SiO2 - 56.15%; AL2O3 - 35.42%;
+400 um - 0,7%
+250 um - 12,5%
+200 um - 9,7%
+160 um - 28%
+100 um - 34%
-100 um - 15,1%
Cenospheres (aluminosilicate microspheres) are hollow aluminosilicate glass ceramic beads ranging in size from 400-500 microns 20-50mkm (most often from 100 to 250 microns), which are formed during high-temperature combustion of pulverized coal. The chemical composition of the main component of the cenospheres is silicon oxide SiO2 (45-60%), aluminium oxide Al2O3 (15-40%), iron oxide Fe2O3 (1.0-10%), calcium oxide CaO (1.5- 4.5%), potassium oxide K2O (2.0-4.5%) and other certain oxides that make up the balance of the content are typically less than 1.0%. Due to the unique set of physical and chemical characteristics of the cenospheres, they are used in the manufacturing of various composite materials. They are used in solving technical issues that require: reduction in the weight material with a low thermal conductivity, high strength, volume efficiency, increased resistance to erosion and aggressive environments.
Physical & Chemical Properities "1. Cost reduction; 2. Weight reduction; 3. Non-combustible; 4. Thermal insulation; 5. Sound absorption; 6. Good Fluidity; 7. High thermal stability; 8. Low density; 9. High particle strength 10. Low water absorption 11. Stable property " Application 1. Spherical particle, surface vitrified, good fluidity while mixing, good workability, mixed evenly shortly, then reduce the aggregate broke when dry-wet mixing, good thermal property and mechanical property. 2. Can be used in a wide variety of paint and coating systems to reduce VOCs, improve flow and leveling characteristics, and enhance chemical and wear resistance properties. 3. Low water absorption, easily controlled in mortar, low shrinkage, no hollowing and cracking, stable thermal property and mechanical property, increase the mortar service life. 4. Can used in boards and panels for both commercial and residential interiors.The boards are comfortable to handle and easy to cut and fasten like wood.
Physical & Chemical Properities "1. Cost reduction; 2. Weight reduction; 3. Non-combustible; 4. Thermal insulation; 5. Sound absorption; 6. Good Fluidity; 7. High thermal stability; 8. Low density; 9. High particle strength 10. Low water absorption 11. Stable property " Application 1. Spherical particle, surface vitrified, good fluidity while mixing, good workability, mixed evenly shortly, then reduce the aggregate broke when dry-wet mixing, good thermal property and mechanical property. 2. Can be used in a wide variety of paint and coating systems to reduce VOCs, improve flow and leveling characteristics, and enhance chemical and wear resistance properties. 3. Low water absorption, easily controlled in mortar, low shrinkage, no hollowing and cracking, stable thermal property and mechanical property, increase the mortar service life. 4. Can used in boards and panels for both commercial and residential interiors.The boards are comfortable to handle and easy to cut and fasten like wood.
Grade: S40W/D, S60W/D, S80W/D The solid content of wet type marked with W is about 15%. Product Description: Expanded microsphere is a kind of hollow spherical plastic particles. The products can be use as light fillers because of low density. It made by expandable microsphere with Sinnos proprietary technology. Application: Leather repair, automotive repair of atomic dust, unsaturated polyester, epoxy casting and printing ink.
Oil and gas industry: Accelerating the process and improving the efficiency of well drilling; increasing the life of drilling equipment; drilling fluids and plug cements of low density and high strength. Construction: ultralight and ultra-lightweight concrete; high-strength and low-density thermal and acoustic insulation boards; increased adhesion of concrete or brick walls, excellent leveler. dry mortars, lime and liquid mortars, cements, plaster, insulating roof coatings and soundproofing materials - lightweight, smooth surface, low cost, heat resistant, shrinkage resistant. sensitizer for the use of emulsion BBs. paints - resistance to chemical corrosion and light, thermal insulation, smoothness. Styrofoam: Aircraft, spacecraft, ship construction - low density and moisture absorption, high mechanical properties of materials for vibration damping, insulation and thermal protection. Ceramics: Refractory materials and coatings, insulation materials. Plastics Epoxy resins: production of polyethylene - improving strength and abrasion resistance. production of bearings, cameras, furniture and its accessories - tensile strength, impact strength, hardness, resistance to heat and light. Profiled materials, pipes, plates - dimensional stability, rigidity, heat resistance; TV housings, auto parts - compressive strength, bending elasticity, shrinkage reduction.
Microsphere aluminosilicate / cenosphere SiO2. 58.4% Al2O3. 36.5% Fe2O3 1.8% Density 0.8% Moisture 0.1% Colour Grey Form sphere Bulk density 400kg/m3 Annual quantity 3000 MT
Our company produces and sells dry cenosphere(microspheres) in Europe and England. We sell the following fractions of cenospheres: 100um,160um,180um,300um,500um.\Our cenosphere contains the chemical composition: Control parameters Measurement Bulk density g/cm3 0,300 â?? 0,450 Specific gravity g/cm3 0,5 0,8 Floating rate % > 95 Melting point oC 1000 - 1300 Moisture content %
Supplier: Microspheres
Supplier: Cenosphere, talc powder, wollastonite powder, fly ash, silica fume, silicon powder