Manual Mold Silicon Rubber

Applications of manual mold silicone rubber Manual mold silicone rubber is mainly used for model design of manual mold, cement products, low melting point alloy molds, alloy toys, plastic toys, electronics, handicrafts, stationery, large-scale sculpture, reproduction of cultural relic, pad printing allocation, electronic equipment antivibration, and so on. Features of manual mold silicone rubber Manual mold silicone has good elasticity, non-deformation, high temperature resistance, low shrinkage. And it is suitable for manual mold design and small duplication mold production. FAQ of manual mold silicone rubber Why is the manual silicone mold oily? The molding silicone rubber itself doesn contain any oil, so it won be oily. If the mold is oily, it may be because you add the compound silicone oil, which contains silicon oil and white oil. For getting further information about our silicone rubber, Please feel free to contact with Miss Shameya. She can speak good Arabic and English and Chinese for an easier communication with you.

Applications of manual mold silicone rubber Manual mold silicone rubber is mainly used for model design of manual mold, cement products, low melting point alloy molds, alloy toys, plastic toys, electronics, handicrafts, stationery, large-scale sculpture, reproduction of cultural relic, pad printing allocation, electronic equipment antivibration, and so on. Features of manual mold silicone rubber Manual mold silicone has good elasticity, non-deformation, high temperature resistance, low shrinkage. And it is suitable for manual mold design and small duplication mold production. Faq of manual mold silicone rubber Why is the manual silicone mold oily? The molding silicone rubber itself doesn contain any oil, so it won be oily. If the mold is oily, it may be because you add the compound silicone oil, which contains silicon oil and white oil. For getting further information about our silicone rubber, please feel free to contact with miss shameya. She can speak good arabic and english and chinese for an easier communication with you.

a. Applications of Manual Molding Silicone Rubber: Manual Molding Silicone Rubber is mainly used for model design of manual mold, PVC plastic molds, cement products, low melting point alloy molds, alloy toy, plastic toy, electronics, handicrafts, large-scale sculpture, reproduction of cultural relic, sole molds, pad printing allocation, Electronic equipment anti-vibration, etc. b. Model Codes of Manual Molding Silicone Rubber: HY-528 is applicable to make molds of smaller products and the production will be 2 to 3 pieces. HY-540, compared to other two types, for its moderate hardness and better quality & performance, its production will be 20 to 30 pieces. HY-570is applicable to large size products duplications and Electronic equipment anti-vibration. b. Operation Instructions for Manual Molding Silicone Rubber: RTV-2 Manual Molding Silicone Rubber is a flowable liquid, and the quality has nothing to do with the color. It consists of two components. Part A is a flowable liquid silicone rubber, part B is the curing agent. Firstly, after your previous work of dealing with the original model, take some liquid silicone rubber , add 2% to 3% curing agent of the amount of silicon, and mix them evenly. Then after vacuum-pumping the mixture, you can pour it into the mold frame. The silicone mold will cured in 2 to 3 hours. Note: The time for vacuum-pumping should be less than 3 to 5 mins, otherwise, once the silicone rubber has cross-link reaction during vacuum zing, it will not be operated. FAQ of manual molding silicone rubber: How to prevent silicone manual molds getting sticky? The main reason for this problem is that you do not handle the products or original molds well, and then you should deal with the original mold or products carefully before molding. Such as for the products with a complicated pattern or an unsmoothed surface, you should polish and clean the products after which it will be molded, then spray the release agent. Normally, the release agent can be Vaseline, detergent. Liquid wax Etc. In practical process, you can bush different release agent according to different material. The second reason is that the operator pours the silicone into the mold when the mixture is mixed evenly, then the finish silicone mold will not cure and dry entirely. Place of Origin Guangdong China Brand Name Hong Ye Silicone Rubber Payment & Shipping Terms: Minimum Order Quantity: 200 Kilogram Price: FOB shenzhen USD 4.8~7.5/KG Packaging Details: 25kg/drum and 200kg/drum Delivery Time: within 3 days after payment confirmed in our bank. Payment Terms: L/C,T/T Supply Ability: 8 Ton per Day Certifications:RoHS.MSDS.SGS ISO9001:2000 25kg/drum and 200kg/drum

Applications of manual mold silicone rubber Manual mold silicone rubber is mainly used for model design of manual mold, cement products, low melting point alloy molds, alloy toys, plastic toys, electronics, handicrafts, stationery, large-scale sculpture, reproduction of cultural relic, pad printing allocation, electronic equipment antivibration, and so on. Features of manual mold silicone rubber Manual mold silicone has good elasticity, non-deformation, high temperature resistance, low shrinkage. And it is suitable for manual mold design and small duplication mold production. Faq of manual mold silicone rubber Why is the manual silicone mold oily? The molding silicone rubber itself doesn contain any oil, so it won be oily. If the mold is oily, it may be because you add the compound silicone oil, which contains silicon oil and white oil. For getting further information about our silicone rubber, please feel free to contact with miss shameya. She can speak good arabic and english and chinese for an easier communication with you. 200kg/drum, 25kg/drum

Manual mold silicone rubber applications Manual mold silicone rubber is mainly applicable to manual mold design, PVC plastic molds, cement product molds, melting point alloy molds, alloy toy craftworks, plastic toy craftworks, gifts and stationery, large statues, duplication of cultural relics, shoe sole mold fabrication, pad printing positioning, shock resistance for electronic equipments, etc. Manual mold silicone rubber features description Manual mold silicon rubber features with the resistance to deformation, good tensile strength as well as low shrinkage, and time of reproduction determined on the basis of customers. 1 Good elasticity 2 Non-deformation 3 Heat resistance 4 Low shrinkage Model Codes of Manual Mold Silicone Rubber HY-528 is applicable to make molds of smaller products and the production will be 2-3 pieces. HY-540 compared to other two types, for its moderate hardness and better quality & performance, its production will be 20-30 pieces. HY-57 is applicable to large size products duplications and Electronic equipment antivibration. Manual mold silicone rubber operations Firstly process and prepare the model mold or the product to be duplicated, take certain amount of the silicon rubber, add 2-3% solid curing agent, and mix evenly and they are ready for use. One pair of mold can be solidified and formed in 2-3 hours. (Note: our company does not recommend you to add silicon oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicon oil can be added to soften the mold for easy demolding.) Frequently asked questions for manual mold Silicon rubber 1. What should we do when the air bubbles appeared in the process of mold making ? To handle this situation depends on different cases. Under the condition of an available vacuum pumping machine, mix the silicon rubber and curing agent evenly and then take it to vacuum chamber to deair. If without a vacuum pumping machine, reduce the amount of the curing agent properly. For example, change the mixing ratio of the silicon rubber and the curing agent from former 4% to 1%-2%. In this way, the pre-crosslinking time of silicon rubber will slow down, so the air in the mold will be eliminated gradually to reduce the air bubbles. 2. What should we do when silicone rubber mold didn't cure evenly? The reasons why the phenomenon arises are as follows: incorrect mixing proportion of the silicone rubber and the curing agent due to unqualified weighing; uneven mixing of the silicone rubber and the curing agent, which may cause material wasting , and we should avoid it . 3.What should we do when the silicone rubber stick with the mold? It arises because we didn't handle the model mold (product mold) properly. Before mold making, the model mold has to be sanded and polished, and cleaned carefully concerning the master mold with a coarse surface or to make complex molds. and then brushing a layer of release agent evenly. General release agents include Vaseline, detergent, liquid paraffin, etc. The release agents can be selected according to the different textures of various model molds. 4.What should we do if a silicone rubber mold product deforms? The solution depends on the size of the product. In principle, the size of the product should be in direct proportion to the hardness of the silicone rubber. Regarding small or very fine detailed products, soft silicone with hardness of 10-20 shore A is required for easier demould without damaging the lines of the fine products. Regarding large products, such as products with size above 50 cm, silicone rubber with hardness of 40-50 shore A is required for non-deformation. Regarding large but fine products, silicone rubber with hardness of about 30 shore A can be used for mold making (the method is to brush a layer silicone rubber and then paste a layer of glass fiber cloth and brush another silicone rubber), the outer mold can be made of gypsum, fiberglass reinforced plastics (unsaturated resin plus glass fiber cloth) for preventing the products from deforming. Place of Origin:Guangdong China Brand Name:HY silicone rubber Model Number:HY5 series rubber for manual mold making Minimum Order Quantity:200 Kilogram Packaging Details:25kg/drum and 200kg/drum Delivery Time:within 3 days after payment confirmed in our bank. Payment Terms:L/C,T/T Supply Ability:5 Ton per Day Price: 3.9-5.2usd/kg Certifications: RoHS. MSDS.SGS ISO9000/9001/9004/9011: 2000 25kg/drum and 200kg/drum

Features of Manual molding silicone rubber 1. Good elasticity 2. Non-deformation 3. Heat resistance 4. Low shrinkage Applications of Manual Molding Silicone Rubber: Manual Molding Silicone Rubber is mainly used for model design of manual mold, PVC plastic molds, cement products, low melting point alloy molds, alloy toys, plastic toys, electronics, handicrafts, stationery, large-scale sculpture, reproduction of cultural relic, shoe sole molds, pad printing allocation, Electronic equipment antivibration, etc. Model Codes of Manual Molding Silicone Rubber: HY-528# is applicable to make molds of smaller products and the production will be 2-3 pieces. HY-540#, compared to other two types, for its moderate hardness and better quality & performance, its production will be 20-30 pieces. HY-570# is applicable to large size products duplications and Electronic equipment antivibration. Operation Instructions for Manual Molding Silicone Rubber: RTV-2 Manual Molding Silicone Rubber is a flowable liquid, and the quality has nothing to do with the color. It consists of two component. Part A is a flowable liquid silicone rubber, part B is the curing agent. Firstly, after your previous work of dealing with the original model, take some liquid silicone rubber , add 2%-3% curing agent of the amount of silicon, and mix them evenly. Then after vacuum-pumping the mixture, you can pour it into the mold frame. The silicone mold will cured in 2-3 hours. Note: The time for vacuum-pumping should be less than 3¡ª5 mins ,otherwise, once the silicone rubber has cross-link reaction during vacuumizing, it will not be operated. FAQ of manual molding silicone rubber How to prevent silicone manual molds getting sticky? The main reason for this problem is that you do not handle the products or original molds well, then you should deal with the original mold or products carefully before molding. Such as for the products with a complicated pattern or a unsmoothed surface, you should polish and clean the products after which it will be molded ,then spray the release agent. Normally, the release agent can be Vaseline , detergent. liquid wax Etc. In practical process, you can bush different release agent according to different material. The second reason is that the operator pour the silicone into the mold when the mixture is mixed evenly, then the finish silicone mold will not cure and dry entirely. 25kg/drum and 200kg/drum.

Manual mold silicon rubber. 25kg/drum.

Description of manual mold making: silicone manual mold making silicone is a flowable liquid and it contains two parts. the mixture of manual mold making silicone and curing agent(the catalyst). Applications of manual mold making silicone: manual mold making silicone is mainly applicable to manual mold design, PVC plastic molds, cement product molds, melting point alloy molds, alloy toy craftworks, plastic toy craftworks, gifts and stationery, large statues, duplication of cultural relics, shoe sole mold fabrication, pad printing positioning, shock resistance for electronic equipments, etc. Features of manual mold making silicone: Manual mold silicone has good elasticity, non-deformation, high temperature resistance, low shrinkage. And it is suitable for manual mold design and small duplication mold production Model number: 518 618 628 FOB price : USD5.8~7.8 Port: Shenzhen Min: 100kg Supple ability:4ton/per day. 25kg/drum and 200kg/drum.

Applications of Manual mold making silicone rubber: Manual mold making silicone rubber is mainly applicable to manual mold design, PVC plastic molds, cement product molds, melting point alloy molds, alloy toy craftworks, plastic toy craftworks, gifts and stationery, large statues, duplication of cultural relics, shoe sole mold fabrication, pad printing positioning, shock resistance for electronic equipments, etc. Description of Manual mold making silicone rubber: Manual mold making silicone rubber is flowing liquid with consistant quality in whatever color. It consists of two components, wherein component A is silicone rubber, and component B is curing agent or vulcanizing agent. Firstly process and prepare the model mold or the product to be duplicated, take certain amount of the silicone rubber, add 2-3% solidifying agent, and mix evenly for use. One mold pair can be solidified and formed in 2-3 hours. The formed mold can be used repeatedly without deformation and water shrinkage and with high temperature resistance, thereby providing fast duplication of the product with a product shrinkage 2. The 418 manual mold silicon is mainly applicable to manual molds and small number of product duplication. Operation Instruction of Manual mold making silicone rubber: 1. The Manual mold making silicone rubber is applied to small products or products with fine patterns. The mold for the fine detailed and small products should be made of soft silicon to protect the products from easy breaking when demoulding. 2. If large product duplication or fabrication, the mold should be made of higher hardness silicone rubber so that the products made will not deform. 25kg/drum, 200kg/drum.