PRODUCT DATA SHEET ACID RESISTANT BRICK Material : FIRECLAY Type Acid Resistant Brick Size (mm) : 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : * We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: * Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions - Heavy thermal shock Characteristic Fireclay Type Acid Resistant Brick - Test Standard Bulk Density, lbs/ft3 - 2.25 to 2.30 ASTM C-20 Water Absorption, % - 0.1 to 1.8 ASTM C-20 Apparent Porosity, % - 4.05 to 4.14 ASTM C-20 Acid Solubility (H2SO4), Loss in Mass,% - 6.1 to 6.8 ASTM C-279 Modulus of Rupture, Mpa - 14.6 ASTM C-67 Compressive Strength, PSI - 15500 to 17250 ASTM C-67 Abrasion Resistant , Volume in mm3 - 71 to 96 EN 102 Surface Hardness, MOHS Scale - 7 Thermal Conductivity, BTU-in/hr-ft-F - 6.94 to 7.12 ASTM C-236 Thermal Expansion Coefficient,in/in/Fx10-6 - 2.6 to 2.8 EN 103
Item Fireclay brick Sk32 Sk34 Al2o3 (%) ¡ý 38 42 Refractoriness (oc) ¡ý 1670 1730 Refractoriness under load, oc, 0.2mpa ¡ý 1250 1300 Linear change(%), oc¡á2h 1350 1350 -0.5~0 -0.5~0 Porosity (%)¡ü 26 26 Cold crushing strength, mpa¡ý 15 20 Wooden pallets
Y-fb gfb40 gfb42 gfb45 Al2o3(%)min. 40 40 42 45 Fe2o3(%)max. 2.5 Refractoriness()min. 1710 1730 1750 1750 Refractoriness under load 0.2mpa()min. 1300 1350 1400 1400 Apparent porosity(%)max. 22 20 20 20 Cold crushing strength (mpa)min. 30 30 35 40 Linear change after reheating(%)max. At 1350 2h +0.1 -0.4 At1400x3h +0.1 +0.1 +0.2 - 0.5 -0.4 -0.2.
Refractory clay bricks, fireproof clay bricks, or refractory clay bricks are blocks of refractory ceramic material used to line furnaces, kilns, fireboxes and fireplaces. Manufactured by Yutong, these bricks are primarily used to withstand high temperatures, but often also have a low thermal conductivity to improve energy efficiency. Our company manufactures and supplies these refractory bricks for steel, glass, furnaces and various other industries that require fire to survive. Ordinary bricks will not survive at such temperatures. Yutong is a well-known manufacturer and supplier of high-quality refractory bricks. Refractory clay bricks are available in a wide range of shapes and sizes and many other shapes and sizes can be customized to meet customer/site requirements. Our high alumina refractory bricks / high-density refractory bricks are proven solutions for various industries for refractory applications in the temperature range of 1260 c - 1450 c and have been successfully used by different companies around the world.
Description The low Porosity fireclay Bricks are made of super calcined flint clay and calcined bauxite, With high Pressure formed and high temperature sintered. Due to its low apparent porosity, Strong resistance to erosion and high refractoriness under load,They are wildly used in Glass kiln,Blast furnace, Metal mixer Furnace,Hot metal mixer ladle,Coke dry quenching devices , etc. Specifications 1. Low bulk density, low thermal conductivity, good thermal performance. 2. Refractory category allow direct contact of fire, suitable for various atmosphere 3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely
ZS Refractories offers you high quality fireclay refractory brick with competitive prices. It is mostly used refractory brick in the iron & steel industry, glass industry, non-ferrous industry, cement industry, pottery kilns and many other industries. With the advantage of its lower cost, the main chemical components of fireclay brick are SiO and Al. And the main raw materials are heat resistant bonding clays and fired clays.
ProductSD42 ITEMREQUIRED SPECIFICATION REFRACTORINESS C1750 RUL C1450 Reheating linear change 1450C*2H+0.1/-0.4 CCS MPa40 AP %21 BD g/cm32.20 Al2O3 %42 Fe2O3 %1.8
Circle fireclay bricks are specialized fire bricks that are used to construct circular structures or lining in high-temperature environments. The circular shape of these bricks allows for smooth and continuous lining without the need for excessive cutting or fitting. This makes them more efficient to use in curved or circular structures, helping to ensure a reliable and durable construction in high-temperature environments. Applications of Circle Fireclay Bricks: Kilns: Circle fireclay bricks are commonly used to build the inner lining of kilns, which are used for firing ceramics, pottery, and other materials at high temperatures. Furnaces: In industrial settings, circle fireclay bricks are used to construct the interior of furnaces, which are used for melting metals or processing other heat-intensive materials. Chimneys: The circular shape of these bricks makes them ideal for constructing chimneys and flues, where they can withstand the high temperatures and corrosive byproducts of combustion. Forges: Circle fireclay bricks are also used in blacksmith forges, where they create a heat-resistant lining to contain the intense heat needed for metalworking. Pizza Ovens: In traditional pizza ovens, circle fireclay bricks are often used to line the cooking chamber, as they can endure the high temperatures required for baking pizzas.
Fireclay bricks are mainly made from chamotte, being high pressure pressed and sintered in high temperature. Main minerals compositions are mullite phases. These products are widely used in all parts of furnace lining for middle and small capacity blast furnaces because of their excellent physical and chemical properties in high temperature. It also can be used in lining for other kinds of furnace.
Sk-36 ItemStandard Ai2o3(%)55 Fe2o3 (%)2.0 Refractoriness (sk)36 Refractoriness under load, 0.2mpa, ta, ((°c)1450 Porosity (%20-24 Bulk density (g/cm³)2.2-2.30 Cold crushing strength (mpa)45 Thermal expansion at 1000°c (%)0.3 Sk-38 ItemStandard Ai2o3(%)75 Fe2o3 (%)2.0 Refractoriness (sk)38 Refractoriness under load, 0.2mpa, ta, ((°c)1520 Porosity (%20-22 Bulk density (g/cm)2.4-2.5 Cold crushing strength (mpa)55 Thermal expansion at 1000°c (%)0.2.
Fire clay brick sk-32 ItemStandard Ai2o3(%)30 Fe2o3 (%)3.5 Refractoriness (sk)32 Refractoriness under load, 0.2mpa, ta, (°c)1300 Porosity (%)22-26 Bulk density (g/cm³)2.05 Cold crushing strength (mpa)25 Thermal expansion at 1000°c (%)0.6 Sk-34 ItemStandard Ai2o3(%)45 Fe2o3 (%)2.0 Refractoriness (sk)34 Refractoriness under load, 0.2mpa, ta, ((°c)1350 Porosity (%19-23 Bulk density (g/cm³)2.10-2.15 Cold crushing strength (mpa)25 Thermal expansion at 1000°c (%)0.6.
Physical properties Brand SK-32 SK-34 SK-35 SK-36 SK-38 Index Refractoriness íµ 1730 1750 1770 1770 1790 bulk density g/cm3 2.15 2.2 2.3 2.35 2.52 Apparent porosity ¿Q% 24 24 23 23 23 Cold crushing strength ¿RMpa 30 35 40 45 65 Refractoriness under load (0.2MP) íµ 1350 1350 1400 1450 1550 Permanet liner change 1500íµ 2hrs% +0.2to-0.2 +0.2to-0.2 +0.1to-0.4 +0.1to-0.4 +0.1to-0.4 Thermal expansion at 1000 íµ 0.5 0.5 0.5 0.5 0.5 Fe3O4% 1.96 1.93 1.9 1.87 2 Al2O3% ¿R 42 48 55 60 65 SiO2 48-50 46-48 41-44 37-40 27-30
1.Low thermal conductivity, 2.Good thermal insulation performance. 3.Good integrity with furnace lining Tyical features: High compressive strength in normal temperature, high ability for anti-abrasion during work, low shrinkage degree under high temperature so as to maintaining an integrity of the furnace lining; low apparent porosity, and fe2o3 content to reduce the carbon deposit in the blowhole and avoid the bricks broken in case of expansion; seldom melting point settings shape. Fireclay bricks are divided into different kinds which are mainly as below: (1) normal purpose fireclay bricks (2) fireclay bricks for coke oven (3) fireclay bricks for blast furnace (4) fireclay bricks for hot-blast stove (5) glass furnace bottom fireclay blocks (6) lower porosity fireclay bricks. In plastic sheets or in wooden pallets
Products: Refractory bricks, unshaped refractory, refractory fibre, landscape brick, etc. Our refractory brick include: fireclay brick, high alumina brick, low porosity fireclay brick, mullite brick, silica brick, zircon brick, insulating brick, alkali resistant bricks, etc.
Our company located in yangquan city, shanxi province, china, and yanquan city is one of the Largest refractory material base in china. We are in position to supply various kinds of Refractory bricks, such as high alumina and fireclay bricks, insulating bricks etc With the catalogue as follows: 1. Fireclay brick 2. High alumina brick 3. Insulating brick 4. Unsintered phosphate brick 5. Al-c sliding plate 6. Nozzle 7. Hollowwares 8. Refractory mortar 9. Refractory castables 10.Other refractory material.
For hot blast stoveFor eaf roofFor general use Goods no.Ghha65,Ghha55,Ghha48,Rhs,Rh1,Rh2Al,75Al-1Al-2 Al2o3(%) min655548807565756555 Refractoriness( ) min179017701750185018001790179017901770 Refractriness under load 0.2 mpa( )150014701420155015301520152015001470 Apparent porosity (%) max_191922232322 Ccs (mpa)min4944.139.278.568.658.8544944.1 Shrinkage after reheating 1500x2h (%) max+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4+0.1-0.4.
Magnesia Bricks Description Magnesia Bricks are alkaline refractory materials. These products have over 90% magnesium oxide content and adopt periclase as the principal crystalline phase. Magnesia Bricks can be divided into two categories of Burnt Magnesia Bricks and Chemical Bonded Magnesite Brick. They have excellent performance of superior high temperature mechanical strength and volume stability. Magnesia Bricks can service in the high temperature of 1750.. They are ideal products for glass furnace application. Magnesia Bricks Features: It is a kind of alkaline refractory product with periclase as main phase magnesite-alumina spinel clinker as basic material. the product has such characteristics as good temperature vibration, good strength and volume stability in high temperature. Magnesia Bricks Application Basic open-hearth furnace for steelmaking Electric furnace bottom and wall Permanent lining of oxygen converter Non-ferrous metal metallurgy furnace Hyperthermia tunnel kiln Lining of rotary cement kiln Heating furnace bottom and wall Regenerative chamber of glass furnace Magnesia Bricks Properties High Refractoriness Good alkaline slag erosion resistance High apparent initial softening temperature Good thermal conductivity High thermal expansion Magnesia Bricks Manufacturing Process Burnt Magnesia Bricks are manufactured with magnesite clinker as the raw material and fired in the high temperature of 1550~1600 after smashing, burdening, mulling and molding. High-purity products can be fired in the temperature that over 1750. Chemical bonded magnesite brick is produced with certain chemical bonding through mixing, molding and drying.
Insulation Bricks
Refractory Fire Brick
PRODUCT DATA SHEET ACID RESISTANT BRICK Material : RED SHALE Type Acid Resistant Brick Size (mm) 230 (LENGTH) X 115 (WIDTH) X 100,76,65,50,40,38,30,25 (THICK) Specification : ASTM C279, ASTM C410, IS 4860-1982 DESCRIPTION : We offer premium quality acid resistant bricks Red â?? Shale , tiles and special shapes. We also offer customized sizes as per clients' requirements. Our acid bricks comply with ASTM C279 Type-III, ASTM C410 Type H, L, and Indian Standard 4860 - 1982 Class-I for all applications where low absorption and high acid resistance is required. FEATURES OF ACID RESISTANT BRICK: Excellent resistant against wide range of chemicals except hydrofluoric acid, high abrasion resistance, low wearing properties, High Thermal resistant to sudden change in temperature AREA OF APPLICATION: Chemical Analysis (Average) Acid and Alkali Storage Tank Farms Demineralization plants and Water treatment plants Chimney inside lining, FGD linings Towers and Columns Process Vessels and Tanks Sewerage Treatment Plants and Lines Industrial Flooring and Bund Areas Chimney and Flue Gas Linings Hoppers and Chutes SiO266.4 Al2 0324 TiO21.1 Fe2 O31.1 K2 O + Na2 O2.5 NOT RECOMMENDED: HF acid or other fluoride solutions Heavy thermal shock Typical Physical Properties of GANESHAS Acid and Chemical Resistant Brick Characteristic RED SHALE ACID RESISTANT BRICK Test Standard Bulk Density, gm/cc - 2.3 to 2.35 ASTM C-20 -Water Absorption, % - 0.1 to 1.5 IS 4860-1968 Apparent Porosity, % -0.5 to 1.75 S 4860 Acid Solubility (H2SO4), Loss in Mass,% -0.1 to 1.8 ASTM C-279 Modulus of Rupture, PSI -2133 to 3555 ASTM C-67 Compressive Strength, Kg/cm2 - 700-900 IS 4860-1968 Abrasion Resistant , Volume in mm3 -69 to 85 EN 102 Surface Hardness, MOHS Scale - 7