Sk-36 ItemStandard Ai2o3(%)55 Fe2o3 (%)2.0 Refractoriness (sk)36 Refractoriness under load, 0.2mpa, ta, ((°c)1450 Porosity (%20-24 Bulk density (g/cm³)2.2-2.30 Cold crushing strength (mpa)45 Thermal expansion at 1000°c (%)0.3 Sk-38 ItemStandard Ai2o3(%)75 Fe2o3 (%)2.0 Refractoriness (sk)38 Refractoriness under load, 0.2mpa, ta, ((°c)1520 Porosity (%20-22 Bulk density (g/cm)2.4-2.5 Cold crushing strength (mpa)55 Thermal expansion at 1000°c (%)0.2.

Fire clay brick sk-32 ItemStandard Ai2o3(%)30 Fe2o3 (%)3.5 Refractoriness (sk)32 Refractoriness under load, 0.2mpa, ta, (°c)1300 Porosity (%)22-26 Bulk density (g/cm³)2.05 Cold crushing strength (mpa)25 Thermal expansion at 1000°c (%)0.6 Sk-34 ItemStandard Ai2o3(%)45 Fe2o3 (%)2.0 Refractoriness (sk)34 Refractoriness under load, 0.2mpa, ta, ((°c)1350 Porosity (%19-23 Bulk density (g/cm³)2.10-2.15 Cold crushing strength (mpa)25 Thermal expansion at 1000°c (%)0.6.

Y-fb gfb40 gfb42 gfb45 Al2o3(%)min. 40 40 42 45 Fe2o3(%)max. 2.5 Refractoriness()min. 1710 1730 1750 1750 Refractoriness under load 0.2mpa()min. 1300 1350 1400 1400 Apparent porosity(%)max. 22 20 20 20 Cold crushing strength (mpa)min. 30 30 35 40 Linear change after reheating(%)max. At 1350 2h +0.1 -0.4 At1400x3h +0.1 +0.1 +0.2 - 0.5 -0.4 -0.2.

Our landscape brick include: paving brick, water permeable brick, square brick, antique brick etc. We have passed the evaluations of iso9001:2008 quality system certification. And our landscape brick already export to many countries. Landscape brick ten advantages: 1. Light flavor, quality excellent. 2. A variety of colors, elegant designs, specifications. 3. Good high temperature resistance and freeze-thaw resistance. 4. Excellent permeability, adjust air humidity, prevent the urban heat island effect. 5. Acid erosion, rain erosion resistant. 6. No radiation, no dust, no pollution, ecological environmental protection. 7. Never fade. 8. High strength, long service life. 9. Convenient construction, easy operation and easy to repair and maintain. 10. Daily cleaning is simple. High quality, Low price. Product application: Antique buildings, paths, traffic lanes, steps, plazas, squares gardens, courtyards, patios, etc.

1.Description Fire clay refractory brick is made from flint clay clinker and binder, through high temperature sintering. Al2o3 content is 30%-48%, sio2 content is 50%-65%, and a small number of alkali metals, alkaline earth metal oxides, etc. Mineral composition is usually mullite, quartz and glass phase. Its refractoriness is 1580-1750¡ãc, refractoriness under load is 1250-1450 ¡ãc, line expansion coefficients is low, with good thermal shock resistance and strong ability to resist erosion acid slag. 2.Feature 1. High refractoriness, high-temperature endurable; 2. Good thermal shock resistance; 3.Good volume stability at high temperature; 4. Good corrosion resistance; 5. Good spalling resistance and wear resistance; 6. High mechanical strength; 7. High-temperature creep rate is low; 3.Applications Fire clay refractory brick is widely used in blast furnaces, hot blast stove, ladle lining, reheating furnace, cement kiln, tunnel kiln, boiler, coke oven, waste incinerators , carbon furnace, glass kiln , steel smelting furnace and various kiln lining and thermal technology equipment etc. On wooden pallets with plastic cover Pallet size:1.05*1.05m

1.Description High alumina fire brick contain al2o3 more than 48%, which is made of high grade bauxite through high temperature calcinations. Its refractories is usually above 1770 ¡ãc. The main mineral components are corundum and mullite phases. It is a kind of neutral refractory material so that it enjoys excellent resistance to acid and alkali corrosion. According to al2o3 content, it can be divided into three degrees:the al2o3 content is more than 75%.The al2o3 content range from 60% to 75%.The al2o3 content range from 48% to 60%. 2.Feature 1. High-temperature endurable . 2.Good thermal shock resistance. 3.High cold crushing strength 4.Good resistance to abrasion and corrosion. 5.Good thermal spalling resistance. 6.High mechanical strength. 7.Good volume stability at high temperature. 3.Applications High alumina fire brick is used for building blast furnaces, hot blast stove, electric stove roof, ladle, blast furnace and reverberatory furnace, lining of rotary kiln and glass kiln and chemical industrial kiln. In addition, high alumina brick is widely used as regenerative checker brick of open hearth, pouring system with the plug head, nozzle brick, etc. On wooden pallets with plastic cover Pallite size:1.05*1.05m

nductivity 4.Good heat insulating effect and energy-efficient 5.Good thermal shock stability. 6.Corrosion and erosion resistance 7.Long service life 3.Application Fire clay insulating brick can not be in direct contact with the flame, this insulating brick can be used as inner lining brick of industry kilns wall and industry furnance.Such as blast furnace, hot blast stoves , electric arc furnace, cement kiln, melting furnace, ignition furnace, flue, refining equipment, heating equipment and piping, regeneration device, gas furnace, soaking furnace, annealing furnace, heat reaction chamber and other thermal industrial equipment. On wooden pallets with plastic cover Pallite size:1.05*1.05m

It has the common advantages of corundum castable and mullite castable.High temperature strength, good thermal shock resistance and structure spalling resistance;Good thermal shock resistance, high load softening temperature, low high temperature creep rate, good chemical corrosion resistance, can be used for large power station boiler anti-wear lining and other high temperature kiln lining.

Clay brick

WE CAN SUPPLY THE MATERIAL AS PER INDIAN STANDARD, ASTM, GOST,ISO AND AS PER CUSTOMER'S SPECIFICATION BRICKS ARE PACKED IN CORRUGATED BOXES AND THEN PALLETIZED

The series of insulating refractory bricks supplied by our ZS Refractories are assigned to the group of lightweight refractory bricks and are manufactured on the basis of naturally occurring lightweight raw materials, including high alumina light weight insulation brick, fire clay insulation brick, silica insulation brick, mullite insulation brick and so on. Having advantages of low thermal shock resistance, corrosion atmosphere resistance, high dimensional accuracy and low reheat shrinkage, our insulation bricks can greatly meet your demands of different shapes and types.

Our high alumina brick is manufactured with selected bauxite chamotte as main material, fired at high temperature by advanced process with strict quality control. High alumina, as the name tells, meaning the content of alumina percentage is higher than 45. And alumina is one of the most chemically stable oxides, it offers excellent hardness, strength and spalling resistance. Our high alumina brick is widely used in industries which need heat insulation, such as the linings of masonry furnaces, hearth and shaft of blast furnaces, ceramic kilns, glass tanks, cement rotary kilns and so on.

ZS Refractories offers you high quality fireclay refractory brick with competitive prices. It is mostly used refractory brick in the iron & steel industry, glass industry, non-ferrous industry, cement industry, pottery kilns and many other industries. With the advantage of its lower cost, the main chemical components of fireclay brick are SiO and Al. And the main raw materials are heat resistant bonding clays and fired clays.

Silica brick is a kind of acid refractory mainly made from tridymite, cristobalite and a small amount of residual quartz as well as glass phase. The raw refractory material is natural silica sand whose SiO2 content should be more than 96%. The higher SiO2 content in silica sand, the higher temperature silica bricks resist, its refractoriness under load is as high as 1640 ~ 1670. Glass kiln silica brick has high temperature and volume stability, no pollution to glass liquid, chemical corrosion resistance, small bulk density, and can reduce the weight of furnace body. It also has the ability of resistance to acidic and alkalic steam attack with high performance of flushing resistance. It is mainly used to build the doghouse crown, suspended wall of channel, top crown and inlet sealing, and also to be used to build the checker chamber, chute, combustion chamber, coking chamber and furnace arch in glass melting furnaces. Silica brick has good corrosion resistance to glass liquid. It is the preferred refractory for crown construction of glass melting furnaces, in terms of cost, strength and of defect potential.

Zircon brick is an acid refractory brick with the advantages of good slagging resistance, mechanical strength, high refractoriness under load, excellent thermal shock stability, good creep resistance and good corrosion resistance to glass liquids. Our zircon brick is made from stable zircon sand, it is widely used in the high erosive zones of glass furnace, non-ferrous metal smelting furnace, pure steel furnace, chemical industry, and metallurgy industry, especially used in soda-lime glass kiln as neutral brick, skew brick etc. It is suitable for paving and sub paving, channel blocks as well as sidewall of meter of glass fiber furnace and floating glass tanks.

fireclay insulation brick high alumina insulation brick mullite insulation brick bulk density: 0.5-1.0 g/cm3

Magnesia carbon brick isprepared by using high grade fused magnesia and big crystal flake graphite as raw materials,adding compound high efficiency antioxidant and additives,after appropriate grading, moulding and heat treatment process.They are characterized by good oxidation resistance,slagresistance and thermal shock resistance. It can be applied in different parts of steel making equipment,such as converter, electric furnace, refining frnace and ladle.

The content of magnesium ramming material is above 84%, calcium oxide is controlled at 6%~8%, and ferric oxide is about 6%. Due to its high fire resistance, the service temperature reaches 1850~1950. With the use of superfine powder technology, make the material with high CaO magnesia and ultrafine iron oxide, can fully in the process of calcining synthetic reaction, generating distribution evenly throughout the material 2 calcium ferrite, and no obvious shrinkage phenomenon in the sintering process, ensuring the quality of the material of the sintering synthesis and improve the effect of the use of the material at the same time.After being sintered at 1600â?? for 3 hours, the compressive strength of the sample can reach 40~50MPa, which basically meets the compressive strength indexes required by nickel iron smelting.Therefore, after a certain temperature (not less than 1200â??), the material has high density, high compressive strength, good erosion resistance and volume stability. Magnesium ramming material is used in the bottom of the hot nickel iron furnace. Magnesium ramming material has good heat preservation and insulation property, which can reduce heat loss, improve furnace temperature, shorten smelting time and reduce smelting power consumption.The compactness of the forged furnace lining is good, which solves the local leakage phenomenon caused by the non-compactness of the formed magnesia brick masonry furnace lining. The use of magnesia ramming material to build the nickel-iron furnace has obviously improved the lining life cycle, reduced the consumption of refractory materials, and replaced the shaped materials with amorphous materials, which is over the water.

The Al2O3 content is more than 55%, and is calcined from a high-content alumina raw material such as a silicone raw material or a bauxite. High heat resistance and high temperature resistance at 1770 C and above. Has good slag resistance, mainly used in the masonry of steelmaking electric furnace, glass furnace, cement rotary furnace and so on. Characteristics of High Alumina Brick Price: 1.Refractoriness: More refractory than refractory clay bricks and semi-silica bricks, up to 1750-1790C, belonging to high-grade refractory materials. 2. Load softening temperature: Since the high aluminum has a high Al2O3 content, a low impurity content, and a low formation of the molten glass body, the fire-resistant softening temperature is higher than that of the refractory clay brick. However, since the mullite crystal has not yet formed a network structure, the load softening temperature is lower than the load softening temperature of the silica brick. 3. Slag resistance: High Al2O3 has high Al2O3 content, close to neutral refractory material, and can resist the erosion of acid slag and alkali slag. Because it contains SiO2, the resistance to alkali slag is less than acid resistance.