We are supply Heavy melting steel. ... ISRI 203 (HMS 2): Wrought iron or steel scrap, black and galvanized, 18 inch (3.175 mm) and larger in thickness. ISRI 204 (HMS 2): Same as ISRI 203 except piecesmust be smaller than 36 in Ã? 18 in (914 mm Ã? 457 mm).
The scrap consists out of a mix of mill scrap (stampings, cuttings, bars, etc.), Industrial scrap (nuts, bolts, misc. pieces, etc), auto and truck frames and bodies, railroad scrap (wheels, axles, parts of locomotives and carriages, etc.), ship scrap (fittings, plate pieces, parts), construction scrap (plate, bars, angle pieces, rods, steel pipe, etc.) and miscellaneous commercial scrap (appliance casings, frames and parts, etc.). Non-Metal impurities total of 1% (one percent), or less.
HMS 1 - ISRI Code 200: Heavy melting steel. Wrought iron and/or steel scrap 1/4 inch or steel scrap
1/4 inch and over in thickness. Individual pieces not over 60 x 24 inches (charging box size) prepared in a manner to insure compact charging.
HMS 1 - ISRI Code 201: Heavy melting steel 3 feet x 18 inches. Wrought iron or steel scrap 1/4 inch over in thickness individual pieces not over 36 inches x 18 inches (charging box size) prepared in a manner to insure compact charging.
HMS 1 - ISRI Code 202: Heavy melting steel 5 feet x 18 inches. Wrought iron or steel scrap 1/4 inch and over in thickness individual pieces not over 60 inches x 18 inches (charging box size) prepared in a manner to insure compact charging.
HMS 2 - ISRI Code 203: Heavy melting steel. Wrought iron or steel scrap, black and galvanized.
1/8 inch and over in thickness, charging box size to include material not suitable as No.1 heavy melting steel. Prepared in a manner to ensure compact charging.
HMS 2 - ISRI Code 204: Same as ISRI 203 but max size 36x18 inches.
HMS 2 - ISRI Code 205: Same as ISRI 204 but free of sheet iron or thin-gauged material.
HMS 2 - ISRI Code 206: Same as ISRI 204, but max size 60 x 18 inches.
The scrap should be free from heavy oxidation, grease, mud, dirt, cast iron, tin, sand, and lead coated materials.
The scrap should be free from non-ferrous materials, excessive rust and corrosions.