Specifications
1. Thickness: 0.1-1.2mm, width: 25-395mm
2. Grade: Q195,
3. Zinc coating:40-180g/m2
4. Pallet weight: 1.80-2.50MT
5. Surface treatment: oiled, un-oiled, chromate
6. Packing: packed in pallet suitable for ocean transportation
7. Supply ability: 120000tons/ year
8. Delivery time: according to the ordered quantity
9. Application: Nowadays Hot Dipped Galvanized Steel Coil has become the most perfect building materials in construction, transportation, manufacture, light industry, office furniture, and other areas all over the world.
10. There are 6 hot-dipped galvanized line, this including tow galvanized lines and four gas calefaction lines. The thickness of the Zinc coating of the product can be controlled exactly, the dimension tolerance is very small, the surface of passivated steel strip has a good performance of anti-corrosion. The available products can be fulfilled according to the JISG and national standard.
Packed in pallet suitable for ocean transportation.
We deals in the following products of India, China, Taiwan and Korea Origin:-
Galvanized Steel (Galvanized Steel Tapes, Galvanized Steel Wires, Galvanized Steel Strips, Galvanized Steel Coils, Galvanized tubes etc)
* Galvanized strip steel is a kind of raw material called (zinc), which is used to coat the long and narrow strip steel which is cold-rolled or hot-rolled to varying degrees. Hot dip galvanizing has the advantages of even coating, strong adhesion and long service life. Complex physical and chemical reactions occur between the hot-dip galvanized steel pipe substrate and the molten plating solution, forming a corrosion resistant zinc iron alloy layer with compact structure. The alloy layer is integrated with the pure zinc layer and the strip steel matrix. Therefore, it has strong corrosion resistance.
Use of galvanized strip steel: strip steel is widely used in the production of welded steel pipes, as the blank of cold bending section steel, and in the manufacture of bicycle frames, rims, clamps, washers, spring blades, saw blades, hardware products and blades. The use of high hot dip galvanized strip steel is naturally associated with the application of galvanized strip steel in construction, light industry, automobile, agriculture, animal husbandry, fishery, commerce and other industries.
Processing Service : Bending, Welding, Decoiling, Cutting, Punching, Welding
Invoicing : by actual weight
Delivery Time : 7-15 days
Technique : Hot Rolled Based, Cold Rolled
Port:
Tianjin Qingdao or according to your requirement
Packaging Details : in bundles, in bulk, customized packing.
Production process:
The first stage: pickling and decontamination of the whole roll of strip steel to make the surface bright and clean.
The second stage: after pickling, it is cleaned in ammonium chloride or zinc chloride aqueous solution or mixed ammonium chloride and zinc chloride aqueous solution tank, and then sent to the hot dip tank for galvanizing.
The third stage: after the strip steel is galvanized, it is rolled up and put into storage. The galvanized layer can generally not be less than 500g/m2 according to the customer's needs, and any sample shall not be less than 480g/m2.
Galvanized strip steel is a kind of raw material called (zinc), which is used to coat the long and narrow strip steel which is cold-rolled or hot-rolled to varying degrees. Hot dip galvanizing has the advantages of even coating, strong adhesion and long service life. Complex physical and chemical reactions occur between the hot-dip galvanized steel pipe substrate and the molten plating solution, forming a corrosion resistant zinc iron alloy layer with compact structure. The alloy layer is integrated with the pure zinc layer and the strip steel matrix. Therefore, it has strong corrosion resistance.
Use of galvanized strip steel: strip steel is widely used in the production of welded steel pipes, as the blank of cold bending section steel, and in the manufacture of bicycle frames, rims, clamps, washers, spring blades, saw blades, hardware products and blades. The use of high hot dip galvanized strip steel is naturally associated with the application of galvanized strip steel in construction, light industry, automobile, agriculture, animal husbandry, fishery, commerce and other industries.
Production process:
The first stage: pickling and decontamination of the whole roll of strip steel to make the surface bright and clean.
The second stage: after pickling, it is cleaned in ammonium chloride or zinc chloride aqueous solution or mixed ammonium chloride and zinc chloride aqueous solution tank, and then sent to the hot dip tank for galvanizing.
The third stage: after the strip steel is galvanized, it is rolled up and put into storage. The galvanized layer can generally not be less than 500g/m2 according to the customer's needs, and any sample shall not be less than 480g/m2.
Post treatment of galvanized strip steel includes passivation, pre phosphating and oiling. First of all, passivation treatment should be carried out on the galvanized strip steel, which can improve the surface structure and luster of the zinc coating, improve the corrosion resistance and service life of the zinc coating, and improve the adhesion between the coating and the base metal.
Galvanized strip steel is a kind of raw material called (zinc), which is used to coat the long and narrow strip steel which is cold-rolled or hot-rolled to varying degrees. Hot dip galvanizing has the advantages of even coating, strong adhesion and long service life. Complex physical and chemical reactions occur between the hot-dip galvanized steel pipe substrate and the molten plating solution, forming a corrosion resistant zinc iron alloy layer with compact structure. The alloy layer is integrated with the pure zinc layer and the strip steel matrix. Therefore, it has strong corrosion resistance.
Use of galvanized strip steel: strip steel is widely used in the production of welded steel pipes, as the blank of cold bending section steel, and in the manufacture of bicycle frames, rims, clamps, washers, spring blades, saw blades, hardware products and blades. The use of high hot dip galvanized strip steel is naturally associated with the application of galvanized strip steel in construction, light industry, automobile, agriculture, animal husbandry, fishery, commerce and other industries.
Production process:
The first stage: pickling and decontamination of the whole roll of strip steel to make the surface bright and clean.
The second stage: after pickling, it is cleaned in ammonium chloride or zinc chloride aqueous solution or mixed ammonium chloride and zinc chloride aqueous solution tank, and then sent to the hot dip tank for galvanizing.
The third stage: after the strip steel is galvanized, it is rolled up and put into storage. The galvanized layer can generally not be less than 500g/m2 according to the customer's needs, and any sample shall not be less than 480g/m2.
65Mn CK67 high carbon cold rolled spring steel strip
Hardened and Tempered Steel Strip
Hardened and Tempered is a thermal process that strengthens steel strips through a controlled heating and cooling process. The hardening process involves heating the steel strip to above the rapidly cooling. The steel strip in this condition is extremely brittle and requires further treatment in the tempering. Then strips are reheated to a lower temperature and holding it at the given temperature for a given period of time. This process is done in an inert atmosphere to avoid oxidation. This type of steel strip has big degree of toughness and has excellent spring properties
Standard AISI, ASTM, BS, DIN, GB, JIS
Place of Origin China
Material Hot Rolled
Surface Polished
Application shutter door, plastic trowel, bricklayer trowel, putty knives, scraper, springs, metal part, shoe insole, shoe accessories, blade, band saw blade
Brand Name HENSON
Width 2.0mm-300.0mm
Length Customize
Tolerance +/-10%
Hardness 40-55HRC
Surface nature, blue, yellow, white, polish
Edge Slit,Round,Square
MOQ 1000KGS
Tolerance thickness+/-0.01mm max,width +/-0.05mm max
Type strip,coil,sheet
Coil ID 300-500 mm
Tensile Strength 540-1575N/mm2
Yield Strength 370-1475N/mm2
Commodity: Hot dipped galvanized steel strips
Surface: Chromated, Unoiled, tension-levelled
Spangle: regular spangle
Zinc Coating: 60-275gms/m2/ both sides
Coils ID: 508mm
Coils OD: 1000mm-1300mm
Size: (0.20-2.5)mm * (32-600) mm *C
Standard: Q195
Usage: The galvanized steel strips are used in the making of C-style steel, fire protection volume valve, the paint keel, the light steel keel, guard rail, and the galvanized steel pipes.