80-86 80 Penetration 0.1mm/100g 5s at25 C ASTM D1321-2010 10-18 12 Oil content ASTM D721-2006 1-3 1 Viscosity mm2/s 100 C ASTM D445-2009 8-10 9 Colour:White powder Packing:25 KG Valve bag / 980KG Jumbo bag

Usage :Fischer-Tropsch Wax for Hot Melt Adhesive, PVC, Master-batch, Road Marking Paint PACKING :25 KG Valve bag / 980KG Jumbo bag Properties Test Method Specification Drop point ASTMD3954-94-2004 107 Viscosity,mm2/s at120 ASTM D445-2009 11.3 Viscosity,cps at140 Brookfield 6.7 Penetration,0.1mm/100g,5s @25 ASTM D1321-2010 3.8 Oil content ASTM D721-2006 3.2% Size,40mesh GB/T 6005-2008 92%

Usage :Fischer-Tropsch Wax for Hot Melt Adhesive, PVC, Master-batch, PVC Stabilizer, Road Marking Paint PACKING :25 KG Valve bag / 980KG Jumbo bag Properties Unit Specification Solidifying point 100-109 Drop point 110-119 Viscosity mm2/s at120 18-35 Penetration 0.1mm/100g 5s at 25 Max.2 Oil content % wt Max.0.2 Size,16mesh - 85%

Fischer Tropsch Wax Properties Test Method Specification Drop point ASTMD3954-94-2004 102-103 Oil content ASTM D721-2006