It is a cobalt-based alloy that is resistant to wear and corrosion. The first cobalt-based alloy was a cobalt-chromium binary alloy, which was later developed into a cobalt-chromium-tungsten ternary composition, and then later did the cobalt-chromium-molybdenum alloy develop. Cobalt-chromium-molybdenum alloy is a kind of alloy with cobalt as the main component, containing a considerable amount of chromium, molybdenum and a small amount of nickel, carbon and other alloying elements, and occasionally also containing iron.
contact us for more information.
Cobalt-chromium-molybdenum alloy (CoCrMo) is a kind of cobalt-based alloy, and is also a kind of Stellite alloy. It is a cobalt-based alloy that is resistant to wear and corrosion. The first cobalt-based alloy was a cobalt-chromium binary alloy, which was later developed into a cobalt-chromium-tungsten ternary composition, and then later did the cobalt-chromium-molybdenum alloy develop. Cobalt-chromium-molybdenum alloy is a kind of alloy with cobalt as the main component, containing a considerable amount of chromium, molybdenum and a small amount of nickel, carbon and other alloying elements, and occasionally also containing iron. DM FOR MORE IMFO
COBALT CHROMIUM ALLOY ELGILOY :(Composition (Nominal): 40 Co ., 20 Cr., 15 Ni , 7 mo , Fe Balance ;( ELGILOY alloy exhibits high strength, ductility, fatigue life, and good mechanical properties. Corrosion resistant in numerous environments.:(Specifications: ASTM-F1058):(1. Mechanical Property can be improve with Cold Worked & Aged process; (2. Rod forms fully compliance with chemical component; :(3. Annealed possible for wire & Strip ;: (Product availability and request a QUOTE!
1. Product: Cobalt cut cathode 2. Brand: ..... cobalt (given upon interest) 3. Quality: typical assay sent before 4. Quantity: mutually agreed up to 40MT/month, but if less required MOQ 10 mt/m can be agreed. 5. Packing: In original producer's sealed drum on pallets 6. Price: Metal Bulletin Low Grade Low Quotation Monthly Average (M) + 5% 7. Delivery: ex bonded warehouse 8. Payment: Conditional release by T/T payment 9. Shipment: from May to December, 2018
Incoloy 903 is a high-temperature alloy material, also known as Inconel 903, which is a kind of nickel-based alloy. It is mainly composed of nickel, chromium, iron, cobalt, copper, titanium, aluminum and other elements. It has good high temperature strength, creep resistance and corrosion resistance, and is widely used in aerospace, petrochemical, energy and other industries under high temperature and high pressure environments. and other fields. Following are some features and applications of Incoloy 903: characteristic High temperature strength: It has good strength and rigidity at high temperature, and can withstand stress and load under high temperature and high pressure environment; Creep resistance: It can be used for a long time without deformation under high temperature and high pressure environment; Corrosion resistance: good corrosion resistance in strong acid, strong alkali and other corrosive media; Machinability: Incoloy 903 can be machined, forged and welded through a variety of processing techniques. The international standards for Incoloy alloy 903 in various countries are as follows: United States: AMS 5800, AMS 5801, AMS 5802, AMS 5803, AMS 5826, ASTM B166, ASTM B408, UNS N19903 Germany: DIN 17742, DIN 17754, W.Nr. 2.4633 United Kingdom: BS HR 6, BS 3076 Europe: EN 10095 We can provide the following the form:Incoloy alloy903 coil; Incoloy alloy903 strip;Incoloy alloy903 plate; Incoloy alloy903 sheets; Incoloy alloy903 tube; Incoloy alloy903 pipe;Incoloy alloy903 flat; Incoloy alloy903 bar BS:HR 5/JIS:NW4893/UNS:N19903/W.Nr:2.4665 Incoloy 903 has a wide range of applications, mainly used in the following fields: Aerospace industry: components such as aero-engines, aero-bearings, gas turbines, etc.; Petrochemical industry: such as chemical reactors, high pressure vessels, steam generators and other equipment; Energy industry: such as nuclear reactor components, heat exchangers, coal-fired power plant boilers and other equipment; Other fields: such as the manufacture of high-temperature valves, heat treatment furnaces, medical equipment, etc.
Incoloy is a nickel-chromium-iron alloy, which is a nickel-iron-chromium iron-nickel-based corrosion-resistant alloy designed for anti-oxidation and carbonization when the temperature rises. This alloy is used in high-temperature water vapor, including steam-air-CO2 In mixed gas, it has good corrosion resistance. In some high-temperature and high-pressure water media, its stress corrosion resistance is significantly better than 18-8 stainless steel and Inconel600; it also has good corrosion resistance in H2+H2S media. In the alkaline medium containing NaOH, its stress corrosion resistance is better than high-nickel alloys such as Inconel600.
Haynes 188 is a high-temperature, high-strength, and high-corrosion-resistant superalloy developed and produced by Haynes International in the United States. It is typically used in high-temperature, high-pressure, and corrosive environments. Haynes 188 alloy is renowned for its outstanding high-temperature strength and excellent corrosion resistance. The main components of Haynes 188 alloy include nickel, chromium, molybdenum, iron, titanium, aluminum, and tantalum. The combination of these elements gives Haynes 188 extremely high heat resistance and corrosion resistance. It can be used at temperatures as high as 1095 and has excellent oxidation and thermal corrosion resistance. Additionally, Haynes 188 has good machinability, weldability, and castability, making it suitable for manufacturing components of various shapes and sizes. The following are the international standards for Haynes 188 alloy: United States: AMS 5608, AMS 5772, AMS 5801, AMS 5796, AMS 5797, AMS 5800, AMS 5879, AMS 6925, AMS 5803, AMS 5596, AMS 5708, AMS 5804, AMS 5806, AMS 5799, AMS 5836, AMS 5875, AMS 5954, ASTM B574, ASTM B574M, ASTM B435, ASTM B582, UNS R30188 Europe: EN 2.4683, EN 2.4684, EN 2.4694 Germany: DIN 17743 France: AFNOR Z 20 CNDT 35.20, AIR 9165 United Kingdom: BS HR 203, BS HR 504, BS HR 505 Japan: JIS NW 5886 We can provide the following the form:Haynes 188 coil; Haynes 188 strip;Haynes 188 plate; Haynes 188 sheets; Haynes 188 tube; Haynes 188 pipe;Haynes 188 flat; Haynes 188 bar GB:GH5188/JIS:NW 6190/UNS:R30188/W.Nr:2.4683 Haynes 188 is primarily used in aerospace, petrochemical, chemical, energy, and marine fields. In aerospace, Haynes 188 is commonly used to manufacture components such as turbine blades, combustors, and nozzles in turbine engines. In petrochemical, chemical, and energy fields, Haynes 188 is often used to manufacture petrochemical reactors, catalyst carriers, high-temperature pipelines, corrosion-resistant coatings, and oil extraction equipment. In the marine industry, Haynes 188 is commonly used to manufacture components in marine environments such as propellers and bearings. Overall, Haynes 188 alloy has excellent high-temperature, high-strength, and high-corrosion resistance properties and is widely used in various industrial fields. It is an important superalloy material.
Haynes 242 is a nickel-chromium-molybdenum alloy with excellent high-temperature strength, good oxidation resistance, and resistance to hot corrosion and thermal fatigue. It is typically used in gas turbine engine components, such as turbine blades, vanes, and combustor liners, as well as in industrial furnace applications. Haynes 242 offers excellent high-temperature strength, with a minimum yield strength of 880 MPa and a minimum tensile strength of 1100 MPa. It also has good ductility, with a minimum elongation of 12%. In addition, it has good thermal stability and resistance to thermal fatigue, making it suitable for use in high-temperature applications. Haynes 242 also has good resistance to oxidation and hot corrosion, which makes it suitable for use in gas turbine engine components that are exposed to high-temperature and corrosive environments. It has a maximum HB hardness of 300 and excellent fatigue strength at high temperatures. Haynes 242 is typically available in the form of sheet, plate, bar, and wire. It can be machined using conventional methods and is weldable using standard welding techniques. Overall, Haynes 242 is a high-strength, high-temperature alloy with excellent resistance to oxidation and hot corrosion, making it ideal for use in gas turbine engine components and industrial furnace applications. Here are the national standards for Haynes 242 alloy: United States: AMS 5708, AMS 5776, AMS 5777, AMS 5853, AMS 5854, AMS 5857, AMS 5858, AMS 5895, AMS 5896, AMS 5897, AMS 5898, AMS 5965, AMS 5966, AMS 5967, AMS 5968, AMS 5969, AMS 5970, AMS 5971, AMS 5972, AMS 5973, AMS 5974, AMS 5975, AMS 5976, AMS 5977, AMS 5978, AMS 5979, AMS 5980, AMS 5981, ASTM B435, ASTM B572, UNS R30556 Europe: EN 2.4683 Germany: DIN 17743, VdTÃ??V 435 United Kingdom: BS HR 202, BS HR 501, BS HR 502 Japan: JIS NW 6242 We can provide the following the form:Haynes 242 coil; Haynes242 strip;Haynes 242 plate; Haynes 242 sheets; Haynes 242 tube; Haynes 242 pipe;Haynes 242 flat; Haynes 242 bar GB/JIS:NW 625/UNS:N10242/W.Nr:2.4683 Haynes 242 is typically used in gas turbine engine components, such as turbine blades, vanes, and combustor liners. It is also used in industrial furnace applications, including muffles, retorts, and heat treating fixtures. The high-temperature strength and excellent resistance to oxidation and hot corrosion make Haynes 242 an ideal material for use in high-temperature and corrosive environments. It is commonly used in aerospace, power generation, and industrial applications where high-temperature and corrosive conditions are present.
Inconel nickel alloy It is a solid-solution strengthened nickel-based deformed superalloy with molybdenum and niobium as the main strengthening elements. It has excellent corrosion resistance and oxidation resistance. It has good tensile properties and fatigue properties from low temperature to 980 �° C, and is resistant to salt spray. Stress corrosion in atmosphere. Therefore, it can be widely used in the manufacture of aero-engine parts, aerospace structural parts and chemical equipment. The alloy has good processing and welding properties, and can supply a variety of plates, bars, pipes, wires, strips and forgings
Elgiloy alloy property data sheet - product availability and request a QUOTE! :(Composition (Nominal): 40cobalt-20chromium-16iron-15nickel-7molybdenum ;( Elgiloy® alloy exhibits high strength, ductility, fatigue life, and good mechanical properties. Corrosion resistant in numerous environments.:(Specifications: ASTM-F1058):(1. Mechanical Property can be improve with Cold Worked & Aged process; (2. Rod forms fully compliance with chemical component; :(3. Annealed possible for wire & Strip