Detailed Product Description
Chemical Analysis Norm Fact
Selica (SIO2) 20,840
Aluminia (AI2O3) 4,460
Ferric Oxide (FE2O3) 4,130
Lime (CaO) 65,210
Magnesia (MgO) 4,0 0,780
Sulphic Anhydrid (SO3) 2,640
Mass part of Chloride 0,1 0,003
Insolube Residue 1,5 0,160
Looses on Ignition 3,0 0,650
Calcium Oxide (K2O) 0,690
Natrium Oxide (Na2O) 0,400
Tri-Calciu Aluminate 4,800
Product Origin: UKRAINE
Payment Terms: L/C
Payment Remarks: Irrevocable, Transferable, Divisible, Auto-revolving Documentary LC, payable 100% at sight
Supply Ability: 5,000,000 MT
Minimum Order: 150,000 MT
Delivery Lead Time: 45
Inner Packing: In bags of 50kg with markings in Standard English
Certification(s): SGS
50 kg und big bags (1.000kg & 1.500kg) or bulk or at buyers option Delivery terms : fifteen (35) days to forty five (45) days following sellerÆs receipt lc From buyer or from reseller in shipments of 12500/ 25.000 /50000 Mt per vessel / United states astm c-150, british bs 12/1996, european en-197 1/2000 Or russian m-400 or m-500. Chemical composition Silicon dioxide (sio2) 21.00 Aluminium trioxide (al2o3) 5.50 Ferric oxide (fe2o3) 3.30 Calcium oxide (cao) 65.60 Magnesium oxide (mgo) 1.40 Sulphate (so3) 2.70 Loss on ignition (loi ) 1.40 Dicalcium silicate (c2s) 15.00 Tricalcium silicate (c3s) 60.00 Tricalcium aluminate (c3a) 8.05 Tricalcium alumino ferric (c4af) 9.76 Physical and mechanical properties Fineness by blain cm/g 3250 Autoclave expansion 0.02 Initial setting time (vicat) 105 minutes Final setting time (vicat) 135 minutes Compressive strength 03 day's 230 kg/cm2 Compressive strength 07 days 305 kg/cm2 Compressive strength 28 day's 420 kg/cm2 Product packing : 50 kg und big bags (1.000kg & 1.500kg) or bulk or at buyers option
Aluminum oxide Alumina powder for Electric vacuum tube shell ceramic Al2O3 item value Classification ALUMINA CAS No. 1344-28-1 Other Names Alumina MF Al2O3 EINECS No. 215-691-6 Grade Standard Electron Grade, Industrial Grade, Reagent Grade Purity 99.5% Appearance White powder Application electronic ceramics Color White Grade Industrail Grade Density 3.5 g/cm3 Melting point 2054 Boiling Point 2980 Molecular Weight 101.96 Shape Ionische Water Solubility Hard Packing 25 Kg Pp Bag or plastic barrel Sample Availiable
Since ancient times, people have used hydrated lime to build houses and high buildings. Today, the massive architectural works and high-rise buildings are constructed more and more. Why appear firm architectural construction? That is cement â??important hydraulic binder in building process, helping to link projects together, forming a solid mass. With modern advanced machines and science, abundant human resources. Portland cement is the most common type of cement in general use around the world, used as a basic ingredient of concrete, mortar, stucco, and most non-specialty grout. It is a fine powder produced by heating materials in a kiln to form what is called clinker, grinding the clinker, and adding small amounts of other materials. Several types of Portland cement are available with the most common being called ordinary Portland cement (OPC) which is grey in color, but a white Portland cement is also available.
Supplier: Portland cement 32, 5 r/n, portland cement 42, 5 r/n portland cement 52, 5 r/n
Cement is a crucial building material used in construction to bind other materials together. It is a powder made from a mixture of materials, such as limestone, clay, shells, silica, and iron ore There are several types of cement, each with its own specific properties and uses. The most common types include like portland 32.5/42.5/52.5
Portland cement Portland cement: 42, 5 n/r type i & ii din en 197 1/2000 or bss 12/1996 or astm c 50 kg or in 1.5 tn bags
we are wholesale of Portland cement contact us for wholesales price .
PORTLAND CEMENT TYPE I/II Low Alkali ASTM C150 Mill sheet will be provided upon request. 52.5 and 42.5 Monthly capacity: 52.5 - 150000.0 MTs 42.5 - 500000.0 MTs
325 425 525 Portland cement Specification Sulfate Resistant Portland Cement SRPC also named Sulfate Resistant Cement SRC is one of hydraulic binding materials can resistance to sulfate ion attack Type High Sulfate Resistant Cement PHSR and Moderate Sulfate Resistant Cement PMSR Grade 325 425 Application To make concrete of sulfate resistance marine concrete maritime works To make cement boards precast cement products cement pipes precast concrete pile shop fabricated members Sea water attack resistance projects for example sea wall dam mariculture project sea water desalination project oceanarium etc Chemical resistant engineering concrete To make sulfate resistant concrete engineering of harbor water conservancy underground tunnel drainage pipe diversion works road and bridge foundation etc