Submerged ARC welding wires are used with corresponding flux to get metal welding with excellent machinery properties. They have a series of advantages, such as high production efficiency, stable welding quality, beautiful welding bead appearance, deep penetration, etc.
Features: submerged-arc welding wire is used with corresponding flux to get metal welding with excellent machinery properties. They have a series of advantages, such as high production efficiency, stable welding quality, beautiful welding bead appearance, deep penetration, etc. Submerged-arc welding wire can be used in shipbuilding, bridge building, machinery manufacture and general welding purposes.
Application: submerged-arc welding wire can be used to welding low carbon steel and some low-alloy steel (16mn) structures with flux hj430, hj431, hj433 in the field of, such as boilers, nuclear stations, chemical containers, ships, pressure vessels, etc.Used together with sintered flux 101. It can be used for welding atmospheric corrosion-resistant steel structures with tensile strength of 550mpa. Submerged-arc welding wire are widely used as welding carbon steel and corresponding strength, such as 5mnvn, suitable for pipe-line steel welding.
Packing:
1. 25kg, 50kg, 150kg, 200kg, 350kg transverse wind without core, vaccum packing
2. 250kg, 500kgs steel spool
Submerged-arc welding wire can be packed as your requirements.
Packing:
Spool packing:precision layer wire self into coils, covered with the wax paper, each coil in ploybag and then in the carton, then put on wooden pallets
Tig packing: straight line wire, 1000mm for the length, every 5kg in one plastic tube.
We have the largest automated factory in northern China.The annual production capacity of welding wire is 300,000 tons.There are varieties such as ER70S-G, ER70S-3, ER70S-4, ER70S-6, ER70S-6N, ER70S-8, ER90S-G, ER100S-G, ER110S-G, etc. The companya's products have successively passed the certifications of EU CE and ABS, CCS, LR, DNV, GL, KR, and NK classification societies. I can give you the best quotation. You can send me the specifications and Datasheet of the products you need.
Buy SAW Wire Submerged Arc Welding Wire. If you're looking for a high-quality wire to weld with, look no further than AWS EL8 SAW Wire Submerged Arc Welding Wire. This wire is made from chrome-molybdenum alloy, which makes it strong and durable.
Buy Copper Alloy Submerged Arc Welding Flux and Wire. Submerged Arc Welding Flux and Wire is a professional grade welding flux and wire. It is designed to help you weld faster and easier.
78154 Submerged Arc Welding Wires Suppliers
Short on time? Let Submerged Arc Welding Wires sellers contact you.
Buy Submerged Arc Welding At Royal Welding Wires. Do you need long-lasting, quality saw welding wires Look no further than Saw Welding Wires - Submerged Arc Welding! These professional-grade wires are designed to withstand the toughest welding conditions.
Weldings solder CO2 gas shielded welding wire ER50-6 submerged-arc welding wire H08A, ER05-6 AWS ER70S-6
CO2 gas shielded welding wire
Types: flux-cored wire and solid wire
Diameter: 0.8mm-1.6mm
Melting Point: Normal
Weight: 5~20kg/spool;250~350kg/drum
Application: welding
Flux Content: standard
Packaging Detail:15kgs/roll/carton, 72cartons/pallet, 21-24metric tons/20ft container
Usages:
CO2 gas shielded welding wire Almost used in welding of the carbon steel and the low alloy steel. And welding material is the combination of filler and fluxes.
ER50-6 welding wire 16.mm
1.Diameters: 0.8mm,1.0mm,1.2mm,1.6mm
2.Weight: 5kg,10kg,15kg/spool
3.Packing: 15kgs/roll/carton, 72cartons/pallet, 21-24metric tons/20ft container
4.Types: flux-cored wire and solid wire
ER50-6(AWS A5.18 ER70S-6) meet China standard, main chemical composite(%): c0.06-0.15¡¢mn1.40-1.85¡¢si0.80-1.15¡¢p¡Ü0.025¡¢s¡Ü0.035¡¢cu¡Ü0.50.
Usages:
CO2 gas shielded welding wire Almost used in welding of the carbon steel and the low alloy steel. And welding material is the combination of filler and fluxes.
Co2 welding wire AWS ER70S-6, 1.2mm
Material: Cooper plating
Wire Size: 0.8mm 1.0mm 1.2mm 1.6mm
HO8Mn2SiA Ho8Mn2Si Ho8Mn2SiMoa
Spool Size: D100mm, D200mm,D270mm,D300mm,K300mm
Melting Point 500(¡æ)
Net Weight: 1kg,5kg,15kg,18kg,20kg
Application: welding low carbon steel and high strength steel structure
GB/8110-1995 ISO9001:2000
Fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam
1. Properties: Used for welding low carbon steel and low alloy steel structures, especially for welding of thin plates and can be applied to carbon steels, vehicles, construction, shipbuilding, bridge building, etc.
2. Product features: have excellent mechanical performance such as fast melting rate, high depositing efficiency, stable arc, little spatter, beautiful seam. Suitable for all-position welding work.
3. Technical data:
A. Chemical composition: C0.06-0.15, Mn 1.40-1.85, Si 0.80-1.15, P <=0.025, S <=0.035, Cu <=0.35, Ni <=0.30, Cr <=0.20
B. Tensile strength: ¡Ý500MPa, yield point: ¡Ý420MPa, elongation: ¡Ý22, AK-V impact value: ¡Ý27(-29)
Lj-sj501 welding flux aws a 5.17 f6a0-el12 soldering flux f7a2-em12k
Flux type: aluminum-rutile
Basicity index: 0.5-0.8
Remark: 1.Before welding, fluxes should be baked for two hours at 300-350ºc.
2.Removal of rust, oil, dirt, water, impurities, etc in welding areas.
Packing: 25kg/bag, pallets are available.
Lead time: 2 weeks
Performance: vrey good weld bead appearance, excellent slag removal with narrow groove and fillet welds. High resistance to cracking and porosity and insensitive to oil, rust, scale and dirt on the surface to be welded.
Applications: used for ordinary carbon steel, low alloy structure and boiler quality steel and high speed welding.
Contact: miss helen duan
Tel/fax: 0086-532-85641729
Lj-sj501 welding flux aws a 5.17 f6a0-el12 soldering flux f7a2-em12k
Flux type: aluminum-rutile
Basicity index: 0.5-0.8
Remark: 1.Before welding, fluxes should be baked for two hours at 300-350ºc.
2.Removal of rust, oil, dirt, water, impurities, etc in welding areas.
Packing: 25kg/bag, pallets are available.
Lead time: 2 weeks
Performance: vrey good weld bead appearance, excellent slag removal with narrow groove and fillet welds. High resistance to cracking and porosity and insensitive to oil, rust, scale and dirt on the surface to be welded.
Applications: used for ordinary carbon steel, low alloy structure and boiler quality steel and high speed welding.
Contact: miss helen duan
Tel/fax: 0086-532-85641729
CO2 gas shielded welding wires, this series welding wires can be used for welding low carbon steel and low alloyed steel structure, such as ships, vehicles, bridges, engineering machinery, pressure vessel and construction etc.
"TAA"CO2 gas shielded welding wires have excellent technological properties such as smooth steady feeding,fast melting rate,high depositing efficiency,little spatter and beautiful seam,which are suitable for all-position welding work.
The series of welding wires are mainly suitable for welding low carbon steel and low alloyed steel structure,such as ships,vehicles,bridges,engineering machinery,pressure vessel and construction etc.
Standard: AWS ER70S-6
Diameter:0.6mm-2.0mm
Package:15kg/D270mm black spool,1080kg or 1260kg/pallet.
Argon arc welding technology is on the basis of the principle of common electric arc welding, using the argon gas protection for metal welding materials, through high current on the welding backing weld material melt into a liquid pool formation, cause the weld metal and weld material at a metallurgical bonding. Welding technology, due to the continuously in high temperature melting welding on argon gas, make the weld material can not contact with oxygen in the air, to prevent the oxidation of the weld material, thus welding stainless steel, iron, metal metal
This products have been approved by abs / ccs / dnv / kr / nk / gl / lr, and tuv / ce / db.
Description:
·ly er50-6 is a low alloy steel gas shielded welding wire, protected with pure co2 or ar+co2 gas.Stable arc, low spatters, excellent fabrication weldability and lowsensitivity of weld gas porosity can be obtained during welding.It is suitable for all position welding especially with large welding current range.It can show very good welding performance.
Applications:
·suitable for single-pass and multi-pass welding for structures fabricated by carbon steel and 500mpa grade low alloy steel, such as vehicles, bridges, construction and mechanical structures etc.
Instructions:
A.Suitable for using shielding gas at the speed of 20-25 liters per minute.
B.Windshield must be set up in the welding zone, due to gas porosity may be caused by strong wind.
C.Wire extention should be 10-20mm if the current range is under 300a and if above 300a, 20-25mm.
Chemical composition of wire(%)
CMnSiSPCuOthers
Standard(gb)0.06-0.151.40-1.850.80-1.15?0.035?0.025?0.50?0.50
Standard(tuv/ce)0.06- 0.141.30-1.600.70-1.0?0.035?0.025?0.35?0.50
Type0.081.510.920.0200.0160.200.02
Mechanical proper ties of deposited metal
Tensile strength?bmpa)Yield point?0.2(mpa)Elongationd5(%)Impact v-notch (j)(-20oc)Shielding gas
?500?420?22?27100%co2
56050027102100%co2
Specification & recommended current range(dc+)
Diameter(mm)
F0.8 f1.0 F1.2 F1.6
F current(a)40~18050~22080~350170~550
V current(a) 40~14050~16050~180
Oh current(a) 40~12050~16045~180
Specification: f0.6mm/f0.8mm/f0.9mm/f1.0mm/f1.2mm/f1.6mm
1kg/spool; 5kg/spool; 15kg/spool or as customers's requirements.
Package: plastic spool or metal spool.
1 spool per carton, 72 cartons per pallets.
We are a professional supplier of welding wire products with excellent welding process performance; We have the largest welding wire production base in northern China,The annual output of welding wire is 300,000 tons.
The compan's products have successively passed the certifications of EU CE and ABS, CCS, LR, DNV, GL, KR, and NK classification societies.
We look forward to closer cooperation between our two companies .Hope you will take this opportunity for mutual benefit .Assure that you will delight our product quality and good service .
We have the largest automated factory in northern China.The annual production capacity of welding wire is 300,000 tons.There are varieties such as ER70S-G, ER70S-3, ER70S-4, ER70S-6, ER70S-6N, ER70S-8, ER90S-G, ER100S-G, ER110S-G, etc. The company�¢??s products have successively passed the certifications of EU CE and ABS, CCS, LR, DNV, GL, KR, and NK classification societies.
I can give you the best quotation. You can send me the specifications and Datasheet of the products you need.
We have the largest automated factory in northern China.The annual production capacity of welding wire is 300,000 tons.There are varieties such as ER70S-G, ER70S-3, ER70S-4, ER70S-6, ER70S-6N, ER70S-8, ER90S-G, ER100S-G, ER110S-G, etc. The companyâ??s products have successively passed the certifications of EU CE and ABS, CCS, LR, DNV, GL, KR, and NK classification societies.
I can give you the best quotation. You can send me the specifications and Datasheet of the products you need.
78154 Submerged Arc Welding Wires Suppliers
Short on time? Let Submerged Arc Welding Wires sellers contact you.