G9-power Cast Iron Non Machinable SIZE - 2,5 X 350 MM, 3.5 X 350 MM, 4X 450 MM ELEMENTS C % Mn% Si % S % P % Cr% Ni% Mo% Cu% Fe% 0.100 0.48 0.030 0.030 0.030 * * * * Bal Joining and repair of cast iron parts, repair of defective castings, joining cast iron to mild steel etc. Weld joints are non machinable. G9-POWER CAST IRON MACHINABLE FE-NI-(E NI FE CL) (NICKEL 55) SIZE - 3.5 X 350, 4X 450 ELEMENTS C % Mn% Si % S % P % Cr% Ni% Mo% Cu% Fe% 0.150 0.52 0.26 0.029 0.030 * 55 * 2.5 Bal Popular and versatile NiFe-Cl type cast iron welding rod for high strength, hot or cold welding of; cast iron to itself (incl. grey / malleable, nodular, SG & austenitic cast irons) and cast iron to steel. Machineable weld deposit. Extremely soft, smooth arc with low spatter. Weld metal is stronger and more resistant to solidification cracking than the pure nickel electrode types (such as Ni-Cl). Classification: AWS ENiFe-CL. Available in blister/handy packs & 1kg re-usable packs, in 3.2mm. G9-POWER CAST IRON MACHINABLE(E NI CL)(NICKEL 99) For fabricating cast iron machine components, rebuilding worn out surfaces and heavy castings. ENiCI Nickel 99 welding electrode is designed for welding gray iron castings to themselves as well as joining them to mild or stainless steels. It is also used to repair castings. With the high nickel content, the welds are easily machined. A Preheat and interpass temperature of not less than 350â?°F is recommended during welding. ELEMENTS C % Mn% Si % S % Cr% Ni% Mo% Cu% Fe% 2.00 2.50 4.00 0.03 * 85 * 2.5 8