Item AL-1 AL-2 AL-3 AL-4
Al2O3(%min) 75 65 55 48
Fe2O3(%max) 0.7 1.0 1.0 1.8
R.U.L 0.2mpa 1520 1500 1470 1420
Refractoriness 1790 1790 1770 1750
A?P 22 22 21 21
C?C?S Mpa 53.9 49 44.1 39.2
The Al2O3 content is more than 55%, and is calcined from a high-content alumina raw material such as a silicone raw material or a bauxite. High heat resistance and high temperature resistance at 1770 C and above. Has good slag resistance, mainly used in the masonry of steelmaking electric furnace, glass furnace, cement rotary furnace and so on. Characteristics of High Alumina Brick Price: 1.Refractoriness: More refractory than refractory clay bricks and semi-silica bricks, up to 1750-1790C, belonging to high-grade refractory materials. 2. Load softening temperature: Since the high aluminum has a high Al2O3 content, a low impurity content, and a low formation of the molten glass body, the fire-resistant softening temperature is higher than that of the refractory clay brick. However, since the mullite crystal has not yet formed a network structure, the load softening temperature is lower than the load softening temperature of the silica brick. 3. Slag resistance: High Al2O3 has high Al2O3 content, close to neutral refractory material, and can resist the erosion of acid slag and alkali slag. Because it contains SiO2, the resistance to alkali slag is less than acid resistance.
Product Description: We are a trusted name in manufacturing fire bricks which are a block of ceramic material used in masonry construction. These are sized to be layered with one hand using mortar. Our fire bricks are made from fire clay which is widely used as refractory insulating bricks to maintain insistent temperature. Thee bricks are extensively used in lining furnaces, kilns, fireboxes, and fireplaces.
As per standards. Loose & Pallets
Our company located in yangquan city, shanxi province, china, and yanquan city is one of the Largest refractory material base in china. We are in position to supply various kinds of Refractory bricks, such as high alumina and fireclay bricks, insulating bricks etc With the catalogue as follows: 1. Fireclay brick 2. High alumina brick 3. Insulating brick 4. Unsintered phosphate brick 5. Al-c sliding plate 6. Nozzle 7. Hollowwares 8. Refractory mortar 9. Refractory castables 10.Other refractory material.
For hot blast stoveFor eaf roofFor general use Goods no.Ghha65,Ghha55,Ghha48,Rhs,Rh1,Rh2Al,75Al-1Al-2 Al2o3(%) min655548807565756555 Refractoriness( ) min179017701750185018001790179017901770 Refractriness under load 0.2 mpa( )150014701420155015301520152015001470 Apparent porosity (%) max_191922232322 Ccs (mpa)min4944.139.278.568.658.8544944.1 Shrinkage after reheating 1500x2h (%) max+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4.
High Alumina Bricks for general uses are made from bauxite of super quality, bonding chamotte and additives. It is noted for good erosion resistance high refractorinessthermal shock resistance and accurate dimension. They were widely accepted in various kilns ,thermal equipment of metallurgy, petroleum, chemical industrysuch as high aluminum bricks for blast furnaces steel ladle and electrical furnace and so on .
High alumina bricks
Physical properties Brand SK-32 SK-34 SK-35 SK-36 SK-38 Index Refractoriness íµ 1730 1750 1770 1770 1790 bulk density g/cm3 2.15 2.2 2.3 2.35 2.52 Apparent porosity ¿Q% 24 24 23 23 23 Cold crushing strength ¿RMpa 30 35 40 45 65 Refractoriness under load (0.2MP) íµ 1350 1350 1400 1450 1550 Permanet liner change 1500íµ 2hrs% +0.2to-0.2 +0.2to-0.2 +0.1to-0.4 +0.1to-0.4 +0.1to-0.4 Thermal expansion at 1000 íµ 0.5 0.5 0.5 0.5 0.5 Fe3O4% 1.96 1.93 1.9 1.87 2 Al2O3% ¿R 42 48 55 60 65 SiO2 48-50 46-48 41-44 37-40 27-30
Al2O3: 42-99% refractoriness min 1790 bulk density: 2.1-3.0 apparent porosity: 24-17%
High alumina bricks are commonly utilized in industries such as steelmaking, cement manufacturing, and non-ferrous metallurgy for lining furnaces, kilns, and other high-temperature equipment due to their excellent resistance to thermal shock, abrasion, and chemical corrosion.