Specification: Make barrel, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating. Application: HDPE (high density PE) - is used in products and packaging such as plastic bags, milk jugs, detergent bottles, margarine tubs, garbage containers, water pipes, woven bag, raincoat, polyethylene monofilament, woven yarn etc.. LDPE resins are made by high pressure autoclave process and mainly used for blown film extrusion and wire coating (cable sheath) etc.. They are widely used for applications for general purpose packaging films, heavy duty bags, shrink films, and foams. Application Suitable for film, heavy packaging film, cable insulation materials, blow molding and foam products.

Application: DS7601 application on PP, textiles, fabrics. Composition: Polypropylene synthesis Pipe grade

Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %

Raw Material : PP or BOPP Raw Material : Virgin material or recycled Color : All kinds of colors or as the customers requirement Printing : One side or both sides in multi-colors with film or non film Width : From 260-1300mm Length : As the customer’s requirement Weave : 10x10,11x11,12x12,14x14 or be customized Denier : 450D to 1500D Weights/m : 50g to 200g Surface Dealing : Anti-slip or plain Top : Heat cut or hemmed Bottom : Single folded, double folded, single stitch, double stitch Liner : coated or with liner bag for moisture proof Usage : rice, flour, sugar, salt, animal feed, asbestos, fertilizer, sand, cement and so on. Packing : 500pcs(bale),1000pcs(bale) or can be customized Minimum Order 20 feet container Delivery Time : 10-30days after place an order or negotiation Trade Term : CIF, CNF, FOB QINGDAO Special Requirements : As the customers requirements Treat : UV treated or as the customers requirement Loading qty. : 12 Tons/20’container, 23tons/40’hq. We can make all kinds of size

Raw Material: PP or BOPP Raw Material: Virgin material or recycled Color: All kinds of colors or as the customers' requirement Printing: One side or both sides in multi-colors with film or non film Width: From 260-1300mm Length: As the customer’s requirement Weave: 10x10,11x11,12x12,14x14,12×11or be customized Denier: 450D to 1500D Weights/m²: 50g to 200g Surface Dealing: Anti-slip or plain Top: Heat cut or hemmed Bottom: Single folded, double folded, single stitch, double stitch Liner: coated or with liner bag for moisture proof Usage: rice, flour, sugar, salt, animal feed, asbestos, fertilizer, sand, cement and so on. Packing: 500pcs(bale),1000pcs(bale) or can be customized Minimum Order20 feet container Delivery Time: 10-30days after place an order or negotiation Trade Term: CIF,CNF,FOB QINGDAO Special Requirements: As the customers' requirements Treat: UV treated or as the customers' requirement Loading qty.:12tons/20’container, 23tons/40’hq. we can make all kinds of size

Low density polyethylene (LDPE), also known as high pressure polyethylene, is a kind of plastic material, it is suitable for thermoplastic molding processing of various forming processes, forming processing is good. LDPE is mainly used for thin film products, but also for injection products, medical devices, medicine and food packaging materials, blow molding hollow molding products and so on. Item Value Product Name LDPE Granules Other Names Low Density Polyethylene Place of Origin China Grade Standard Industrial Grade,Injection molding grade Density 0.91-0.93 g/cm³ Appearance White Granules,customized color Application Plastic,film , bag Sample provide Package 25 kg/bag,1000 kg/bag,customized packag

LDPE Granules Low-density polyethylene (LDPE) is a synthetic resin using a high-pressure process via free radical polymerization of ethylene and is therefore also called high-pressure polyethyleneâ. It features light, flexible, good freezing resistance and impact resistance. LDPE is chemically stable. It has good resistance to acids (except strongly oxidizing acids), alkali, salt, and excellent electrical insulation properties. Its vapor penetration rate is low.

Can supply: approx. 95% HDPE - approx. 5% PP GRIND (REGRIND) FROM CAPS MIXED COLORS IN BIG BAGS. Size 8-10mm. Post commercial. Clean. No foreign bodies inside. Can load in 1x40' HC container approx. 23 MT (10%) Ready for shipment. Photos available upon request. If you are interested kindly contact us for more information (price, available quantity etc.). You are welcome to visit our company premises and supervise our materials. Certificate ISO: 9001, ISO: 14001, OHSAS 45001, AQSIQ and CCIC.

Item Test Condition Test Method Value Unit Density ISO 1183 0.950~0.955 g/cm MFR 190 C/2.16kg ISO 1133 1.7~2.5 g/10min Tensile strength at yield ISO 527-2 24 MPa Elongation at break ISO 527-2 >600 %

HDPE: HDPE cable material Property Unit Typical Value Mass density g/cm 3 0.941-0.959 Melt flow Rate(190 centidegree /2.16kg) g/10min 1.0 Tensile yield strength MPa 19.0 Flexural modulus Mpa 965 Elongation@ break % 400 Impact Embrittlement temperature centidegree MAX -118 Dielectric Constant 100KHZ 2.32 1MHZ 2.31 Loss Tangent 100KHZ MAX 0.0001 1MHZ MAX 0.0001 Volume resistivity OHM-CM MIN 1x10 15 Application Mainly used for the production of high toughness of the telephone,cable insulation material LDPE: Physical Properties Test Method Nominal Value Unit Density ISO 1183 0.921 g/cm3 Melt Mass-Flow Rate (MFR) ISO 1133 1.9 g/10min Hardness Shore Hardness (shore D) ISO 868 45 Mechanical Properties Tensile Modulus ISO 527-2 175 MPa Tensile Strength Yield, ISO 527-2 9.0 MPa Break, 13.0 MPa Tensile Strain(Break) ISO 527-2 850 % Modulus of Elasticity Internal Method 250 MPa Thermal Vicat Softening Temperature ISO 306/A50 89.0 �°C Melting Temperature (DSC) DIN 53765 108 �°C Peak Crystallization Temperature (DSC) DIN 53765 97.0 �°C Heat of Fusion DIN 53765 110 J/g Electrical Volume Resistivity ASTM D257 8.5E+15 ohm â?¢cm Dielectric Strength ASTM D149 30.0 kV/mm Dielectric Constant (60Hz) ASTM D150 2.20 % Dissipation Factor (60 Hz) ASTM D150 0.00050 LLDPE Properties Test conditon Test method Test data Unit Density 0.91 MFI 2 Drop impact strength ASTM D-1709 90 g Elongation ,vertical/horizontal ASTM D-882 600/800 % tensilestrength,thermal resistance ASTM D-1004 105/95 Kg/cm elongation ASTM D-638 930 % tensile strength ASTM D-638 180 tensile strength,vertical/horizontal ASTM D-882 380/350 Vicat softening point ASTM D-1525 103 C melting point ASTM D-2117 126 C Turbidity ASTM D-1009 12 % 45 glossness ASTM D-2457 75 %

Specification: Virgin. Type: Film grade, Injection molding grade, Blowing molding grade, extrusion grade,

PP granules, all colors available. Please contact us for more information

Polypropylene PP Virgin Granules/PP Raw Material Granule/ PP Granules Virgin Polypropylene. Please contact us for more information,

Virgin & Recycled Low Density Polyethylene LDPE Granules

Properties 1. Excellent transparency, outstanding resistance to aging. 2. It has good insulating properties and mechanical strength; to acid, alkali, salt has a strong resistance to corrosion; and because easy processing. Applications 1.Extruded sheets for signage, displays and building material 2.Motive parts such as tail lamps, meter covers and sun visors 3.General sundries such as tableware, kitchenware, giftware and bathroom accessories 4.Optical lenses such as sunglasses, reading glasses and camera lenses 5.Light guide panels for LCD displays 6.Other applications such as mobile phone display panels, clock covers, lighting covers/accessories, optical fibres, toys, etc.

Item Test Condition Test Method Value Unit MFR 190C/2.16kg ASTM D-1238 20 g/10min Density --- ASTM D-792 0.954 g/cm3 Tensile strength at yiled --- ASTM D-638 28 MPa Elongation at break --- ASTM D-638 250 % Impact tensile strength --- ASTM D-1822 42 kJ/m2 ESCR ASTM D-1693 3 --- VACIT --- ASTM D-1525 127 C

Virgin LLDPE Granules LLDPE 7042 LLDPE raw material film grade

Can supply TEXTILE WASTE WHITE FABRIC CLIPS CUTTINGS NON WOVEN BALES Composition of clips cuttings approx 60 POLYESTER approx 30 VISCOSE and approx 10 TENCEL LYOCELL May have foreign bodies approx 1 comes from baling procedure POST INDUSTRIAL MATERIALS COME FROM FACTORY THAT PRODUCE BABY WIPES Can load in 1x40HC container approx 22 MT 10