High Speed Cut To Length

We put forward a high quality of assortment of Nickel which is available in many forms including LME registered and non registered cathodes, cut cathodes, briquettes, pellets, disks, shots, granules, foil, powder, flakes, sheet, wire, mesh, spheres, “evaporation slugs”, and rods. Nickel is a silvery white metal that takes on a high polish. It is hard, malleable, ductile, somewhat ferromagnetic, and a fair conductor of heat and electricity

SPECIFICATIONS: the following Percentage Points: Chemical Composition Carbon - 0.54 to 0.82% Phosphorus - 0.035% max Manganese - 0.60 to 1.05% As. - 0,01max of Mass share Silicone - 0.18 to 0.40% Sulphur - 0.035% max Norms - R-50 GOST-7173-75 / R-65 GOST- 8165-75 The scrap consists of R-50 (51,67 KG/m) R-65 (64,72KG/m) Used Rails shall be considered free of alloys when the residual alloying elements do not exceed Cut to 1.5 meter length (standard) 1. Technical terms: USED RAIL R50-R65 2. Specifications and Chemical Composition: Used Rail: R50 (51.67KG/Meter, GOST 7173-55), Used Rail: R65 (64.72KG/Meter, GOST 8161-75). Size & Weight: Length: 12meter ~ 12.5meter Maximum or less according tobuyerâ??s instruction; Expenses on seller Width: 5.5 inches ; Weight: 64.72Kg. No fishplates or steel pieces or bolts are attached to the used rails. All rails are clean and straight. No pitting. Only atmospheric rust No heavy rust. It is mandatory that Rails must be cut into length 1.5 meter(max.) before shipment.

Length: As Required Cu (Min): 99.9% Alloy Or Not: Non-Alloy Ultimate Strength ( MPa): 205 Elongation ( %): 45% Wall Thickness: 0.2mm~910mm Outside Diameter: 2mm*4mm~1016mm*1219mm Processing Service: Bending, Punching, Cutting Standard: JIS ASTM DIN EN ISO Material: C10200/C11000/C12000/C12200/TU1/TU2/T2/custom Surface: Polished Feature: High Strength Technique: Cold Rolled Hot Rolled Size: Custom Size

Monel 401 has excellent strength and plasticity, and has good pressure processing performance in both cold and hot states. It is a corrosion-resistant alloy with large dosage, wide application and excellent comprehensive performance. The alloy has excellent corrosion resistance in HF and F2 media, and is one of the few important materials that can withstand hydrofluoric acid. An important feature of this alloy is that it generally does not produce stress corrosion cracks and has good cutting performance. A kind of Monel alloy, its alloy structure is a high-strength single-phase solid solution, 3 a nickel-based alloy similar to Monel 400, and the corrosion resistance of the metal is fundamentally obtained by hindering the migration of charged particles through the discharge process of hydrogen ions. Obtained, the addition of 30% Cu by mass fraction minimizes the corrosion rate of TH, Ni in F, Cl and other halogen element ionic media, and the higher the Cu content, the better the resistance to sulfuric acid and phosphoric acid. Adding mass fraction to Monel 401 55% Cu improves the corrosion resistance of the alloy in reducing acids. Application fields: Wirewound Resistors bimetal contact Electrical and Electronic Applications Marine Engineering Chemical and Hydrocarbon Processing Equipment petrol and fresh water tanks Distiller degas heater Boiler feed water heaters and other heat exchangers Valves, pumps, shafts, fittings and fasteners Industrial heat exchanger Chlorinated solvents Crude distillation tower We can provide the following the form:Monel alloy401 coil; Monel alloy 401 strip;Monel alloy 401 plate; Monel alloy 401 sheets; Monel alloy 401 tube; Monel alloy 401 pipe;Monel alloy 401 flat; Monel alloy 401 bar UNS:N04401