Material: High Density Polyethylene.
Origin: Saudi Arabia.
Source: Petrochemical Industry.
Grade: Injection Molding.
Color: Natural.
Packing: 750-850 KG Jumo Bags.
Loading Port: Jeddah Saudi Arabia.
Payment Terms: TT basis for less than 100 TONS order.
LC basis for minimum 100 Tons order.
Please contact for price and more details.
Item Test Condition Test Method Value Unit MFR 190 C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C
HDPE (High Density Poly Ethylene) Origin: Petrochemical Plant Grade: Blown Film Grade Shape: Granules Loading Port: Jeddah, Saudi Arabia
Item Test Condition Test Method Value Unit MFR 190°C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 °C
Granule LDPE/HDPE virgin granules for General Purpose Injection Molding Features · Good Process Ability, High Stiffness, Homopolymer. ASTM and ISO Properties Properties Unit ASTM Test Density 0.900 g/cm³ D1505 MI (230 ºC/2.16 kg) 14 g/10min D1238 Tensile Strength @ Yield 35.3 MPa D638 Elongation @ Yield 10 % D638 Flexural Modulus 1720 MPa D790B Notched Izod Impact Strength @ 230 ºC 25.5 J/m D256A Heat Deflection Temperature @ 4.6 kg/cm² 99 ºC D648 Rockwell Hardness (R-Scale) 97 D785A Water Absorption after 24 hours 0.020 % D570 Fabrication · Equipment Raw or Screw Injection Machine · Techniques Standard Processing Advantages · Good Process Ability · High Stiffness · Good Heat Deflection Temperature · Microwaveable for Food Reheating Purposes Applications · Closures · Containers · Housewares · Medical / Healthcare Applications · Toys · Writing Instruments
Application Hdpe injection-molding grade is used for making reusable containers, such as beer cases, beverage cases, food cases, Vegetable cases and egg cases and can also be used for making plastic trays, goods containers, home appliances, daily goods use and thin-wall food containers. It can also be used in the production of industrial-use barrels, garbage bins and toys. Through the extrusion and compression molding process and injection molding, it can be used to produce the caps of purified water, mineral water, tea beverage and juice beverage bottles. 25kg/bag, 18mt/20fcl.
MATERIAL : Hdpe injection molding pellet CATEGORY :HDPE TYPE :Pellet GRADE :Black and Grey SPECIFICATION :"2 to 5 mfi Black will be loaded in a different bag and grey will be loaded in a sep bag" ORIGIN : NZ LOADING WEIGHT : 23 FAS (USD/Ton) : $670-870
(HDPE) Polyethylene Injection Red granules (HDPE) Polyethylene Injection Green granules (HDPE) Polyethylene Injection Black granules (HDPE) Polyethylene Injection Black Regrind (HDPE) Polyethylene Injection Blue granules.
Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %
Specification: Virgin. Type: Film grade, Injection molding grade, Blowing molding grade, extrusion grade,