- Product name: Portland cement - Standard: ASTM C150 type 1 - Colour: Grey - Feature: Expansive - Main Raw Material: Silicate - Hardening Feature: Extra Rapid Hardening - Heat of Hydration: Moderate Heat - Pack in 25-40-50kg PK/PP bag directly or in 25-40-50kg PK/PP bag repack in 2 tons sling or pack in 1-1.5-2 tons jumbo bag. - Delivery: in containers or in bulk vessels
Portland Cement Type CEM II 42.5R Specifications: SO3: 2.20 % Chloride: 0.003 % Finess test: 3578 cm2/g Setting time: - Initial set: 125 minutes Soundness (LeChatelier): 0.5 Mm Compressive strength: - 2 days: 27.5 Mpa - 28 days: 54.6 Mpa
Portland Cement Type CEM I 52.5N SO3: 2.2 % SiO2: 21.33 % Fe2O3: 2.92 % Al2O3: 6.03 % CaO: 61.65 % Chloride: 0.005 % MgO: 1.78 % LOI: 2.75 % Insoluble residue: 0.37 % Total alkali: 0.56 % Finess test: 3614 cm2/g Setting time: - Initial set: 145 minutes - Final set: 205 minutes Soundness (LeChatelier): 1.0 Mm Compressive strength: - 2 days: 23.1 Mpa - 28 days: 54.2 Mpa
Portland Cement ASTM C150 Type I Specifications: SO3: 2.2 % MgO: 1.77 % LOI: 2.88 % Insoluble residue: 0.39 % Total alkali: 0.56 % Finess test: 0.56 cm2/g Setting time: - Initial set: 109 minutes - Final set: 191 minutes Autoclave expansion: 0.07 % Air content of mortar: 7.96 % False set, final penetration: 89.5 % Compressive strength: - 3 days: 21.41 Mpa - 7 days: 32.00 Mpa - 28 days: 44.28 Mpa
oPPGI, Pre-painted Galvanized Iron oColor Coated Sheet Coil.