Hot-dip galvaning is a process in which the wire is dipped in zinc to create a zinc coating. Hot-dip galvanized steel wire has the advantages of corrosion resistance, good weather-resistance and long life, so it is widely used in many fields.
The requirements for hot-dip galvanized steel wire are as follows:
1. Uniform galvanized layer: The galvanized layer of hot-dip galvanized steel wire should be uniform and dense, without defects such as uneven galvanizing, wrinkling, and falling off.
2. The thickness of the zinc layer is appropriate: the thickness of the zinc layer of the hot-dip galvanized steel wire should meet the standard requirements to ensure its corrosion resistance.
3. Good surface: The surface of hot-dip galvanized steel wire should be smooth, without obvious burrs and oxides.
4. Strong adhesion of galvanized layer: The galvanized layer of hot-dip galvanized steel wire should have good adhesion and not easy to peel off.
5. The chemical composition of galvanized steel wire is stable: the chemical composition of hot-dip galvanized steel wire should meet the relevant standards to ensure its quality stability.
6. The size of the galvanized steel wire is accurate: the diameter, strength and other dimensional parameters of the hot-dip galvanized steel wire should meet the standard requirements to ensure its performance.
In short, the requirement of hot-dip galvanized steel wire is to ensure that its galvanized layer has good quality and stable performance, so as to improve its corrosion resistance and life.

Material: 45#- 75#,77B,Q235 etc
Dia: 1.0mm-6.0mm
Zinc coating :100g/m2 - 800g/m2 Grade A/ B /C�£??
Breaking strength:350mpa-2200mpa
Steel wire (dia:1.0mm-7.0mm ) for ACSR,preformed line products and so on.
Standard: ASTM B 498,ASTM A 411 AS 3863,BS 4565 ,JIS G 3548 ,EN 10264
we can offer high-quality products with good and smooth surface,no joints, uniform and continuous coating,free from imperfections not consistent with good commercial practice.The zinc coating can be up to 800g/m2 for 3.0meter. We can also provide galvanized wire to meet the specific requirements of our customers.

Material:45#- 75#,77B,Q235etc
Dia: 1.0mm-6.0mm
Constructions :1X3, 1X7 ,1X19,1X37
Zinc coating :100g/m2 - 800g/m2 Grade A/ B /C ?
Breaking strength:350mpa-2200mpa
YB/T 5004-2001, GB/T 3428-2002,CAN/CSA-G12,BS 183/BS443,BS EN 10244,ASTM A 475,ASTM A 363
Its widely used in domestic & abroad power, cable, telecommunication, broadcast and television industries. We can produce very heavy zinc thickness steel wire,for example 800 g/m2 for 3.00mm.
Packaging Details: water-proof paper on drums or in coils
Delivery Time: 20 days after confirmed order Payment Terms: L/C,T/T

Zn-5%Al-mischmetal alloy-coated steel wire (galfan / Bezinal ) Specifications
Material: 45 75 ,77B,Q235 etc
Dia: 1.0mm-6.0mm
Aluminum content

Grades Utilities, Common, Siemens-Martin, High Strength and Extra High Strength
Finish Coatings Class A, B and C
Specifications
ASTM A925 -5 % Aluminum-Mischmetal Alloy-Coated Steel Overhead Ground Wire Strand
ASTM A855 Zinc-5 % Aluminum-Mischmetal Alloy-Coated Steel Wire Strand
Galfan a superior corrosive coating of 5% Aluminum and 95% Zinc.

Material: 45#-75#,77B,Q235 etc
Dia: 1.0mm-6.0mm
Zinc coating:100-800g/m2

We can offer high-quality products with good and smooth surface,no joints, uniform and continuous coating,free from imperfections not consistent with good commercial practice.The zinc coating can be up to 800g/m2 for 3.0meter. We can also provide galvanized wire to meet the specific requirements of our customers.

Tianjin Zhongyou Metal Product Co.,Ltd is professional manufacturer with many years experience on metal wire.Founded in 1985, we have produced and exported galvanized

Material:Q195 low carbon steel
Tensile strength:390MPa
Elongation:30%
Material:Q235 low carbon steel

Tensile strength:490MPa

Elongation:23%

Zinc coating:For electron galvanized:8-12g/m

For hot-dip galvanized:60g/m or as your requirement.

0.3mm hot dipped low carbon steel wire
1.Diameter: 0.3mm
2.T/s: 350mpa~500mpa
3.Zinc coating: 30g/m2

En 10244

Size: 0.6mm-5.5mm
Zinc coating: 30g-366g/m2
Tensile strength: 350-1500n/mm2
Packing: 25kg-800kgs per roll

25kg-800kgs per coil
Plastic inside and woven bag or hessian outside

Galvanized Overheadshield Wire
1)1.6mm-4.0mm
2)500kg-800kg per coil OR Spool
3)ASTM B 498 Class A and Class B; ASTM A 475


Orbit Coil; Compact Coil Reel

Materials: high carbon steel wire rod
Application: buildings, constructions,
Standards: astm sae.


4.0mm-8.0mm

Free sample to support the new cooperation !!!!

Oil quenching & tempering spring steel wire

1.Material:50crsia, 55crsia, 60si2mna, 67crva, 65mn, 70#, 67a, 67b, 72a, 72b

2.The range of dia : 0.2-16.0mm

3.Application : for motor or valve

4.Tensile strength : according to customers request

5.Packing: spool or coil, wrapped by plastic

6.Moq: 1 ton/tons

7.Standard: gb/t18983-2003, astm a229m, astm a232m, astm a401m, jis g3560.

Didameter:1.47mm-1.65mm(optional)
Tensile strength:350-450n/mm2
Packing:3.5lbs/coil, 3.125lbs/coil, 1kg/coil(optional) .

1.47mm-1.65mm
3.5lbs, 3.125lbs, 1kg.

Spring steel wire