High Power Graphite Electrode For Eaf

Specifications Graphite electrodediameter: 350mm-600mm (14-24 inch).Length:1800mm-2400mmnipples: 3tpi 4tpiiso9001:2000 standard Specification of uhp graphite electrode ItemsUnitNominal diameter(mm) 350-400450-600 Specific resistance(not over)Electrodenipple¦ì¦¸.M5.54.05.84.0 Bending strength(not below)ElectrodenippleMpa10.516.010.516.0 Elastic modulus(not over)ElectrodenippleGpa14.018.014.018.0 Bulk density(not below)ElectrodenippleG/cm31.671.761.671.76 Cte(100-600)0c(not over)Electrodenipple10-6/0c1.51.21.51.2 Ash(not over)Electrodenipple%0.30.20.30.2 Suggested current carrying capacities of graphite electrode: Diameter Suggested current-carrying capacities ( a ) MmInchA A/cm2 3001215000-2200020-30 3501420000-3000020-30 4001625000-4000019-30 4501832000-4500019-27 5002038000-5500018-27 5502245000-65000 6002450000-70000 Size of graphite electrode: DiameterLength NominalActual(mm)NominalTolerance Mm InchLow spotMinMaxMm Mm 350143493523571800Max+100min-100 400164004034091600, 1800, 2000, 2200 45018451454460 500205025055111800, 2000.2200, 2400 55022553556562 600246046076132000, 2200, 2400 Wood packaging

Items, unit, nominal diameter(mm) , , 250-400 Specific resistance (not over), electrodenipple, .M, 6.55.0 Bending strength (not below), electrode nipple, mpa, 10.0 14.0 Elastic modulus (not over), electrode nipple, gpa, 12.0 14.0 Bulk density (not below), electrode nipple, g/cm3, 1.621.72 Cte(100-600)0c (not over), electrode nipple, 10-6/0c, 2.7 2.5 Ash(not over), electrode nipple, %, 0.30.3 Wood packaging

ItemsUnitNominal diameter(mm) 250-400 Specific resistance (not over)Electrode nipple¦ì¦¸.M6.24.8 Bending strength (not below)Electrode nippleMpa10.0 15.0 Elastic modulus (not over)Electrode nippleGpa12.0 16.0 Bulk density (not below)Electrode nippleG/cm31.65 1.75 Cte(100-600)0c (not over)Electrode nipple10-6/0c2.4 2.2 Ash(not over)Electrodenipple%0.30.3 Wood packaging

UHP 400mm*1800mm UHP 450mm*1800mm Used in steel, cement and glass manufacturing, expanded graphite - based sealing gaskets, graphite grease, braid, brushes, brake lining, etc.

ItemsUnitNominal diameter(mm) 250-400 Specific resistance (not over)Electrodenipple¦ì¦¸.M6.55.0 Bending strength (not below)Electrode nippleMpa10.0 14.0 Elastic modulus (not over)Electrode nippleGpa12.0 14.0 Bulk density (not below)Electrode nippleG/cm31.621.72 Cte(100-600)0c (not over)Electrode nipple10-6/0c2.7 2.5 Ash(not over)Electrode nipple%0.30.3 Wood packaging

Supplier: Graphite, electrode, graphite electrode for electric arc furnace, high power graphite electrode for eaf, graphite electrodes used in eaf or lf, uhp graphite electrode, ultra high power graphite electrode, shp graphite electrode

graphite electrode is acting as a conductive body which release heat in the form of arc for heating and melting steel in the furnace.According to the application, it can be divided into regular power(RP), high power(HP) and ultra high power(UHP). Graphite electrode is widely used in EAF, LRF, submerged arc furnace(producing ferroalloy, pure silicon, yellow phosphorus, calcium carbide etc), resistance furnace

The graphite electrode comprises: (1) Regular power graphite electrode( RP grade Graphite Electrode) . Graphite electrode with current density less than 17a / cm2 is allowed to be used in common power electric furnaces for steelmaking, silicon smelting and yellow phosphorus smelting. (2) Oxidation resistant coating graphite electrode. A graphite electrode coated with an anti-oxidation protective layer (graphite electrode anti oxidant). The formation of both conductive and high temperature oxidation resistant protective layer can reduce the electrode consumption (19% ~ 50%), prolong the service life of the electrode (22% ~ 60%), and reduce the electric energy consumption of the electrode. The popularization and application of this technology can bring such economic and social effects as follows: 1. The unit consumption of graphite electrode is less, and the production cost is reduced to a certain extent. For example, according to the consumption of 35 graphite electrodes per week and 165 refining heats of LF refining furnace in a steel-making plant without shutdown in the whole year, 373 (153 tons) electrodes can be saved every year by using graphite electrode oxidation resistance technology, and RMB 2585700 can be saved by RMB 16900 per ton of ultra-high power electrode per year. 2 The graphite electrode consumes less electricity, saves the unit electricity consumption of steelmaking, saves the production cost, saves energy! 3. Because the graphite electrode is replaced less times, the labor amount and risk coefficient of operators are reduced, and the production efficiency is improved. 4 Graphite electrode is a high consumption and high pollution product, which has a very important social significance in the days of promoting energy conservation, emission reduction and environmental protection. This technology is still in the stage of research and development in China, and some domestic manufacturers have begun to produce it. It is widely used in Japan and other developed countries. At present, there are also companies that import the anti-oxidation protective coating in China. (3) High power graphite electrode (HP grade Graphite Electrode). Graphite electrode with current density of 18-25a / cm2 is allowed to be used in high power electric arc furnace for steelmaking. (4) Ultra high power graphite electrode( UHP grade Graphite Electrode). Graphite electrode with current density greater than 25A / cm2 is allowed. It is mainly used in ultra high power EAF.