Type 2 OPC cement, a variant of Portland cement, possesses moderate heat of hydration and sulphate resistance. Its balanced properties make it suitable for general construction applications, providing durable and stable structures in environments with moderate sulphate exposure. Pozzolan cement is a blend of Portland cement and pozzolanic materials, such as fly ash or silica fume. It enhances concrete properties by improving workability, durability, and reducing heat of hydration. Pozzolan cement offers sustainable construction solutions and reduces the environmental impact of concrete production. Clinker Cement clinker is the intermediate product produced during the cement manufacturing process. It consists of finely ground materials, such as limestone, clay, iron ore, and shale, heated to high temperatures in a kiln. Clinker forms the basis of various types of cement when combined with gypsum and other additives.
White cement is a hydraulic binder produced for decorative purposes by grinding white clinker, which is obtained from a mixture of special-quality clay (pyrophyllite, kaolinite) and limestone, with gypsum. It is a type of cement used in binding of elements such as tiles, ceramics in luxurious architectural structures. It is one of the products with the highest strength and whiteness in the market. This product is for buildings that require high strength, for general use and structures with aesthetic purposes. Its basic distinctive properties are high strength gain, aesthetic and decorative features, smooth surface and elegant appearance. It has a minimum whiteness rate of 85%. It has a stable shade in addition to its high level of whiteness, which provides a great advantage in the production of building elements. It can be used in colored concrete and mortar. Thanks to its high level of whiteness and fine structure, it is used in the production of building chemicals.
Gold, aluminum billets, aluminum ingots, copper, steel, quartz, diesel, jet fuel, d6, bitumen, petroleum coke, indonesian coal, cement, fertilizers, urea 46, sulphur, euro pallets, wooden pallets, tomato paste, frozen potatoes, frozen french fries, frozen chicken, sugar, salt, rock salt, rice, beet pellets, beet molasses, herbs & spices, frozen & fresh strawberries, frozen & fresh fruits, frozen & fresh vegetables.Manufacturing, trading, exporting, brokerage
Moderate SulfateResisting Portland Cement conforming to ASTM C 150-18, Type II.
cement, in general, adhesive substances of all kinds, but, in a narrower sense, the binding materials used in building and civil engineering construction. Cements of this kind are finely ground powders that, when mixed with water, set to a hard mass. Setting and hardening result from hydration, which is a chemical combination of the cement compounds with water that yields submicroscopic crystals or a gel-like material with a high surface area. Because of their hydrating properties, constructional cements, which will even set and harden under water, are often called hydraulic cements. The most important of these is portland cement.
PRODUCTS FALCON ORDINARY PORTLAND CEMENT Ordinary Portland Cement (OPC) OPC being the most popular product under the Falcon Brand is used in all types of general construction. It is manufactured from Portland Cement Clinker and Gypsum and not only conforms but also surpasses to the following standards, European Standard EN 197-1 : 2011, CEM I, Class 42.5N Specification Sheet Physical Properties OPC Properties EN 197-1:2011 CEM I Class 42.5 N PS-232-2008® Fineness cm2/gm 2250 2800 Setting Time Initial (Mins.) 60 Min. 30 Min. 120 Final (Hrs) 10 Max. 3.25 Soundness L-Chatlier(mm) 10 Max 10 Max. 0.50 Auto Clave (%) 0.80 Max. 0.27 Compressive strength 2-Days N/mm2 10 Min. 23.50 3-Days 23.00 Min 30.00 7-Days 33.00 Min* 36.00 28-Days 42.50 Min
Ordinary Portland Cement For Sale Type I/ii Low Alkali Astm C 150 Can Provide Specifications Characteristics Upon Request We Can Arrange For Quantities From 20.000mt - 50.000mt Per Month In Big Bags Of 1.5tons & 2.00tons Do Not Hesitate To Contact Us For Prices Basis Fob Or Cif Or To Provide What Is Your Required Specifications To Arrange
Terry towels, textile made ups, agriculture products, essential oils, sugar icumsa 45, sugar s 30, copper cathodes, copper concentrate, copper ore, iron ore, cobalt, zinc, bauxite, limestone, cement etc..Exporters
Gypsum rocks, gypsum powder, rock salt (industrial salt and deicing salt), food grade salt, sodium bicarbonate, limestone, white limestone (marble chips), sulphur (granular, lumps).
- Product name: Portland cement - Standard: ASTM C150 type 1 - Colour: Grey - Feature: Expansive - Main Raw Material: Silicate - Hardening Feature: Extra Rapid Hardening - Heat of Hydration: Moderate Heat - Pack in 25-40-50kg PK/PP bag directly or in 25-40-50kg PK/PP bag repack in 2 tons sling or pack in 1-1.5-2 tons jumbo bag. - Delivery: in containers or in bulk vessels
Fmcg, industrial supplies, equipment, raw materials, minerals, lubricants, cements, barite , building and construction, fresh vegetables & fruits, lubricants & oils,quartz, dry fly ash, fly ash bricks,quartz stone, all kinds of quartzs, automobile spare parts and all kinds of engineering motors, Automobile spare, Parts And Accessories Of The Motor Vehicles.Fast growing logistics service provider caters to our customers requirements in terms of international freight forwarding. being at the forefront has enabled us to offer a great deal of expertise in the custom clearing and forwarding industry.
Portland Cement Type CEM II 42.5R Specifications: SO3: 2.20 % Chloride: 0.003 % Finess test: 3578 cm2/g Setting time: - Initial set: 125 minutes Soundness (LeChatelier): 0.5 Mm Compressive strength: - 2 days: 27.5 Mpa - 28 days: 54.6 Mpa
Portland Cement Type CEM I 52.5N SO3: 2.2 % SiO2: 21.33 % Fe2O3: 2.92 % Al2O3: 6.03 % CaO: 61.65 % Chloride: 0.005 % MgO: 1.78 % LOI: 2.75 % Insoluble residue: 0.37 % Total alkali: 0.56 % Finess test: 3614 cm2/g Setting time: - Initial set: 145 minutes - Final set: 205 minutes Soundness (LeChatelier): 1.0 Mm Compressive strength: - 2 days: 23.1 Mpa - 28 days: 54.2 Mpa
Portland Cement ASTM C150 Type I Specifications: SO3: 2.2 % MgO: 1.77 % LOI: 2.88 % Insoluble residue: 0.39 % Total alkali: 0.56 % Finess test: 0.56 cm2/g Setting time: - Initial set: 109 minutes - Final set: 191 minutes Autoclave expansion: 0.07 % Air content of mortar: 7.96 % False set, final penetration: 89.5 % Compressive strength: - 3 days: 21.41 Mpa - 7 days: 32.00 Mpa - 28 days: 44.28 Mpa
Dates, olive oil, olive, salt, fruits and vegetables, cement, gypsum, silica sand, clinker, lime, dolomite, bentonite, kaolin products, dolomite lime, marble powder, marble grit, granulated slag, steel slag, carton boxes..
It is a crucial ingredient if you want to achieve pure white concrete or mortar. Without its integration, standard portland cement alone will produce concrete and mortar that is grey adding titanium dioxide pigments can lighten the colour, but no concrete can be truly white without the addition of white cement mix. In this guide, we ll explore the uses and benefits of white cement, alongside other dyeing options for cement mixes. Type Cement Apperance white powder Colour white Brightness Super 90 Package weatherproof bag Main Raw Materials Calcium silicate Bag size 1*25kg Drying Method Air drying 2-3 hours Shelf Life 6 months HS Code 2523210000 Properties Value 3d compressive strength (Mpa): C35 3d flexural strength (Mpa): F5.5 28d compressive strength (Mpa): C47 28d flexural strength (Mpa): F8 Brightness/Whiteness (%): 90 Initial setting time (Min): 165 Final setting time (Min): 200 45�¼m fineness (%) 3.0
white Portland Cement, named White Cement, is hydraulic binding materials adding gypsum and grinding into fine particles. Pure whiteness keep lightness. It's used widely in various construction and decoration ie. Painting, sculpting, flooring, terrazzo products, and also white and colored concrete components. Type Cement Apperance white powder Colour white Brightness Super 90 Package weatherproof bag Main Raw Materials Calcium silicate Bag size 1*25kg Drying Method Air drying 2-3 hours Shelf Life 6 months HS Code 2523210000 Properties Value 3d compressive strength (Mpa): C24.5 3d flexural strength (Mpa): F4.5 28d compressive strength (Mpa): C43 28d flexural strength (Mpa): F7.5 Brightness/Whiteness (%): 90 Initial setting time (Min): 180 Final setting time (Min): 220 45�¼m fineness (%) 4.0
Cement clinker is a solid material produced in the manufacture of Portland cement as an intermediary product. Clinker occurs as lumps or nodules, usually 3 millimetres to 25 millimetres in diameter.
Kaaren gypsum powder, white cement, white portland cement, calcium carbonate, clay aggregate, bentonite, travertine, traonyx and onyx stone, gride bars, gypsum ceiling tiles, access panel, screw, sisal fiber, micro silica, silica sand, industrial salt, tiles adhesive, hydrated lime.
Microsilica (silica fume) is a by-product from silicon metal or ferrosilicon industries, is an amorphous silicon dioxide SiO2. This product reacts chemically with the calcium hydroxide in the cement paste which yields a calcium silicate hydrate gel that significantly enhances strength and durability. The super fine microsilica fills the voids between cement particles creating a very dense, less permeable concrete. White Cement advantages: Sustainability: Solar Reflectance Index (SRI): Floors finished with white or pastel color concrete will have a much higher SRI than floors with gray concrete, therefore they will reflect light better, and generate energy savings for the lifetime of the floors. Reduction of Heat Island effect: By constructing buildings with white concrete roofs or light-colored roof tiles, the Heat Island Effect is reduced from surfaces generating less heat and improved reflectivity. Architectural Concrete: White Portland Cement is ideal for decorative concrete and Architectural Concrete applications, Masonry and Cementitious Building Products. A key advantage of using white cement for these applications is that it provides a base color that can be tinted to custom colors to meet any color spectrum demand.