Application The FSR-01 Shrink Force and Ratio Tester serves the purpose of measuring both the shrinking forces and shrinkage ratio of heat shrinkable films. These films are typically created through extrusion and stretching (hot drawing) during their manufacturing process, retaining this stretched state even after cooling.
When the heat shrinkable film is reheated to the temperature at which the initial stress was introduced and subsequently fixed during its production, this stress is released, causing the film to contract or "shrink back." Depending on the specific manufacturing treatment applied, the film can be categorized as either biaxially oriented (stretched in two directions) or uniaxially oriented (stretched in one direction).
Test Process
1. A well-insulated air oven is heated to the set temperature. The two samples are placed separately on two test stations, for shrinkage rate and shrink/contraction force testing.
2. A temperature probe is located to measuring area, to give result as reference temp. The air oven is driven down automatically to cover the sample area. The force and shrink rate are to be measured and the shrinkage temperature is reached when the maximum shrinking force is attained.
3. When this force has decreased by around 15%~30%, the air oven is lifted and time is recorded.
4. The assessment of shrinkage ratio is performed at the mean time.
Technical Features
1. PLC Control and HMI Touch Screen: ensuring industrial-level stability.
2. Well-Insulated Air Oven: The air oven is excellently insulated and capable of automatic lowering and lifting, enhancing the precision of the testing.
3. Non-Contact Shrink Ratio Measurement: accomplished through a noncontact method, improving accuracy and reliability.
4. Real-Time Display:including shrinking force, contracting force, and shrinkage ratio, allowing for immediate analysis and monitoring.
5. Elimination of Interference Factors: Irrelevant interference factors like friction and cool air are effectively eliminated, ensuring the accuracy of the results.
6. Stable Heating System: The heating system is stable and well-balanced, maintaining consistent and controlled test conditions.
7. Easy Sample Loading: Sample loading is made easy, streamlining the testing process and reducing setup time.
8. High-Resolution Sensors: The system is equipped with high-resolution force transducers and thermometers, guaranteeing precise measurements.
9. Connectivity and Software:(optional) It includes an RS232 port for data connectivity and offers optional professional software for advanced data analysis and reporting capabilities.
Standards: ISO 14616, DIN 53369
Main Parameters
Force Range 5 N ( or as required)
Accuracy ±0.5%
Resolution 0.001N
Displacement Range 0.1 ~ 95 mm
Accuracy ±0.1 mm
Temperature Range Ambient ~ 210C
Accuracy ±0.5C
No. of Specimens 2
Sample size 110*15 mm, L*W
Power Supply 220V 50Hz
We are glad to propose 500 MT of stain less steel mill scale. Mill scale is formed on the outer surfaces during by the hot rolling lamination of stainless-steel products. At a visual inspection the material is a hard brittle sand and is mainly composed of iron oxides, mostly ferric, and is bluish black in colour, but it also contains considerable alloying elements such as chromium and nickel. The recovery ratio after melting in furnace for the most valuable alloy elements is: - Ni: 3.5 - 4.5% - Cr: 6-8% From the chemical and physical analysis performed on the scrap, and according to the European environmental rules, the material has been classified as a special non dangerous waste, listed in green list. In particular the mill scale can be classified as follows: Waste code: 10 02 10 The material is stored on cemented flooring, and it can be loaded loose in tipper trucks or containers. Chemical analysis of the material is available on request.
Commodity: Synthetic Cryolite Formula: Na3AlF6 M.W.: 209.95 Properties: The product is a white crystalline powder or a sandy-size granularity, and a pinkish crystalline powder or a sandy-size granularity as well. Sp.gr.2.953.01g/cm3, melting point about 1000centigrade, specific heat 1.056j/gcentigradeat 18100centigrade. Its slightly soluble in water, but insoluble in anhydrous hydrogen fluoride. The content of its crystal water will be decreased while the increasing of the molecular ratio, therefore its loss on ignition will be also decreased while the increasing of the molecular ratio. After the paste of synthetic cryolite with different molecular ratio dehydrates, the loss on ignition at 800centigrade will appear 10.34%, 6.22% and 2.56% when the molecular ratio reaches 1.74, 2.14 and 2.63 reactively. Specifications: Appearance white powder F 52% min Al 12% min Na 33% max SiO2 0.36% max Fe2O3 0.08% max CaO 0.5% max P2O5 0.03% max SO4 0.6% max H2O 0.4% max Loss on ignition 2 % max Uses: Its mainly used as a flux in the aluminum smelting by fused-salt electrolysis; also an opalizer in the manufacture of enamel; an opacifier and auxiliary solvent of glass and enamel; an insecticide of crops; a flux in aluminum alloy casting; and in the production of ferrous alloy and effervescing steel; as well as a wear-resistant filler for resin and rubber-boned abrasive wheels. Packing & Storage: In plastic coating woven bags with plastic film inside, 25kg,40kgs, 50kgs or 1000kgs net each, or as the requirement of clients.Stored: in a cool , ventilated, dry place.
Product Name:Aluminium sulphate Molecular Formula:AL2(SO4)3 Hs Code: 2833220000 CAS Code:10043-01-3 Standard:HG2225-2010 Shape:flake, powder, 2-4cm lump and 2-5mm/3-8mm granular Properties:There are two types,anhydrous aluminium sulphate and aluminium sulphate octadecahydrate. In normal condition , it is AL2(SO4)3 18H2O; AL2(SO4)3 14H2O after efflorescence, can be white powder , glittering flaky or crystalline flakes, odorless, sweet to slight bitter. Use:Sewage Treatment, treatment of drinking water, Sizing of paper , Cement Additive. Specifications Item Name Standard AL2O3 15.6% 16.5% 17% Fe2O3 ¤0.5 % 0.005 % 0.004% PH value .0 3.0 3.0 Water insoluble matter 0.2% 0.04% 0.03% Packing 25kg or 50kg or 1000kg in plastic lined woven bag
Product Features The purity of the product, calcium and phosphorus ratio appropriate to ensure a higher degree of its biological effects. Phosphorus content greater than 21% of the products, their biological effects better. This unique high-tech companies use technology to make our products crystallization, high purity. Drying process advanced products, products with low free water under the premise that the product does not lose crystallization of water, avoid the product in the drying process for the loss of water caused by crystallization of biological effects of the reduction. coarse particles MDCP in the animals stay in the stomach longer and more conducive to the absorption of calcium phosphate, the product produced by micro-particles MDCP form, without any chemical binder. Specifications Appearance white powder or granule Phosphate  21% min Calcium     15% min Fluorine    0.18% max Arsenic    30ppm max Pb   30ppm max Source of OriginRock Packing and Storage Knitted bags lined polyethylene plastic bags double packaging, Weighing 25Kg. Transportation-and harsh rain. Stored in a cool, ventilated, dry place.
Monocalcium Phosphate (MCP) Feed grade Product Features The purity of the product, calcium and phosphorus ratio appropriate to ensure a higher degree of its biological effects. Phosphorus content greater than 22% of the products, their biological effects better. This unique high-tech companies use technology to make our products crystallization, high purity and its harmful impurities significantly below standards:HG28611997 Drying process advanced products, products with low free water under the premise that the product does not lose crystallization of water, avoid the product in the drying process for the loss of water caused by crystallization of biological effects of the reduction. Specifications Appearance white powder or granule Total P 22%min Ca 13-18% F 0.18% max As 10 ppm max Pb 10ppm max Moisture 4%max Source of OriginRock Packing and Storage Knitted bags lined polyethylene plastic bags double packaging, Weighing 25Kg. Transportation-and harsh rain. Stored in a cool, ventilated, dry place
Commodity: Calcium chloride Molecular formula CaCl2 H.S code 28272000 Product feature Calcium chloride is an inorganic salt, which exists as solid or liquid. Solid calcium chloride is a white, crystal substance in the form of flake, granule, pellet or powder. With different crystallized water contents, it can be dihydrate or anhydrous. Liquid calcium chloride is a colorless, clear solution. As calcium chloride has such properties as quick dissolving, exothermic ability, attracting moisture from the air and surroundings, dissolving at very low temperature, Specifications: Analysis Item Standard Calcium chloride (CaCl2) 74%min,77% min,94%min Total Chlorinated Alkali: (NaCl) 5.0%max Magnesium Chloride(MgCl2) 0.5%max Insoluble matter in water 0.25%max Calcium Sulfate (CaSO4): 0.2%max Ferric Oxide (Fe2O3) 0.025%max Heavy Metal as Cu., Pb., Cd., Cr., Hg., As 0.005%max Application Mainly used in drying, melting snow for airport express and street, concrete desiccant and concreting fast, removing dust and oil industry. Exporting Packing :Plastic woven bag with PE ,25kg/50kg/1000kgs net weight or 25kg x 40 bags into one big bag or 40 bags on a pallet with shrink-wrapped Means of transportation :in containers or by bulk vessel with large quantity
Commodity: Dicalcium phosphate Feed Grade Use DCP is the feed preparation of raw materials, Animal right to supplement calcium needs. Coarse its products more applicable to the preparation hens, ducks feed, concentrate feed and premix. Product Nature Molecular Formula:CaHPO4·2H2O,Molecular weight:172.09,After drying with loose white powdery crystals or granules. Neutral products, the melting acid, water-soluble, hygroscopicity small, heated to 90 around gradually lose water of crystallization. Product Features The purity of the product, calcium and phosphorus ratio appropriate to ensure a higher degree of its biological effects. Phosphorus content greater than 18% of the products, due to a small amount of MCP, and its biological effects better. This unique high-tech companies use technology to make our products crystallization, high purity and its harmful impurities significantly below standards:HG26362000 Drying process advanced products, products with low free water under the premise that the product does not lose crystallization of water, avoid the product in the drying process for the loss of water caused by crystallization of biological effects of the reduction. Coarse particle DCP in the animals stay in the stomach longer and more conducive to the absorption of calcium phosphate, the product of Micro-particle DCP granulation from mechanical, without any chemical binder. Specifications Appearance white and gray powder/granule Total P 18% min Calcium 21% min F 0.18% max As 30 ppm max Pb 30 ppm max Packing and Storage Knitted bags lined polyethylene plastic bags double packaging, Weighing 25Kg/50KG/1000Kg. Transportation-and harsh rain. Stored in a cool, ventilated, dry place.
pellet machine, with the advantages of low noise, easy and stable operation, high automation, can make pellet dia size from 6mm to 12 mm and the output capacity from 1.5t/h to 2.5t/h. We can offer you the complete solution for making pellets, from crushing, drying to pelletizing. Features : 1. This machine adopts gear first stage driving system, with ideal drive ratio and enormous driving force, its transmission us stable with low noise, operate simply, no blocking is happened to the machine easily. 2. The maximize design if pinch roller can lower the requirement to moisture content of materials in particle molding. 3. The motor and gear cases are installed at the heavy pedestal, pin coupling is used to realize direct connecting, which can exempt from foundation installation and easy to repair and maintain. 4. The machine is equipped with patented water circulation; the cooling system can be used to control the temperature rising of each part efficiently, to guarantee the continuous, stable, reliable running of the machines. 5. The machine adopts advanced variable frequency motor to feed, which equipped with overload intelligent protection.
THF is an important organic synthetic raw material and a solvent with excellent performance. It is especially suitable for dissolving PVC, polyvinylidene chloride and butyl aniline. It is widely used as a solvent for surface coatings, anticorrosive coatings, printing inks, tape and film coatings, and used in combination. As a reaction solvent, the thickness and brightness of the aluminum layer can be arbitrarily controlled when used in the aluminum electroplating solution. THF itself can be polycondensed (ring-opening and repolymerization initiated by cations) into polytetramethylene ether glycol (PTMEG), also known as tetrahydrofuran homopolyether. PTMEG and toluene diisocyanate (TDI) are made into special rubbers with abrasion resistance, oil resistance, good low temperature performance and high strength; with dimethyl terephthalate and 1,4-butanediol to make block polyether polyester elastic Material.